Cement-based water-in-water multicolor paint

A multi-color paint, cement-based technology, applied in cement paint, multi-color effect paint, coating and other directions, can solve the problems of durability and poor weather resistance, and achieve the effect of reducing material cost, suppressing efflorescence, and beautiful decorative effect.

Pending Publication Date: 2021-11-12
许敬修
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the durability, weather resistance and other performances of the existing water-in-water multicolor coatings are all determined by the performance of the polymer emulsion of organic materials, resulting in poor durability and weather resistance, and its artificial weather aging resistance time is only 1000h. Compared with the service life of the building > 50 years, it is too different

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The cement-based water-in-water colorful paint is composed of the following materials by weight:

[0021] Cement-based color pellet slurry parts by weight flame retardant 10 6mm glass fiber (silanized) 0.3 Alkali inhibitor 0.5 Superplasticizer 0.3 water 17.77 lubricant 0.1 Dispersant 0.12 Defoamer 0.003 Coalescent 0.1 antifreeze 0.13 plasticizer 0.08 preservative or fungicide 0.1 Hydroxyethyl cellulose 0.1 Acrylic Emulsion 16 pigment 0.5 Sulphoaluminate cement 40 800 mesh sericite powder (silanized treatment) 7 120 mesh quartz sand (silanized treatment) 7

[0022] The protective slurry adopts the raw materials and methods for preparing the protective slurry of the water-in-water colorful paint in the prior art.

Embodiment 2

[0024] On the basis of the first embodiment, the following materials are also included:

[0025] bridging lotion parts by weight water 30 Dispersant 0.7 Coalescent 0.81 antifreeze 0.8 lubricant 0.5 preservative or fungicide 0.7 plasticizer 0.3 Acrylic Emulsion 69.5 6mm glass fiber (silanized) 0.5

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cement-based water-in-water multicolor paint which is composed of cement primary color granular slurry and protective slurry; and the cement primary color granular slurry comprises the following components in parts by weight: 30-70 parts of cement, 20-70 parts of aggregate, 0.6-5 parts of pigment, 6-40 parts of mixed glue solution of polymer emulsion or redispersible polymer glue powder and water, and 5-40 parts of water. The paint has the remarkable advantages of durability and extremely excellent weather resistance. After 2160 hours of an all-weather aging test, the performance of the mortar is still the same with that of cement mortar and even improved while the performance of an existing product only reaches 1000 hours. The super-high durability of the cement and the flexibility of the polymer are realized. The comprehensive performance is excellent. Saltpetering is obviously inhibited or avoided, and the decorative effect is exquisite. The acid and alkali resistance and anti-freeze-thaw performance are high, the cost is low, and particularly, compared with a building with the service life of more than or equal to 50 years, the maintenance cost of the whole life cycle of the building is reduced by several times, and the paint is suitable for outer walls, inner walls and roofs of the building.

Description

technical field [0001] The invention relates to the technical field of the preparation of water-in-water colorful paints, in particular to the realization of chemical interaction through the combination of cement and polymers to generate ionic bonds, and fibers interspersed with each other. A cement-based water-in-water colorful paint with dual characteristics of polymer reaction curing and emulsion volatilization curing. Background technique [0002] The existing water-in-water colorful paint is made by dispersing water-based color particles in a system composed of water-based film-forming substances, pigments, fillers, water, auxiliary agents, etc., wherein the filler itself does not generate strength due to hydration reaction, and it is closely related to the film-forming material. There are few chemical reactions between substances that enhance the bond strength. During construction, after spraying into a colorful coating, with the volatilization of water, the emulsion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/08C09D7/61C09D7/62C09D7/65C09D5/29
CPCC09D1/08C09D7/61C09D7/62C09D7/70C09D7/65C09D5/29
Inventor 许浒许敬修
Owner 许敬修
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com