Non-sticking wall template material and preparation method thereof

A wall and formwork technology, which is applied in the field preparation of formwork/formwork/work frame, building components, construction, etc., can solve the problem of high requirements for wooden wall formwork support, reduce support requirements, and promote Detachment, the effect of preventing natural shedding

Inactive Publication Date: 2021-06-18
天造机器人科技(广东)有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a non-stick wall formwork material and a preparation method, which solves the problem of pasting the wall formwork and the wooden wall formwork for the existing pouring wall after the pouring wall is dried. The problem of high requirements for body formwork support

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The embodiment of the present invention provides a non-stick wall formwork material and its preparation method, comprising the following components by weight: 25 parts of Portland cement, 10 parts of clay powder, 5 parts of fly ash, 5 parts of sepiolite, 1 part of Basalt fiber, 5 parts of glass fiber, 1 part of chitosan, 1 part of nano-silica airgel powder, 5 parts of calcium oxide, 1 part of insect repellent, and 1 part of flame retardant.

[0029] The insect repellant is one of chlordane emulsion, chlordane oil, and salicylic acid, and the flame retardant is any one of magnesium hydroxide and aluminum hydroxide.

[0030] A preparation method of a non-stick wall formwork material, comprising the following steps:

[0031] Step 1: Micro-carving on the surface of the wall formwork

[0032] Use micro-carving equipment to carry out micro-carving treatment on the surface of the pouring cavity of the wall pouring formwork. The depth of the micro-carving carving is at least 2...

Embodiment 2

[0040] The embodiment of the present invention provides a non-stick wall formwork material and its preparation method, comprising the following components by weight: 30 parts of Portland cement, 12 parts of clay powder, 8 parts of fly ash, 8 parts of sepiolite, 3 parts Basalt fiber, 7 parts of glass fiber, 2 parts of chitosan, 3 parts of nano-silica airgel powder, 8 parts of calcium oxide, 1.5 parts of insect repellent, and 1.5 parts of flame retardant.

[0041] The insect repellant is one of chlordane emulsion, chlordane oil, and salicylic acid, and the flame retardant is any one of magnesium hydroxide and aluminum hydroxide.

[0042] A preparation method of a non-stick wall formwork material, comprising the following steps:

[0043] Step 1: Micro-carving on the surface of the wall formwork

[0044] Use micro-carving equipment to carry out micro-carving treatment on the surface of the pouring cavity of the wall pouring formwork. The depth of the micro-carving carving is at l...

Embodiment 3

[0052] The embodiment of the present invention provides a non-stick wall formwork material and its preparation method, comprising the following components by weight: 35 parts of Portland cement, 15 parts of clay powder, 10 parts of fly ash, 10 parts of sepiolite, 5 parts Basalt fiber, 10 parts of glass fiber, 5 parts of chitosan, 5 parts of nano-silica airgel powder, 10 parts of calcium oxide, 2 parts of insect repellent, and 2 parts of flame retardant.

[0053] The insect repellant is one of chlordane emulsion, chlordane oil, and salicylic acid, and the flame retardant is any one of magnesium hydroxide and aluminum hydroxide.

[0054] A preparation method of a non-stick wall formwork material, comprising the following steps:

[0055] Step 1: Micro-carving on the surface of the wall formwork

[0056]Use micro-carving equipment to carry out micro-carving treatment on the surface of the pouring cavity of the wall pouring formwork. The depth of the micro-carving carving is at le...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a non-sticking wall template material and a preparation method thereof, and relates to the field of buildings. The non-sticking wall template material is prepared from the following substances in parts by weight: 25-35 parts of Portland cement, 10-15 parts of pottery clay powder, 5-10 parts of fly ash, 5-10 parts of sepiolite, 1-5 parts of basalt fiber, 5-10 parts of glass fiber, 1-5 parts of chitosan, 1-5 parts of nano silicon aerogel powder, 5-10 parts of calcium oxide, 1-2 parts of an insect-resist agent and 1-2 parts of a flame retardant. The surface of the wall formwork is subjected to micro-carving treatment, the adhesive force of all components on the wall formwork is improved, natural falling is prevented, the service life is prolonged, under the action of basalt fibers and glass fibers, the strength of the wall formwork can be improved, then the supporting requirement in construction can be reduced, separation of a poured wall can be promoted, and the pouring wall body is better protected.

Description

technical field [0001] The invention relates to the field of construction, in particular to a non-stick wall formwork material and a preparation method. Background technique [0002] As people's demand for building houses is increasing, the traditional form of brick and stone construction has evolved into the pouring method, which can complete the construction of building houses with high construction efficiency. [0003] After the poured wall is solidified and dried, the wall formwork for pouring needs to be removed. Due to the adhesion of the poured concrete, after the wall formwork is disassembled, a layer of the surface of the wooden wall formwork will stick to the poured wall. In fact, this will cause damage to the wall formwork. During the demolition process, not only is it laborious and time-consuming, but a little carelessness will cause damage to the pouring wall, and the current wooden wall formwork needs a lot of support to meet the use requirements. very trouble...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04E04G11/08
CPCC04B28/04E04G11/08C04B2111/2092C04B14/361C04B14/042C04B14/42C04B14/4643C04B14/064C04B18/08C04B22/064C04B24/38C04B2103/63C04B2103/67
Inventor 刘敬德
Owner 天造机器人科技(广东)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap