Multi-functional non-woven fabric and preparation method thereof

A non-woven, multi-functional technology, applied in textiles and papermaking, fiber treatment, biochemical fiber treatment, etc., can solve the needs of special working environments, African swine fever does not have antiviral activity, and cannot take into account antibacterial and deodorizing Effectiveness and other issues, to achieve the effect of good comprehensive performance, good antibacterial and antibacterial effect, and good air permeability

Active Publication Date: 2021-04-02
嘉兴市科富喷绘材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008]1. Antiviral activity African swine fever (ASF) does not have antiviral activity and cannot meet the needs of some special working environments;
[0009]2. Poor antibacterial effect;
[0010]3. Poor adsorption to peculiar smell and poor deodorizing effect;
[0011]4. Not to mention good antibacterial and deodorizing effects, excellent mechanical properties such as tensile strength, soft hand feeling, good air permeability and other comprehensive properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] A kind of preparation method of multifunctional non-woven fabric, comprises the steps:

[0067] A. Prepare impregnation slurry with high pore volume, high air permeability and moisture permeability;

[0068] The impregnated slurry with high pore volume, high air permeability and moisture permeability is made of the following raw materials in parts by weight:

[0069] Ethylene-vinyl acetate copolymer A: 28 to 35 parts,

[0070] 20-24wt% aqueous dispersion of hollow silica nanoparticles with large pores: 40-55 parts,

[0071] 10-14wt% polyvinyl alcohol aqueous solution: 25-32 parts,

[0072] Dispersant: 1 to 3 parts,

[0073] Compound antibacterial powder: 3 to 10 parts;

[0074] Weighing the raw materials of the high-pore volume, high-breathability and moisture-permeability impregnating slurry, stirring and mixing evenly, and then adding water to adjust the viscosity to 9000CPS-11000CPS to obtain the high-pore volume, high-breathability and moisture-permeability impr...

Embodiment 2

[0099] A kind of preparation method of multifunctional non-woven fabric, comprises the steps:

[0100] A. Prepare impregnation slurry with high pore volume, high air permeability and moisture permeability;

[0101] The impregnated slurry with high pore volume, high air permeability and moisture permeability is made of the following raw materials in parts by weight:

[0102] Ethylene-vinyl acetate copolymer A: 28 parts,

[0103] 20wt% aqueous dispersion of hollow silica nanoparticles with large pores: 40 parts,

[0104] 10wt% polyvinyl alcohol aqueous solution: 25 parts,

[0105] Dispersant: 1 part,

[0106] Compound antibacterial powder: 3 parts;

[0107] Weighing the raw materials of the high-pore volume, high-breathability and moisture-permeability impregnating slurry, stirring and mixing evenly, and then adding water to adjust the viscosity to 9000CPSCPS to obtain the high-pore volume, high-breathability and moisture-permeability impregnating slurry;

[0108] B. Immerse ...

Embodiment 3

[0132] A kind of preparation method of multifunctional non-woven fabric, comprises the steps:

[0133] A. Prepare impregnation slurry with high pore volume, high air permeability and moisture permeability;

[0134] The impregnated slurry with high pore volume, high air permeability and moisture permeability is made of the following raw materials in parts by weight:

[0135] Ethylene-vinyl acetate copolymer A: 35 parts,

[0136] 24wt% aqueous dispersion of hollow silica nanoparticles with large pores: 55 parts,

[0137] 14wt% polyvinyl alcohol aqueous solution: 32 parts,

[0138] Dispersant: 3 parts,

[0139] Compound antibacterial powder: 10 parts;

[0140] Weighing the raw materials of the high-pore volume, high-breathability and moisture-permeable impregnation slurry, stirring and mixing evenly, and then adding water to adjust the viscosity to 11000CPS, to obtain the high-pore volume, high-breathability and moisture-permeability impregnation slurry;

[0141] B. Immerse ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of multi-functional non-woven fabric. The preparation method comprises the following steps: A, preparing impregnation slurry with high pore volume, high air permeability and high moisture permeability; B, immersing PET non-woven fabric into the impregnation slurry with high pore volume, high air permeability and high moisture permeability, carrying outpressing and rolling, and then carrying out solidification, washing and drying to obtain pretreated PET impregnated non-woven fabric; C, preparing blade coating slurry with high pore volume, high airpermeability and high moisture permeability and E, coating the pretreated PET impregnated non-woven fabric with the blade coating slurry with high pore volume, high air permeability and high moisturepermeability by adopting a scraper, a first coating thickness being 50+ / -1 g / m<2>, and baking at 75 DEG C until the slurry is half-dry; and coating for the second time, the second coating thickness being 40+ / -1 g / m<2>, and drying at 102 DEG C. The obtained multi-functional non-woven fabric is high in antiviral activity for African swine fever, large in peculiar smell reduction rate, high in normalemissivity, good in antibacterial effect, excellent in mechanical properties such as tensile strength, soft in hand feeling, good in air permeability, and good in comprehensive use performance.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a multifunctional nonwoven fabric and a preparation method thereof. Background technique [0002] Non-woven fabric, also known as non-woven fabric, is composed of directional or random fibers. It is a new generation of environmentally friendly materials. It can be recycled and reused, and it is called cloth because of its appearance and certain properties. [0003] Non-woven fabrics are widely used in hygienic fields such as surface materials of high-grade disposable absorbent articles or other related fields. But its function is mainly to use chemical agents to obtain functions such as disinfection and antibacterial, or to add related physical materials to obtain a single function. [0004] As a polymer material, ethylene-vinyl acetate copolymer (EVA) has good plasticity, elasticity and processability, and the EVA material after foaming treatment has the advantages o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/227D06M15/333D06M11/79D06M11/76D06M11/74D06M101/32
CPCD06M15/227D06M15/333D06M11/79D06M16/00D06M11/76D06M11/74D06M2101/32D06M2200/50
Inventor 吴富荣
Owner 嘉兴市科富喷绘材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products