Antioxidant red mud doped coating for high-temperature steel billet

A technology for anti-oxidation coatings and steel billets, applied in fire-resistant coatings, alkali metal silicate coatings, coatings, etc., can solve problems such as environmental pollution, high cost, and complicated preparation procedures, and achieve rich sources, low pollution, and simple processes. Effect

Inactive Publication Date: 2021-06-25
GUILIN UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Given Al 2 o 3 or SiO 2 The preparation process of the high-temperature anti-oxidation protective coating made of aggregate is cumbersome and the cost is relatively high, and the waste residue of the chromium-containing anti-oxidation coating after cooling and peeling off will cause serious environmental pollution and other problems. The technical problems solved by the present invention include: high temperature anti-oxidation The paint preparation process is simple, the cost is low, and the applicability is wide. The oxidation resistance of the steel material coating during the heating process is strong, and it does not contain chromium that pollutes the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antioxidant red mud doped coating for high-temperature steel billet
  • Antioxidant red mud doped coating for high-temperature steel billet
  • Antioxidant red mud doped coating for high-temperature steel billet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A high temperature antioxidant rediscal scaly coating according to the present embodiment consists of a mixed powder, a binder, a dispersant solvent. Among them, the mixed powder is from the following mass percent components as: a red mud powder 16.8%, silica powder, 16.8% alumina powder, 8.3% graphite powder, 1.7% magnesium oxide powder, high temperature adhesion 6%, dispersant 0.4%. The main components of the red mine powder in the above mixed powder are silica, alumina, calcium oxide, magnesium oxide, oxide, and iron oxide. The high-temperature binder in the high temperature antioxidant rediscal coating of the present embodiment is sodium silicate, and the dispersant is carboxymethylcellulose, and the solvent is selected from 50% of the total mass.

[0031] The preparation method of high temperature antioxidant rediscal doped coating of the present invention is:

[0032] Step 1: Preparation of modified red mud powder. 20 g of raw red musteads and 2 g of alumina powder we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an antioxidant red mud doped coating for a high-temperature steel billet. The coating comprises red mud, silicon dioxide, carboxymethyl cellulose, aluminum oxide, magnesium oxide, graphite powder, sodium silicate and water. The mixed powder comprises the following main components in percentage by mass: 15-50% of red mud powder, 20-60% of silicon dioxide powder, 15-75% of aluminum oxide powder, 1-20% of graphite powder, 1-20% of magnesium oxide powder, 5-15% of a high-temperature binder and 0.4-1% of a dispersant. According to the invention of the anti-oxidation coating, the utilization value of the red mud is improved, the treatment capacity of red mud waste is increased, and the pressure of the red mud on the environment is reduced; The antioxidation coating is low in preparation cost and small in environmental pollution, does not pulverize or crack in a high-temperature environment after being brushed, sprayed or dip-coated on a steel billet, forms a layer of compact protection film on the surface of the steel billet, and has good anti-oxidation performance in the heating and heat preservation processes of the steel billet.

Description

Technical field [0001] The present invention relates to the field of high temperature antioxidant protection of the steel, and also relates to the field of recovery of metallurgical solid waste recovery. Background technique [0002] Metal and alloy materials are heated to a certain temperature in various industrial furnaces before completing the die forging, rolling, annealing, quenching and normalizing. During high temperature heating, the oxidation of steel is inevitable, the longer the heating time, the higher the heating temperature, the more severe the oxidation of the steel parts. In addition, it is easy to oxidize during high temperature heating in the alloy element in the steel, and it is difficult to peel off the oxide layer, and the surface defects are formed in the metal rolling or forging process, which can cause rolling for injection. According to statistics, the oxidation caused by the heating of steel products around the world has more than 10%, leading to huge wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/04C09D7/61
CPCC09D1/04C09D5/18C09D7/61
Inventor 孟征兵胡浩张鑫周颖
Owner GUILIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products