Bamboo-based fiber composite material and continuous preparation method thereof

A fiber composite material, bamboo-based material technology, applied in the direction of wood compression, wood impregnation, manufacturing tools, etc., can solve the problems of low production efficiency, complex preparation method, inability to realize continuous production, etc., and achieve high production efficiency and preparation method. Simple and easy to use, good effect of anti-mildew and insect-proof

Active Publication Date: 2021-02-19
INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] In view of the technical problems existing in the prior art, such as: complex preparation methods, low production efficiency and inability to realize continuous production, the invention provides a continuous preparation method for bamboo-based fiber composites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo-based fiber composite material and continuous preparation method thereof
  • Bamboo-based fiber composite material and continuous preparation method thereof
  • Bamboo-based fiber composite material and continuous preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] First aspect of the present invention provides a kind of preparation method of bamboo-based fiber composite material, described bamboo-based fiber composite material comprises a plurality of bamboo fiberized veneers, and it comprises the following steps:

[0051] Rolling and impregnating the bamboo fiberized veneer with an adhesive to obtain an impregnated product;

[0052] drying the impregnated product to obtain a dried product;

[0053] After sewing the dried product, at least a first bamboo-based material and a second bamboo-based material are obtained;

[0054] Assembling the first bamboo-based material and the second bamboo-based material to obtain a molded body;

[0055] Carrying out hot pressing to described molded body, obtains the blank of bamboo-based fiber composite material;

[0056] The bamboo-based fiber composite material blank is subjected to functional post-treatment to obtain the bamboo-based fiber composite material.

[0057]

[0058] The bamboo...

Embodiment 1

[0103] The bamboo is decomposed into a bamboo fiberized veneer, the width of the bamboo fiberized veneer is 10 cm, and the moisture content is 35%. Then, the fibrous veneer is rolled and compacted with an adhesive, then immersed in the adhesive, and then rolled to obtain an impregnated product. Among them, the rolling pressure is 20MPa. The adhesive is an aqueous solution of water-soluble impregnated phenolic resin, wherein the mass concentration of the water-soluble impregnated phenolic resin is 30%; meter) accounts for 15% of the mass content of the impregnated product after rolling.

[0104] Then, the impregnated product was dried with a mesh belt dryer at a drying temperature of 70° C. and a drying time of 80 min to obtain a dried product. After drying, the moisture content of the dried product was 12%.

[0105] The dried products are arranged in parallel and then subjected to whole-sheet sewing processing to obtain bamboo-based materials. Wherein, in the sewing proces...

Embodiment 2

[0110] The bamboo is decomposed into bamboo fiberized veneer, the width of the bamboo fiberized veneer is 10cm, and the moisture content is 35%, and then the fibrous veneer is rolled with an adhesive and then immersed in the adhesive, Then rolling is carried out to obtain the impregnated product. Among them, the rolling pressure is 15MPa. The adhesive is an aqueous solution of water-soluble impregnated phenolic resin, wherein the mass concentration of the water-soluble impregnated phenolic resin in the adhesive is 25%, after rolling, the moisture content of the impregnated product is 24.30%, and the content of the water-soluble impregnated phenolic resin ( 100%) accounts for 15% of the content of the bamboo-based material after rolling. Then, the impregnated product was dried with a mesh belt dryer at a drying temperature of 70° C. and a drying time of 60 min to obtain a dried product. After drying, the moisture content of the dried product was 12%.

[0111] The dried produ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a bamboo-based fiber composite material and a preparation method thereof. The preparation method comprises the following steps that an adhesive is used for rolling and dippinga bamboo fiberized veneer, and a dipped product is obtained; the dipped product is dried to obtain a dried product; after the dried product is sewn, a first bamboo-based material and a second bamboo-based material are at least obtained; the first bamboo-based material and the second bamboo-based material are assembled to obtain a formed body; hot pressing is carried out on the formed body to obtain a bamboo-based fiber composite material blank; and functional post-treatment is carried out on the bamboo-based fiber composite material blank to obtain the bamboo-based fiber composite material. The preparation method of the bamboo-based fiber composite material is simple and easy to implement, raw materials are easy to obtain, continuous forming and manufacturing can be achieved, and the production efficiency is high.

Description

technical field [0001] The invention relates to a bamboo-based fiber composite material and a preparation method thereof, in particular to a continuous molding manufacturing method of the bamboo-based fiber composite material, which belongs to the field of wood materials. Background technique [0002] my country is the world's largest owner of bamboo resources and the world's largest producer of bamboo products. At present, my country's bamboo industry production scale and technical level rank among the top in the world. As people's awareness of environmental protection is getting stronger and stronger, bamboo has been recognized by the world as an environmentally friendly material with sustainable development characteristics, so the bamboo industry has developed rapidly in our country this year. [0003] Bamboo-based fiber composite material is a new type of natural polymer composite material made of my country's rich bamboo resources as raw materials through directional re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27J1/00B27K9/00B27K3/02B27K5/04B27M1/08B27M1/02
CPCB27J1/00B27K9/002B27K3/02B27K3/0207B27K5/04B27M1/08B27M1/02Y02W30/91
Inventor 张亚慧齐越于文吉张亚梅饶飞吴江源
Owner INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap