A kind of metal glazed tile and preparation method thereof
A technology of glazed tiles and metallic glazes, which is applied in the field of ceramic tiles, can solve the problems of three-dimensionality, poor layering, and the inability to realize filigree inlaid gold and copper weaving, etc., and achieve the effect of strong three-dimensionality, obvious layering, and good metal texture
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0058] Glazed metal ( image 3 For glazed metal front view), comprising sequentially disposed from the bottom blank 1, the end of the glaze layer 2, layer 3 pattern, texture layer 4, the surface glaze layer 5, a metal glaze layer 6.
[0059] The ground coat glaze layer 3 comprises in parts by weight by parts of ball clay, 99 parts of enamel powder, sodium tripolyphosphate 0.4 parts, 0.25 parts of sodium carboxymethyl cellulose. The glaze powder into the parts by weight basis comprises: 48 parts silica, 23 parts of aluminum oxide, ferric oxide 0.15 parts, 0.08 parts of titanium dioxide, 9.8 parts calcium oxide, 3.8 parts of magnesium oxide, 0.15 parts of potassium hydroxide, sodium oxide 5.20 parts, 0.01 parts of zirconium dioxide, barium oxide, 0.08 parts, 0.45 parts of phosphorus pentoxide, 0.08 parts of zinc oxide. The bottom layer of the glaze frit mixed water as a solvent, having a density of 1.80 g / ml.
[0060] The texture layer prepared using oil-based ink inorganic ceramic...
Embodiment 2
[0072] Metal glazed tiles, comprising sequentially disposed from the bottom element 1, the bottom of the glaze layer 2, layer 3 pattern, texture layer 4, the surface glaze layer 5, a metal glaze layer 6.
[0073] The bottom layer of enamel frit by ball clay comprises in parts by weight 2 parts to 98 parts of the glaze powder, 0.3 parts of sodium tripolyphosphate, 0.2 parts of sodium carboxymethyl cellulose. The glaze powder into the parts by weight basis comprises: 48 parts silica, 22 parts of aluminum oxide, ferric oxide 0.10 parts, 0.05 parts of titanium dioxide, 9.5 parts calcium oxide, 3.5 parts of magnesium oxide, 0.10 parts of potassium hydroxide, sodium oxide 5.00 parts, 0.05 barium oxide, 0.40 parts of phosphorus pentoxide, 0.05 parts of zinc oxide. The bottom layer of the glaze frit mixed water as a solvent, having a density of 1.75 g / ml.
[0074] The texture layer prepared using oil-based ink inorganic ceramic obtained by the oil-based ink inorganic ceramic comprising ...
Embodiment 3
[0086] Metal glazed tiles, comprising sequentially disposed from the bottom element 1, the bottom of the glaze layer 2, layer 3 pattern, texture layer 4, the surface glaze layer 5, a metal glaze layer 6.
[0087] The ground coat glaze layer 5 comprises in parts by weight by parts of ball clay, glaze powder into 100 parts, 0.5 parts of sodium tripolyphosphate, 0.3 parts of sodium carboxymethyl cellulose. The glaze powder into the parts by weight basis comprises: 49 parts silica, 23 parts of aluminum oxide, ferric oxide 0.20 parts, 0.10 parts of titanium dioxide, 10.0 parts calcium oxide, 4.0 parts of magnesium oxide, 0.20 parts of potassium hydroxide, sodium oxide 5.50 parts, 0.01 parts of zirconium dioxide, barium oxide, 0.10 parts, 0.50 parts of phosphorus pentoxide, 0.10 parts of zinc oxide. The bottom layer of the glaze frit mixed water as a solvent, having a density of 1.85 g / ml.
[0088] The texture layer prepared using oil-based ink inorganic ceramic obtained by the oil-ba...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| gloss | aaaaa | aaaaa |
Abstract