Vanadium titano-magnetite smelting slag activation method

A technology of vanadium titanomagnetite and activation method, applied in cement production and other directions, can solve the problems of thickening and poor fluidity of titanium slag, and achieve the effects of increasing specific surface area, low power consumption, and increasing total volume

Active Publication Date: 2021-04-20
LIUPANSHUI NORMAL UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reason is that Ti(CNO) can thicken the titanium slag and make the fluidity worse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Mechanical activation under embodiment 1 inert ball milling atmosphere

[0034] Pulverize 10 grams of vanadium-titanium magnetite smelting slag to obtain vanadium-titanium magnetite smelting slag powder, and dry it at a constant temperature of 750°C to remove all absorbed moisture in the material. After drying, the vanadium-titanium magnetite smelting slag is Add 0.01 gram of synergist (in this example, the synergist is a mixture of sodium silicate and calcium carbonate, and the mixing mass ratio of the two is 3:1), mix well and put it in a microwave reactor. The microwave treatment was carried out for 30 minutes at the highest power; the vanadium-titanium magnetite smelting slag powder after the microwave treatment was packed into a container containing 6 stainless steel balls with a diameter of 18 mm and 12 stainless steel balls with a diameter of 12 mm (the grinding aid is ethanol, and the mass ratio of the ball to material is 25:1), first vacuumize the ball mill tan...

Embodiment 2

[0037] With embodiment 1, the only difference is that the ball milling time is 60min.

[0038] The activated vanadium-titanium magnetite smelting slag micropowder prepared in this example is radioactively qualified according to the GB-6566 national standard, the specific surface area is 550㎡ / kg, and the activity index reaches GB / T18046-2008; GB / T203-1994 requirements, pure activation The final vanadium-titanium-magnetite smelting slag fine powder has a 3d compressive strength of 30Mpa and a 28d compressive strength of 50Mpa; using this quality of vanadium-titanium magnetite smelting slag fine powder to replace 25% of PS-32.5 cement, the 3d compressive strength 40Mpa, 28d compressive strength is 60Mpa.

Embodiment 3

[0040] With embodiment 1, the only difference is that the ball milling time is 120min.

[0041] The activated vanadium-titanium magnetite smelting slag micropowder prepared in this example is radioactively qualified according to GB-6566 national standard, the specific surface area is 650㎡ / kg, and the activity index reaches GB / T18046-2008; GB / T203-1994 requirements, pure activation The final vanadium-titanium-magnetite smelting slag fine powder has a 3d compressive strength of 33Mpa and a 28d compressive strength of 51Mpa; using this quality of vanadium-titanium magnetite smelting slag fine powder to replace 25% of PS-32.5 cement, the 3d compressive strength It is 45Mpa, and the 28d compressive strength is 68Mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a vanadium titano-magnetite smelting slag activation method, and belongs to the technical field of smelting slag activation. The vanadium titano-magnetite smelting slag is crushed to obtain vanadium titano-magnetite smelting slag powder, the vanadium titano-magnetite smelting slag powder is dried under a constant temperature condition to remove all adsorbed moisture in the material, and the vanadium titano-magnetite smelting slag powder is uniformly mixed with a synergist and then put into a microwave reactor for microwave treatment; and the powder and a grinding aid into a planetary ball mill, and ball milling is carried out under the protection of inert gas or in 10% air or air atmosphere. According to the method, the hydration activity of the surface of the powder is greatly excited, the specific surface area is greatly increased, the powder subjected to microwave treatment is further subjected to ball milling under the effect of the liquid grinding aid, static electricity on the surface of the powder with the high specific surface area can be effectively reduced, powder aggregation is prevented, and therefore, the vanadium titano-magnetite smelting slag micro-powder with high activity and high dispersity is obtained under lower power consumption, and high-quality treatment of the vanadium titano-magnetite smelting slag is realized.

Description

technical field [0001] The invention relates to the technical field of smelting slag activation, in particular to a method for activating vanadium-titanium magnetite smelting slag. Background technique [0002] my country's vanadium-titanium magnetite smelting history has been 40 to 50 years. In the long years, the solid industrial waste generated after smelting has reached about 100 million tons, and the annual rate is 5 million tons. The increase, piled up with large and small ravines in the production area, not only wasted precious land resources but also polluted the environment, urgently awaiting our comprehensive development and utilization. [0003] my country's scientific and technological workers have never stopped research on the comprehensive utilization of titanium slag. Due to the special physical and chemical properties and mineral structure of titanium slag, no major breakthrough has been made. Chenggang has cooperated with many research and production units ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/153C04B7/36
CPCY02P40/10
Inventor 朱山马毅胡江良袁杰
Owner LIUPANSHUI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com