A fire-proof and heat-insulating material and its preparation method and application

A technology of thermal insulation materials and coatings, applied in textiles and papermaking, structural parts, electrical components, etc., can solve the problems of poor tear strength and cumbersome preparation methods of silicone packages, and achieve excellent high temperature resistance, simple preparation methods, The effect of good mechanical properties and electrical properties

Active Publication Date: 2022-02-18
深圳市富程威科技股份有限公司
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tear strength of the silicone package provided in this technical solution is poor, and the preparation method is loaded down with trivial details

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A fire-proof and heat-insulating material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0078] This embodiment provides a fire-proof and heat-insulating material and a preparation method thereof. The fire-proof and heat-insulating material includes a base layer and a coating layer that fit together; the base layer is a glass fiber cloth layer with a thickness of 0.5 mm, and the coating layer is The thickness is 0.5mm;

[0079] The paint layer is prepared from paint;

[0080] The coating includes the following components in parts by weight: 25 parts of vinyl raw rubber, 28 parts of fumed silica, 50 parts of flame retardant, 6 parts of porcelain-forming filler, 3 parts of vinyltrimethoxysilane, 2,5 - 2 parts of dimethyl-2,5-bis (tert-butyl peroxy) hexane, 0.5 part of platinum catalyst and 0.7 part of 1-ethynyl cyclohexanol; the flame retardant consists of decabromodiphenyl ether and Aluminum hydroxide is composed in a mass ratio of 2:1; the porcelain-forming filler is composed of mica powder, silicon micropowder and glass powder in a mass ratio of 1:1:1.

[0081]...

Embodiment 2

[0088] This embodiment provides a fire-proof and heat-insulating material and a preparation method thereof. The fire-proof and heat-insulating material includes a base layer and a paint layer that fit together; the base layer is a glass fiber cloth layer with a thickness of 0.8 mm, and the paint layer is The thickness is 0.7mm;

[0089]The paint layer is prepared from paint;

[0090] The coating includes the following components in parts by weight: 28 parts of vinyl raw rubber, 30 parts of fumed silica, 55 parts of flame retardant, 3 parts of glass powder, 1-5 parts of vinyl triethoxysilane, over 1 part of di-tert-butyl oxide, 0.3-1 part of platinum catalyst and 0.3 part of dibutyl maleate; the flame retardant is composed of decabromodiphenylethane and aluminum hydroxide in a mass ratio of 1:1.

[0091] The preparation method of the above-mentioned fire-proof and heat-insulating material comprises the following steps:

[0092] (1) Knead vinyl raw rubber and fumed silica for ...

Embodiment 3

[0098] This embodiment provides a fire-proof and heat-insulating material and a preparation method thereof. The fire-proof and heat-insulating material includes a base layer and a paint layer that fit together; the base layer is a glass fiber cloth layer with a thickness of 0.2 mm, and the paint layer is The thickness is 0.3mm;

[0099] The paint layer is prepared from paint;

[0100] The coating comprises the following components in parts by weight: 20 parts of vinyl raw rubber, 20 parts of fumed silica, 40 parts of flame retardant, 8 parts of mica powder, vinyl tris(2-methoxyethoxy) 1 part of silane, 3 parts of dicumyl peroxide, 0.3 part of platinum catalyst and 0.5 part of methyl-1-butyn-3-alcohol; the flame retardant consists of tetrabromobisphenol A and aluminum hydroxide in mass ratio 3:1 composition.

[0101] The preparation method of the above-mentioned fire-proof and heat-insulating material comprises the following steps:

[0102] (1) Knead vinyl raw rubber and fum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a fire-proof and heat-insulating material as well as a preparation method and application thereof. The fire-proof and heat-insulating material includes a bonded base layer and a paint layer; the paint layer is prepared from a paint; the paint includes the following components in parts by weight: 20-30 parts of raw rubber, 20-30 parts of reinforcing agent , 40-60 parts of flame retardant, 3-10 parts of porcelain filler, 1-5 parts of silane coupling agent and 1-3 parts of vulcanizing agent. Knead raw rubber and reinforcing agent to obtain rubber compound A, knead compound rubber A, flame retardant, filler and optional catalyst, inhibitor to obtain compound rubber B, mix it with vulcanizing agent to obtain Mixed rubber C, coated with a silane coupling agent on any side of the base layer; the side coated with the silane coupling agent of the base layer and the mixed rubber B are calendered and then vulcanized to prepare a fireproof and heat insulating material. The fireproof and heat insulating material provided by the invention has good flame retardancy, high temperature resistance and heat insulation, and good mechanical and electrical properties.

Description

technical field [0001] The invention belongs to the technical field of new energy batteries, and in particular relates to a fire-proof and heat-insulating material and its preparation method and application. Background technique [0002] With the development of society and the improvement of people's awareness of environmental protection, electric vehicles have received more and more attention. As the energy source of electric vehicles, the safety of batteries is particularly important. During the use of new energy vehicles, temperature has an important impact on the performance of the battery. The charging and discharging reaction of the battery occurs within a certain temperature. If the temperature is too high or too low, the battery will be difficult to work or the working efficiency will be low. Moreover, during the working process of the battery, with the occurrence of chemical reactions, the internal temperature of the battery is not equal to the ambient temperature,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/04D06N3/00D06M13/513H01M50/231H01M50/229
CPCD06N3/04D06N3/0059D06N3/0063D06N3/0022D06N3/0088D06M13/5135D06N2209/067D06N2209/065D06N2209/103
Inventor 岑海波姜金燕
Owner 深圳市富程威科技股份有限公司