Closestool resin mold cleaning agent

A technology for resin molds and cleaning agents, applied in the field of cleaning agents, can solve problems such as long time, and achieve the effects of increasing capacity, improving cleaning efficiency, and increasing momentum

Inactive Publication Date: 2021-06-11
ZHONGTAO SANITARY WARO MFG CO LTD OF TANGSHAN
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the mud-like particles of clay have very good plasticity and viscosity, this method of cleaning with tap water takes a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Closestool resin mold cleaning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A toilet resin mold cleaning agent, in parts by weight, the composition of the cleaning agent is as follows: 53 parts of ethanol, 39 parts of glycerin, 5.5 parts of polyethylene glycol stearate, 0.8 parts of sodium sulfate, 1.2 parts of copper chloride part, 0.1 part of perfluorocyclohexylamine.

Embodiment 2

[0013] A toilet resin mold cleaning agent, in parts by weight, the composition of the cleaning agent is as follows: 55 parts of ethanol, 38 parts of glycerin, 5.9 parts of polyethylene glycol stearate, 0.7 parts of sodium sulfate, 1.4 parts of copper chloride parts, 0.9 parts of perfluorocyclohexylamine.

Embodiment 3

[0015] A toilet resin mold cleaning agent, in parts by weight, the composition of the cleaning agent is as follows: 57 parts of ethanol, 36 parts of glycerin, 6.4 parts of macrogol stearate, 0.6 part of sodium sulfate, 1.7 parts of copper chloride parts, 0.07 parts of perfluorocyclohexylamine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of cleaning agents, in particular to a toilet resin mold cleaning agent. The cleaning agent is prepared from the following components in parts by weight: 53 to 61 parts of ethanol, 33 to 39 parts of glycerol, 5.5 to 7.3 parts of polyethylene glycol stearate, 0.5 to 0.8 part of sodium sulfate, 1.2 to 2.1 parts of copper chloride and 0.05 to 0.1 part of perfluorocyclohexylamine. The cleaning agent can absorb moisture in clogging of a closestool resin mold, so that the surface of the clogging becomes loose and loses plasticity and viscidity, the clogging is discharged out of the resin mold under the action of pressure and liquid flow to completely remove the cloggings. Therefore, time consumed for cleaning the closestool resin mold is short, and the cleaning efficiency is high.

Description

technical field [0001] The invention relates to the technical field of cleaning agents, in particular to a toilet resin mold cleaning agent. Background technique [0002] Toilets are commonly used sanitary ware, and most of them are produced by pressure grouting. Pressure grouting has the advantages of strong adaptability, ability to produce arbitrary complex shapes, low production cost, and uniform green body structure. In order to improve the service life of the mold, the current toilet pressure grouting molding equipment generally adopts a breathable resin mold, which is distributed with a large number of tiny pores penetrating its inner and outer surfaces. The slurry is injected into the closed cavity in the resin mold, and then pressurized inward through the injection port, the moisture in the slurry is discharged from the pores of the resin mold under the action of pressure, and the material particles in the slurry are due to the size ratio The pores are large and st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C11D1/74C11D3/20C11D3/04C11D3/30C11D3/60C11D11/00
CPCC11D1/74C11D3/201C11D3/2065C11D3/042C11D3/30C11D2111/14
Inventor 夏剑石张凯魏志敏
Owner ZHONGTAO SANITARY WARO MFG CO LTD OF TANGSHAN