A manual arc welding electrode for welding low-nitrogen and non-magnetic naval steel

A manual arc welding and shipbuilding technology, applied in welding equipment, welding media, welding/cutting media/materials, etc., can solve the problems of welding materials that have not been reported publicly, and achieve excellent operation processability, excellent weldability, and seawater resistance Excellent corrosion resistance

Active Publication Date: 2022-03-04
WUHAN UNIV OF SCI & TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of low-nitrogen non-magnetic naval steel is positioned as a super austenitic stainless steel with high Ni content, which can meet the higher requirements of high strength and high corrosion resistance of the ship hull structure, but it can be matched with the low-nitrogen non-magnetic naval steel. The material has not been publicly reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation method of the high-alloy steel core is as follows: batching according to the chemical components and contents of the high-alloy steel core, smelting, forging, rolling, and drawing to obtain the high-alloy steel core.

[0034] The chemical composition and content of the coating are: 45-47wt% for marble; 20-23wt% for fluorite; 3-5wt% for lithium fluoride; 2-4wt% for quartz sand; 10-12wt% for rutile %; manganese nitride is 6-8wt%; the rest is iron powder.

[0035]The preparation method of the manual arc welding electrode is as follows: first batching and mixing according to the chemical components of the coating and their contents, and then adding 10-15 wt% water glass of the chemical components of the coating, stirring evenly, The coating is obtained; then, the coating is pressure-coated on the surface of the high-alloy steel core to prepare a manual arc welding electrode for welding low-nitrogen non-magnetic naval steel.

[0036] The water glass is a bin...

Embodiment 1

[0050] A manual arc welding electrode used for welding low-nitrogen and non-magnetic naval steel. The manual arc welding electrode described in this embodiment is the same as the specific implementation mode except for the following.

[0051] The manual arc welding electrode is composed of 70wt% high-alloy steel core and 30wt% coating.

[0052] The chemical composition and content of the high-alloy steel core are: C is 0.03wt%; Si is 0.2wt%; Cr is 23wt%; Mn is 9wt%; Ni is 17wt%; N is 0.25wt%; is 0.006wt%; S is 0.003wt%; the balance is Fe and unavoidable impurities.

[0053] The chemical composition and content of the coating are: 45wt% for marble; 20wt% for fluorite; 3wt% for lithium fluoride; 2wt% for quartz sand; 10wt% for rutile; 6wt% for manganese nitride; Powder is 14 wt%.

[0054] The preparation method of the manual arc welding electrode is as follows: first batching and mixing according to the chemical composition and content of the coating, and then adding 10wt% wa...

Embodiment 2

[0058] A manual arc welding electrode used for welding low-nitrogen and non-magnetic naval steel. The manual arc welding electrode described in this embodiment is the same as the specific implementation mode except for the following.

[0059] The manual arc welding electrode is composed of 75wt% high-alloy steel core and 25wt% coating.

[0060] The chemical composition and content of the high alloy steel steel core are: C is 0.04wt%; Si is 0.3wt%; Cr is 25wt%; Mn is 8wt%; Ni is 19wt%; N is 0.35wt%; is 0.004wt%; S is 0.002wt%; the balance is Fe and unavoidable impurities.

[0061] The chemical composition and content of the coating are: 46wt% for marble; 21wt% for fluorite; 4wt% for lithium fluoride; 3wt% for quartz sand; 11wt% for rutile; 7wt% for manganese nitride; Powder is 8wt%.

[0062] The preparation method of the manual arc welding electrode is as follows: first batching and mixing according to the chemical composition and content of the coating, and then adding 13wt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manual arc welding electrode used for welding low-nitrogen and nonmagnetic naval steel. The technical solution is: the manual arc welding electrode is composed of 70-80wt% high-alloy steel core and 20-30wt% coating; the preparation method is to add water glass to the chemical components of the coating, stir, press It is produced by coating on the surface of high alloy steel core. Composition and mass content of high alloy steel core: C is 0.03-0.05%, Si is 0.2-0.4%, Cr is 23-25%, Mn is 8-10%, Ni is 17-20%, N is 0.25% ~0.45%, P≤0.006%, S≤0.003%, the balance is Fe and unavoidable impurities. The composition and mass content of the coating: 45-47% for marble, 20-23% for fluorite, 3-5% for lithium fluoride, 2-4% for quartz sand, 10-12% for rutile, nitrided Manganese is 6-8%, and the rest is iron powder. The welding seam metal formed by welding the low-nitrogen non-magnetic naval steel provided by the invention has the advantages of non-magnetism, high strength, good ductility and seawater corrosion resistance.

Description

technical field [0001] The invention belongs to the technical field of manual arc welding electrodes. It particularly relates to a manual arc welding electrode used for welding low-nitrogen and non-magnetic naval steel. Background technique [0002] 917 non-magnetic steel is a non-magnetic steel with Mn-Al composition developed in my country in the 1960s and 1970s. It is the main steel used in shipbuilding. Its carbon content and alloy composition are relatively high, and it belongs to a completely non-magnetic single-phase austenite structure. Carbon steel. With the gradual development of ships with large displacement, large tonnage and deep sea, new requirements are put forward for the strength and corrosion resistance of steel used for hull structures. Although the comprehensive performance of 917 steel is good, it can meet the design and use requirements of various ships, but the actual value of the yield strength is low, within the range of 300-450MPa; it belongs to me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30B23K35/365B23K35/40
CPCB23K35/3086B23K35/3607B23K35/365B23K35/404B23K35/0266
Inventor 王红鸿孟庆润
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com