Cracked peacock blue glaze daily porcelain

A technology of daily-use porcelain and peacock blue, which is applied in the field of daily-use porcelain preparation, can solve the problems such as easy peeling off of the glaze surface, and achieve the effect of high gloss of the glaze surface, not easy to damage cleaning, and clear viewing

Active Publication Date: 2021-06-15
FUJIAN DEHUA HUILONG CERAMIC
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]The traditional peacock blue glaze is colored with copper elements. It is made by hanging the green body and firing at low temperature. The glaze surface is easy to fall off; further improvement is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] Its preparation method comprises the following steps:

[0033] Step 1, preparing base slurry, peacock blue glaze slurry and transparent glaze slurry;

[0034] Step 2, use the base slurry obtained in step 1 to prepare a ceramic body. After the ceramic body is dried, apply the peacock blue glaze slurry prepared in step 1 on the ceramic body in a glazed manner, wherein the peacock blue glaze slurry The thickness is 0.8-1mm;

[0035] Step 3: Put the peacock blue glaze slurry into a kiln after drying, and fire it into a porcelain body under a reducing atmosphere at 1230-1280°C. The specific firing control is as follows:

[0036] Low temperature stage: the temperature in the kiln rises from normal temperature to 320-350°C, and the kiln firing time is 1-2h;

[0037] Decomposition and oxidation stage: the temperature in the kiln is raised to 820-850°C, and the kiln is fired for 3-4 hours;

[0038] High-temperature strong reduction stage: the temperature in the kiln is raised...

Embodiment 1

[0044] A daily-use porcelain with cracked peacock blue glaze, including a body, peacock blue glaze and transparent protective glaze.

[0045] The green body is composed of the following raw materials in parts by weight: 18 parts of Dehua feldspar, 25 parts of Dehua kaolin, 30 parts of quartz, 15 parts of diopside, 12 parts of magnesite, 510 parts of wollastonite, 3 parts of zirconia, 2 parts of yttrium oxide, specifically, the chemical composition of the green body is as follows: SiO 2 : 61.55%, Al 2 o 3 : 18.2%, MgO: 4.1%, CaO: 7.5%, Na 2 O: 3.06%, ZrO 2 : 0.42%, Y 2 o 3 : 0.07%, Fe 2 o 3 : 0.19%, ZnO: 1.76%, I.L: 3.15%.

[0046] The chemical composition of peacock blue glaze is as follows: SiO 2 : 52.7%, Al 2 o 3 : 19.8%, MgO: 8.1%, K 2 O: 9.7%, ZnO: 3.17%, Na 2 O: 1.65%, CuO: 1.36%, CoO: 0.11%, MnO 2 : 0.09%, Fe 2 o 3 : 0.59%, I.L: 2.73%.

[0047] The transparent glaze is composed of the following raw materials in parts by weight: 30 parts of Dehua calcite,...

Embodiment 2

[0060] A daily-use porcelain with cracked peacock blue glaze, including a body, peacock blue glaze and transparent protective glaze.

[0061] The green body is composed of the following raw materials in parts by weight: 22 parts of Dehua feldspar, 20 parts of Dehua kaolin, 40 parts of quartz, 10 parts of diopside, 18 parts of magnesite, 5 parts of wollastonite, 5 parts of zirconia, 1 part of yttrium oxide, specifically, the chemical composition of the green body is as follows: SiO 2 : 66.79%, Al 2 o 3 : 14.9%, MgO: 4.9%, CaO: 6.1%, Na 2 O: 2.48%, ZrO 2 : 0.59%, Y 2 o 3 : 0.09%, Fe 2 o 3 : 0.16%, ZnO: 1.48%, I.L: 2.51%.

[0062] The chemical composition of peacock blue glaze is as follows: SiO 2 : 59.5%, Al 2 o 3 : 16.8%, MgO: 6.4%, K 2 O: 7.8%, ZnO: 3.96%, Na 2 O: 2.07%, CuO: 1.08%, CoO: 0.13%, MnO 2 : 0.07%, Fe 2 o 3 : 0.48%, I.L: 1.71%.

[0063] The transparent glaze is composed of the following raw materials in parts by weight: 40 parts of Dehua calcite, 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

Cracked peacock blue glaze daily porcelain comprises a green body, peacock blue glaze and transparent protective glaze, the green body is prepared from the following specific chemical components in percentage by weight: 61.55 to 66.79% of SiO2, 14.9 to 18.2% of Al2O3, 4.1 to 4.9% of MgO, 6.1 to 7.5% of CaO, 2.48 to 3.06% of Na2O, 0.42 to 0.59% of ZrO2, 0.07 to 0.09% of Y2O3, 0.16 to 0.19% of Fe2O3, 1.48 to 1.76% of ZnO and 2.51 to 3.15% of I.L; AND the chemical components of the peacock blue glaze are strictly controlled, cobalt oxide, manganese oxide and ferric oxide are introduced to be compounded with copper oxide to serve as a coloring agent, and through 1230-1280 high-temperature firing, the glaze surface of the fired porcelain body is peacock blue which is green in blue, and the blue and the green are blended and camouflaged with each other.

Description

technical field [0001] The invention belongs to the field of daily-use porcelain preparation, and in particular relates to cracked peacock blue glaze daily-use porcelain. Background technique [0002] The peacock blue glaze color is greenish in blue, blending with blue and green, and covering each other, just like the feather color of male peacocks in nature. Therefore, the glaze color is based on peacock feathers. The greenish glaze is called peacock green, and the blue glaze is called peacock blue. Rich, gorgeous glaze. Peacock blue glaze utensils have always been loved by people, and have been concerned by the ceramic industry at home and abroad for many years. [0003] The traditional peacock blue glaze is colored with copper elements. It is made by hanging the green body and firing at low temperature. The glaze surface is easy to fall off; further improvement is needed. Contents of the invention [0004] The purpose of the present invention is to overcome the short...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/622C04B41/86C03C8/04
CPCC03C8/04C04B35/14C04B35/622C04B41/86C04B41/5022C04B2235/3217C04B2235/3206C04B2235/3208C04B2235/3201C04B2235/3225C04B2235/3272C04B2235/3244C04B2235/3284C04B2235/6567C04B2235/6583C04B2235/661C04B41/4539C04B41/0072Y02P40/60
Inventor 李玉桃
Owner FUJIAN DEHUA HUILONG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More