A graphene-modified laser absorbing layer coating and coating method thereof

A graphene modification and laser absorption technology, which is applied in the field of surface treatment of parts, can solve the problems of poor coating quality, low efficiency, and poor quality uniformity of the laser absorption layer, and achieve improved laser ablation resistance and reduced The effect of improving damage rate and laser energy utilization rate

Active Publication Date: 2022-04-19
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the invention is: to propose a graphene-modified laser absorbing layer coating and its coating method, which can solve the difficult problems of poor coating quality, low efficiency, and poor quality uniformity of the laser absorbing layer of complex parts, and reduce the The probability of damage to the laser absorbing layer improves the surface quality of laser shock strengthening of complex parts and meets the needs of high-quality complex parts for anti-fatigue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A graphene-modified laser absorbing layer coating and coating method thereof
  • A graphene-modified laser absorbing layer coating and coating method thereof
  • A graphene-modified laser absorbing layer coating and coating method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The invention discloses a graphene-modified laser absorbing layer coating, which is mainly composed of polyurethane resin, black auxiliary material, functional auxiliary agent and deionized water. Wherein, polyurethane resin (50%), black auxiliary material (20%), functional auxiliary agent (10%) and deionized water (20%) are all percentages by mass; polyurethane resin is an aqueous emulsion with a solid content of 10% (mass percentage); black auxiliary material is the carbon black that comprises graphene powder, and the content of graphene is 1.0% (mass percentage); Functional auxiliary agent is sodium stearate.

[0038] The coating method of the laser absorbing layer coating of this graphene modification, the step of coating is as follows:

[0039] (1) Part surface cleaning: use alcohol ultrasonic cleaning to clean the surface of the part to be strengthened by laser shock;

[0040] (2) Coating preparation: Add graphene powder into deionized water to form graphene slur...

Embodiment 2

[0044] The contents of polyurethane resin, black auxiliary material, functional auxiliary agent and deionized water of the coating are X, Y, Z and R respectively, wherein X=70%, Y=15%, Z=10%, R=5% , both are mass percentages. In addition, the polyurethane resin is an aqueous emulsion with a solid content of 60% (mass percentage); the black auxiliary material is iron oxide black containing water-based graphene slurry, and the content of graphene is 5.0% (mass percentage);

[0045] The coating method of the laser absorbing layer coating of this graphene modification, the step of coating is as follows:

[0046] (1) Part surface cleaning: Use alcohol dipped in gauze to wipe the surface of the part to be laser shock strengthened;

[0047] (2) Coating preparation: add the water-based graphene slurry into deionized water to form a graphene slurry, then ultrasonically disperse iron oxide black in the graphene slurry, and then add the mixed slurry to the water-based polyurethane resin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of parts surface treatment, and relates to a graphene-modified laser absorbing layer coating and a coating method thereof; the coating is mainly composed of polyurethane resin, black auxiliary materials, functional additives and deionized water; the invention uses graphite After olefin modification, a higher amplitude and deeper surface residual compressive stress distribution is produced on the surface of the part. The laser absorbing layer coating is coated on the surface of the part by high-pressure gas-driven spraying. After drying, a coating with uniform thickness is obtained on the surface of the complex part, and the bonding force between the coating and the part is good. It can be removed by hand peeling. The method has the advantages of high coating efficiency, good quality reliability, and high removal efficiency, and is beneficial to the processing of complex parts and its mass production.

Description

technical field [0001] The invention belongs to the technical field of parts surface treatment, and relates to a graphene-modified laser absorbing layer coating and a coating method thereof. Background technique [0002] Laser shock strengthening is an advanced surface strengthening technology, which uses the mechanical effect of high-energy plasma shock waves induced by lasers to generate plastic deformation layers and residual compressive stress layers on the surface of parts, thereby improving the fatigue performance of parts. Laser pulses are not directly irradiated on the surface of the part, but indirectly irradiated on the laser absorbing layer on the surface of the part. The absorbing layer has high laser energy absorption rate, heat insulation and excellent comprehensive mechanical properties. At present, the commonly used laser absorbing layer is black tape or aluminum foil, which is manually pasted on the surface of the part. This method has the advantages of sim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D7/61B05D1/02B05D7/24
CPCC09D175/04C09D7/61B05D7/24B05D1/02B05D2503/00B05D2301/00C08K2003/2275C08K3/042C08K3/04C08K3/22
Inventor 罗学昆杨瑞王欣王强马世成许春玲宇波于洋
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com