Universal two-dimensional rare earth MOFs material, solvent-free chemical stripping method and application thereof

A universal, solvent-free technology, applied in the analysis of materials, material analysis by optical means, material analysis by electromagnetic means, etc., can solve the problems of harsh synthesis conditions, achieve simple synthesis methods, high yields, and conditions relatively mild effect

Active Publication Date: 2021-01-26
NORTHEASTERN UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, rare earth ions have high coordination characteristics, RE-MOFs usually exhibit more complex coordination geometries, and due to their harsh synthesis conditions
The development of novel fabricated 2DRE-MOFs nanosheets remains a challenge

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Universal two-dimensional rare earth MOFs material, solvent-free chemical stripping method and application thereof
  • Universal two-dimensional rare earth MOFs material, solvent-free chemical stripping method and application thereof
  • Universal two-dimensional rare earth MOFs material, solvent-free chemical stripping method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A kind of solvent-free chemical exfoliation method of TEAB quaternary ammonium salt-assisted, hierarchical structure bulk rare earth MOFs material, comprises the following steps:

[0048] (1) Eu(NO 3 ) 3 .6H 2 O, trimesic acid and TEAB were mixed in a molar ratio of 1:1:5, and ground for 5 minutes to obtain a mixture;

[0049] (2) Put the mixture in step (1) into a polytetrafluoroethylene reactor, and heat it for 48 hours at a temperature of 160° C. to obtain a product with a hierarchical block shape;

[0050] (3) After the product obtained in step (2) was cooled to room temperature, it was washed with distilled water and ethanol three times in sequence, and then dried at 60°C for 2 hours to obtain a Eu-MOFs material sample, which was named sample 1.

[0051] see figure 2 , the crystal morphology of the Eu-MOFs material obtained in this example is a hierarchical structure block, and the average crystallite size of the Eu-MOFs material is about 10 μm.

Embodiment 2

[0053] A kind of solvent-free chemical exfoliation method of TPAB quaternary ammonium salt-assisted, hierarchical structure bulk rare earth MOFs material, comprises the following steps:

[0054] (1) Eu(NO 3 ) 3 .6H 2 O, trimesic acid and TPAB are mixed in a molar ratio of 1:1:5, and ground for 10 minutes to obtain a mixture;

[0055] (2) Put the mixture in step (1) into a polytetrafluoroethylene reactor, and heat it for 48 hours at a temperature of 160° C. to obtain a product with a hierarchical block shape;

[0056] (3) After the product obtained in step (2) was cooled to room temperature, it was washed with distilled water and ethanol three times in sequence, and then dried at 60°C for 2 hours to obtain a Eu-MOFs material sample, which was named sample 2.

[0057] see image 3 , the crystal morphology of the Eu-MOFs material obtained in this example is a hierarchical structure block, and the average crystallite size of the rare earth Eu-Fs material is about 3 μm.

Embodiment 3

[0059] A kind of solvent-free chemical exfoliation method of TBAB quaternary ammonium salt assisted, accordion-shaped rare earth MOFs material, comprises the steps:

[0060] (1) Eu(NO 3 ) 3 .6H 2 O, trimesic acid and TBAB were mixed in a molar ratio of 1:1:5, and ground for 6 minutes to obtain a mixture;

[0061] (2) Put the mixture in step (1) into a polytetrafluoroethylene reactor, and heat it for 48 hours at a temperature of 160° C. to obtain a product with an organ-shaped appearance;

[0062] (3) After the product obtained in step (2) was cooled to room temperature, it was washed with distilled water and ethanol three times in sequence, and then dried at 60°C for 2 hours to obtain a Eu-MOFs material sample, which was named sample 3.

[0063] see Figure 4 , the crystal morphology of the Eu-MOFs material obtained in this example is accordion-shaped, and the average size of the crystallites of the Eu-MOFs material is about 6 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a universal two-dimensional rare earth MOFs material, a solvent-free chemical stripping method and application thereof. According to the invention, different quaternary ammonium salts are used as a morphology regulator and an intercalation stripping agent, and under a solvent-free state, a mechanical grinding method and heating treatment in a reaction kettle are carried outin sequence so as to achieve effective regulation and control of the rare earth MOFs material from a 3D block shape to a 2D two-dimensional sheet shape are realized; in the process, the quaternary ammonium salt is attached to the surface of the rare earth MOFs material, anisotropic growth of the rare earth MOFs material is caused, and then the ultrathin MOF nanosheet is formed; and the synthesismethod of the rare earth MOFs material provided by the invention is simple and convenient, high in yield and relatively mild in condition, meets the requirements of the 2D rare earth MOFs material onmaterial performance in fluorescence and sensing application, and further has a large-scale production prospect.

Description

technical field [0001] The invention belongs to the technical field of rare earth nanoporous crystalline materials, and in particular relates to a universal two-dimensional rare earth MOFs material and a solvent-free chemical stripping method and application thereof. Background technique [0002] In recent years, two-dimensional (2D) sheet-like nanomaterials have attracted much attention due to their extremely large surface areas and unique physical and chemical properties. Metal-organic frameworks (MOFs for short) are nanoporous crystalline materials constructed of metal ions or clusters and organic bridging ligands. Important material in many fields of application. Among them, 2D metal-organic framework (2D MOFs) nanosheets have attracted great research interest due to their excellent performance in gas separation, energy conversion and storage, catalysis, and sensing. 2D rare-earth metal-organic frameworks (2D RE-MOFs) materials are also widely used in optical fields su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G83/00G01N21/17G01N27/00
CPCC08G83/008G01N21/17G01N27/00
Inventor 徐燕刘佳强
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com