An antifouling flashover coating, a single-component technology, applied in the direction of antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problems of poor adhesion, short life, inconvenient use, etc., to achieve anti-fouling Improved sedimentation ability, increased pollution flashover voltage, and excellent weather resistance

Inactive Publication Date: 2003-11-19
CHENGDU TALY TECH CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of RTV silicone coating is mostly two-component, which is extremely inconvenient to use, and has poor adhesion, large waste and short service life
There are also some single-component anti-fouling flashover coatings, such as "hydrophobic anti-fouling flashover coating" disclosed in CN1077474, "a long-term anti-fouling flashover coating" disclosed in CN11

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The following are examples of the present invention:

[0013] 30 parts (parts by weight) of hydroxyl-terminated polydimethylsiloxane (η=3000~5000mm 2 / s); basic flame retardant Al(OH) 3 4 parts (parts by weight), reinforcing agent treated with gas phase method SiO 2 (The BET is 175m 2 / s) 38 parts (parts by weight), additive inert dimethicone (η=350~500mm 2 / s) 1 part (parts by weight), respectively add to the batching kettle and heat to 150℃ (not less than 600mmHg) under stirring, dehydrate for 2 hours, use N 2 Vent, then add 0.2 parts (parts by weight) of the catalyst titanate chelate, 1 part of the cross-linking agent methyltrimethoxysilane and continue to stir for 1 hour, and then add 60 parts of anhydrous petroleum ether with a diluent 90~120℃ ( (Parts by weight) after continuing to stir for 0.5 hours, filter and seal the package in an iron tin or glass bottle.

[0014]

[0015] In the above-mentioned embodiments, the measured adhesion reached level 1, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides a RTV monocomponent hydrophobic long-acting antifouling flashing paint for porcelain insulator for high-voltage transmission line of power system and its production method. It is formed from the following components (by weight %): 20-40% of terminal hydroxy polysiloxane, 2-10% of basic fire-resisting agent, 3-20% of reinforcing agent, 1-5% of additive, 0.2-0.4% of catalyst, 1-5% of cross-linking agent and 30-60% of diluting agent.

Description

Technical field [0001] The invention relates to an RTV single-component water-repellent long-lasting anti-pollution flashover paint used for high-voltage transmission and transformation (station) lines of electric power systems and porcelain insulators of railway electric locomotives and a production method. Background technique [0002] Porcelain insulators are currently important parts of power transmission and transformation (station) lines and railway electric cars, and are also the most economical products with the longest history of use. Because porcelain insulators are prone to accumulate pollutants during use, that is, dirt, and the hydrophilicity of the surface can easily form a conductive water film under harsh conditions such as rain, fog, and dew, causing "fouling flash" power outage accidents. In order to reduce the surface energy of porcelain insulators and make the surface hydrophobic to reduce and eliminate the pollution flashover and power failure trip accidents ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/16C09D183/04
Inventor 陶云峰王成张向伟胡发岭乔俊祥
Owner CHENGDU TALY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap