Formaldehyde-free impregnated film adhesive and preparation method thereof

A technology of impregnating adhesive film paper and impregnating glue, applied in the field of adhesive film paper, can solve problems such as unsatisfactory

Pending Publication Date: 2021-06-08
东莞市贝辉装饰材料有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To circumvent formaldehyde, other adhesives have been t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A kind of formaldehyde-free impregnated film paper of the present embodiment, soak the base material of described film paper in formaldehyde-free impregnating glue solution, then take out and dry the base material after impregnating, make described film paper, The formaldehyde-free impregnating glue comprises the following raw materials in parts by weight:

[0055] 30 parts of water-based PUA resin

[0056] Emulsifier 10 parts

[0057] Dispersant 5 parts

[0058] Wood special penetrating agent 5 parts

[0059] 3 parts wetting agent

[0060] 50 parts of water.

[0061] The water-based PUA resin is A-2031 water-based PUA resin. The emulsifier is CO-436 alkoxy polyoxyethylene ether sodium sulfate; the dispersant is WMP-0513 aliphatic polyether polyurethane dispersion; the special penetrant for wood is penetrant ZY-88; the The wetting agent is 104E wetting agent.

[0062] A kind of preparation method of formaldehyde-free impregnated adhesive film paper of the present...

Embodiment 2

[0066] A kind of formaldehyde-free impregnated film paper of the present embodiment, soak the base material of described film paper in formaldehyde-free impregnating glue solution, then take out and dry the base material after impregnating, make described film paper, The formaldehyde-free impregnating glue comprises the following raw materials in parts by weight:

[0067] 40 parts of water-based PUA resin

[0068] Emulsifier 12 parts

[0069] Dispersant 7 parts

[0070] Wood special penetrating agent 8 parts

[0071] Wetting agent 5 parts

[0072] 65 parts of water.

[0073] The water-based PUA resin is DA-3100 water-based PUA resin. The emulsifier is CO-436 alkoxy polyoxyethylene ether sodium sulfate; the dispersant is WMP-0513 aliphatic polyether polyurethane dispersion; the special penetrant for wood is penetrant ZY-88; the The wetting agent is 104E wetting agent.

[0074] A kind of preparation method of formaldehyde-free impregnated adhesive film paper of the presen...

Embodiment 3

[0078] A kind of formaldehyde-free impregnated film paper of the present embodiment, soak the base material of described film paper in formaldehyde-free impregnating glue solution, then take out and dry the base material after impregnating, make described film paper, The formaldehyde-free impregnating glue comprises the following raw materials in parts by weight:

[0079] Waterborne PUA resin 50 parts

[0080] Emulsifier 13 parts

[0081] Dispersant 9 parts

[0082] Wood special penetrating agent 9 parts

[0083] Wetting agent 6 parts

[0084] 80 parts of water.

[0085] The water-based PUA resin is a mixture of A-2031 water-based PUA resin and DA-3100 water-based PUA resin with a mass ratio of 2:1. The emulsifier is CO-436 alkoxy polyoxyethylene ether sodium sulfate; the dispersant is WMP-0513 aliphatic polyether polyurethane dispersion; the special penetrant for wood is penetrant ZY-88; the The wetting agent is 104E wetting agent.

[0086] A kind of preparation method...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of film adhesives, in particular to formaldehyde-free impregnated film adhesive and a preparation method thereof. A base material of the film adhesive is soaked in a formaldehyde-free dipping glue solution, and then the dipped base material is taken out and dried so as to obtain the film adhesive. The formaldehyde-free dipping glue solution is prepared from the following raw materials in parts by weight: 30-60 parts of water-based PUA resin, 8-15 parts of an emulsifier, 5-10 parts of a dispersing agent, 5-10 parts of a penetrating agent special for wood, 3-8 parts of a wetting agent and 50-100 parts of water. According to the invention, the base material can be directly dipped in the formaldehyde-free dipping glue solution, the formaldehyde-free dipping glue solution fully permeates the base material, and the prepared film adhesive really does not contain formaldehyde and has good environmental protection property. In addition, due to full dipping of the dipping glue solution, the prepared film adhesive has excellent fullness, luster, hardness, solvent resistance and weather resistance, does not change color or turn yellow during high-temperature baking, and is high in product quality.

Description

technical field [0001] The invention relates to the technical field of film paper, in particular to a formaldehyde-free impregnated film paper and a preparation method thereof. Background technique [0002] China is the world's largest wood-based panel producer and also the largest furniture producer. Currently, the production of wood-based panels exceeds 300 million cubic meters. The wood-based panel furniture needs to be finished. The common ones are melamine formal impregnated paper finish, wood veneer finish, paint finish, etc. Among them, the effect of melamine paper finish is much higher than other finishes, and , low cost and high processing efficiency. [0003] With people's increasing requirements for environmental protection, the production of wood-based panels and the greening of products are becoming more and more popular. More and more wood-based panel manufacturers have begun to produce formaldehyde-free particle boards, multi-layer boards, and fiberboards. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/00D21H17/46D21H23/32D21H25/06D21H21/14D21H21/08
CPCD21H27/00D21H17/72D21H17/46D21H23/32D21H25/06D21H21/14D21H21/08
Inventor 彭峻胡锡咏别恒勇黄美辉
Owner 东莞市贝辉装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap