Infrared germanium antimonate glass and preparation method thereof

An antimonate and glass technology, used in glass manufacturing equipment, glass furnace equipment, manufacturing tools, etc., can solve the problems of lead volatilization, environmental and human harm, and poor thermal stability of germanium-barium glass.

Active Publication Date: 2021-03-26
XINYI XIYI ADVANCED MATERIALS RES INST OF IND TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The commonly used germanium-barium glass has poor thermal stability and poor glass drawing performance, and lead will volatilize in the preparation process of germanium-lead glass, which is harmful to the environment and human body. Therefore, it is necessary to develop a kind of glass with good thermal stability and anti-devitrification ability A composition-tunable germanate glass system to improve the physical and chemical properties of germanate glass for application in fiber lasers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Infrared germanium antimonate glass and preparation method thereof
  • Infrared germanium antimonate glass and preparation method thereof
  • Infrared germanium antimonate glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described below in conjunction with specific examples, but the protection scope of the present invention should not be limited thereby.

[0021] Table 1 lists the formulations of Examples 1-3 and Comparative Examples 1-2.

[0022] The formula of table 1 embodiment 1-3 and comparative example 1-2

[0023]

[0024] The preparation process of embodiment 1-3 and comparative example 1-2 is as follows:

[0025] (1) Weigh GeO according to mole percentage 2 , Sb 2 o 3 , SiO 2 , ZnO, Na 2 O, Nb 2 o 5 、Al 2 o 3 The powders are mixed and ground to form 100g of a uniform mixture; the mixture is put into a platinum crucible and melted together in an electric furnace at 1200-1350°C to obtain a clear and transparent glass liquid. The melting temperature of Example 1 is 1300°C, the melting temperature of Example 2 is 1250°C, the melting temperature of Example 3 is 1200°C, the melting temperature of Comparative Example 1 is 1350°C, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of optical glass preparation, and discloses infrared germanium antimonate glass and a preparation method thereof; the infrared germanium antimonate glass is prepared by adding other various oxides on the basis of GeO2-Sb2O3, and has the advantages of wide infrared transmission range, high refractive index, low phonon energy, good crystallization resistance, good thermal stability and good mechanical properties, and is suitable for being used as an intermediate infrared window material.

Description

technical field [0001] The invention relates to the technical field of optical glass preparation, and provides an infrared germanium antimonate glass and a preparation method. Background technique [0002] Infrared materials are widely used in the fields of military, environmental monitoring, medical treatment, optical fiber communication and basic research. Commonly used infrared crystal materials include ZnS, ZnXe, sapphire, magnesium fluoride, calcium fluoride, etc., which are mainly used in optical lens window materials. This type of material has high infrared transmittance, but has low hardness, difficult manufacturing and processing, Disadvantages such as high cost, and it is difficult to apply to fiber lasers. The second is mainly glass materials, which are also the main source of infrared optical fiber materials at present, including germanate glass, fluoride glass, quartz glass and tellurite glass, etc., but fluoride glass has poor chemical stability, difficult pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C3/062C03C4/10C03B5/16C03B25/00C03C13/04
CPCC03C3/062C03C4/10C03B5/16C03B25/00C03C13/046
Inventor 张乐申冰磊康健甄方正张永丽邱凡陈浩
Owner XINYI XIYI ADVANCED MATERIALS RES INST OF IND TECH CO LTD