A glass fiber cloth reinforced insulating molded board and its preparation method

A glass fiber cloth and molding technology, which is applied in the field of molded boards, can solve problems such as high temperature resistance, mechanical properties that cannot meet actual needs, poor flame retardancy, and flammability, and achieve excellent high temperature resistance, excellent mechanical properties, and component distribution. more suitable effect

Active Publication Date: 2021-10-29
广东纵胜新材料股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Epoxy resin laminates have excellent mechanical properties, electrical insulation properties and easy processing properties, and are widely used in chemical, mechanical, and electrical fields. However, conventional epoxy resin laminates on the market are flammable and have poor flame retardancy. Moreover, the high temperature resistance and mechanical properties cannot meet the actual needs, which brings inconvenience to the actual application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A glass fiber cloth reinforced insulating molded board and its preparation method
  • A glass fiber cloth reinforced insulating molded board and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method of an insulating molded board reinforced by glass fiber cloth, comprising the following steps:

[0038] (1) Take 4-hydroxyphenylboronic acid and tetrahydrofuran, mix them evenly in an ice-water bath at 0°C, then add triethylamine and tetrahydrofuran solution of phenylphosphoryl dichloride, keep warm for 2 hours, then raise the temperature to 25°C, and continue the reaction for 10 hours , after the reaction is finished, it is filtered and washed, and dried in vacuum at 60°C for 24 hours to obtain a flame retardant;

[0039] (2) Take dichloromethane, phenylene anhydride, phenylacetylene and triethylamine, mix and stir for 20 minutes, react at 25°C for 9 hours, filter and wash with suction, and recrystallize to obtain material A;

[0040] Take material A, transfer it to acetone under a nitrogen atmosphere, add an aminosilane coupling agent, react at 25°C for 3 hours, remove the acetone, and obtain a modified silane coupling agent; the aminosilane coupl...

Embodiment 2

[0046] A preparation method of an insulating molded board reinforced by glass fiber cloth, comprising the following steps:

[0047] (1) Take 4-hydroxyphenylboronic acid and tetrahydrofuran, mix them evenly in an ice-water bath at 0°C, then add triethylamine and a tetrahydrofuran solution of phenylphosphoryl dichloride, keep the temperature for 2.5 hours, then raise the temperature to 27°C, and continue the reaction 9h, after the reaction was completed, it was filtered and washed with suction, and vacuum-dried at 65°C for 22h to obtain a flame retardant;

[0048] (2) Take dichloromethane, metaphthalic anhydride, phenylacetylene and triethylamine, mix and stir for 25 minutes, react at 28°C for 8.5 hours, wash with suction, and recrystallize to obtain material A;

[0049] Take material A, transfer it to acetone under nitrogen atmosphere, add aminosilane coupling agent, react at 28°C for 2.5h, remove acetone, and obtain modified silane coupling agent; the aminosilane coupling agen...

Embodiment 3

[0055] A preparation method of an insulating molded board reinforced by glass fiber cloth, comprising the following steps:

[0056] (1) Take 4-hydroxyphenylboronic acid and tetrahydrofuran, mix them evenly in an ice-water bath at 0°C, then add triethylamine and tetrahydrofuran solution of phenylphosphoryl dichloride, keep the temperature for 3 hours, then raise the temperature to 28°C, and continue the reaction for 8 hours , after the reaction is finished, it is filtered and washed, and vacuum-dried at 70° C. for 20 hours to obtain a flame retardant;

[0057] (2) Take dichloromethane, phenylene anhydride, phenylacetylene and triethylamine, mix and stir for 30 minutes, react at 30°C for 8 hours, filter and wash with suction, and recrystallize to obtain material A;

[0058] Take material A, transfer it to acetone under a nitrogen atmosphere, add an aminosilane coupling agent, react at 30°C for 2 hours, remove the acetone, and obtain a modified silane coupling agent; the aminosil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass fiber cloth-reinforced insulating molded board and a preparation method thereof. Adhesiveness and permeability, when the alkali-free glass fiber cloth is impregnated, this application adds modified silane coupling agent, citric acid, sodium hypophosphite to mix, the introduction of modified silane coupling agent, citric acid, sodium hypophosphite The synergistic effect of the components can effectively improve the high temperature resistance and flame retardancy of the glass fiber cloth; the molded plate prepared by the present invention not only has excellent mechanical properties, but also due to the modification of the flame retardant, the silane coupling agent Modified treatment, the molded plate has excellent high temperature resistance, flame retardancy, can be applied to a variety of environmental uses, and has high practicability.

Description

technical field [0001] The invention relates to the technical field of molded boards, in particular to a glass fiber cloth reinforced insulating molded board and a preparation method thereof. Background technique [0002] Molded board, also called laminated board, is a kind of laminated product. A laminated product is a whole made of two or more layers of resin-impregnated fibers or fabrics that are laminated and bonded by heat and pressure. Laminated products can be processed into various insulating and structural parts, which are widely used in motors, transformers, high and low voltage electrical appliances, electrical instruments and electronic equipment. [0003] Epoxy resin laminates have excellent mechanical properties, electrical insulation properties and easy processing properties, and are widely used in chemical, mechanical, and electrical fields. However, conventional epoxy resin laminates on the market are flammable and have poor flame retardancy. Moreover, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/08C08L63/04C08L63/00C08L13/00C08K3/22C08K5/55C08K9/06C08K7/14
CPCC08J5/08C08J2363/04C08J2413/00C08J2463/00C08K5/55C08K2003/2227C08K2201/011
Inventor 张宗权何辉春
Owner 广东纵胜新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com