Fine powder titanium agent for producing aluminum alloy and preparation method of fine powder titanium agent

A technology of aluminum alloy and fine powder, which is applied in the production of aluminum alloy fine powder titanium agent and its preparation field, can solve the problems of reducing the utilization rate of fine powder titanium agent, not having the ability to remove hydrogen, and not being able to change the viscosity of materials, etc., to achieve Increased ability to remove hydrogen, obvious synergistic effect, and reduced waste of raw materials and energy

Pending Publication Date: 2021-11-23
TONGSHAN COUNTY FENGHUA IND & TRADE
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the existing fine powder titanium agent for producing aluminum alloys still has some deficiencies, for example; the existing fine powder titanium agent for producing aluminum alloys does not have obvious synergistic effect of each component in smelting, It cannot play the role of lowering the melting point in the aluminum alloy production process, and cannot change the viscosity of the material, so that the fluidity of the material is weakened, the metal and the slag phase are separated more easily, and the waste of raw materials and energy in the aluminum alloy production process is increased. and the cost of aluminum alloy production, the existing fine powder titanium agent cannot spread on the surface of the aluminum melt, break and adsorb the oxides on the surface of the melt at the melting temperature, the adsorption capacity of the solvent is relatively weak, and it does not have the ability to remove hydrogen , the impurity removal effect is not obvious, which reduces the utilization rate of fine powder titanium

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The invention provides a technical solution: a fine powder titanium agent for producing aluminum alloy and its preparation method, comprising the following raw materials and their weight fractions: titanium powder is 80-90% by mass; aluminum powder is 5-15% parts by mass; the flux is 2-3% by mass; the surfactant is 2-3% by mass; the refining agent is 1-2% by mass and the dispersant is 1-2% by mass.

[0031] Further, the fine powder titanium agent for producing aluminum alloys includes the following raw materials and their weight fractions: 89% by mass of titanium powder; 5% by mass of aluminum powder; 2% by mass of flux; The agent is 2% by mass; the refining agent is 1% by mass and the dispersant is 1% by mass.

[0032] Further, the fine powder titanium agent for producing aluminum alloys includes the following raw materials and their weight fractions: 80% by mass of titanium powder; 10% by mass of aluminum powder; 3% by mass of flux; The agent is 3% by mass; the refin...

Embodiment 1

[0050] The described fine powder titanium agent for producing aluminum alloy comprises the following raw materials and their weight fractions: titanium powder is 89% by mass; aluminum powder is 5% by mass; flux is 2% by mass; surfactant is 2% by mass; 1% by mass of refining agent and 1% by mass of dispersant.

[0051] The preparation steps are as follows:

[0052] a. taking the above-mentioned raw materials according to parts by weight;

[0053] b. After step a is completed, put the weighed titanium powder, aluminum powder, flux, surfactant, refining agent and dispersant into the mixer for mixing. The mixing speed is 700r / min. The time of mixing is 40min, makes mixture A;

[0054] c. After step b is completed, the mixture A is put into the production mold for compression molding to obtain a fine powder titanium agent;

[0055] d. After step c is completed, dry, detect and pack the compressed titanium powder.

Embodiment 2

[0057] The described fine powder titanium agent for producing aluminum alloy comprises the following raw materials and their weight fractions: titanium powder is 80% by mass; aluminum powder is 10% by mass; flux is 3% by mass; surfactant is 3% by mass; 2% by mass of refining agent and 2% by mass of dispersant.

[0058] The preparation steps are as follows:

[0059] a. taking the above-mentioned raw materials according to parts by weight;

[0060] b. After step a is completed, put the weighed titanium powder, aluminum powder, flux, surfactant, refining agent and dispersant into the mixer for mixing. The mixing speed is 700r / min. The time of mixing is 40min, makes mixture A;

[0061] c. After step b is completed, the mixture A is put into the production mold for compression molding to obtain a fine powder titanium agent;

[0062] d. After step c is completed, dry, detect and pack the compressed titanium powder.

[0063] The traditional fine powder titanium agent data paramet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a fine powder titanium agent for producing an aluminum alloy and a preparation method of the fine powder titanium agent. The fine powder titanium agent comprises the following raw materials in percentage by mass: 80%-90% of titanium powder, 5%-15% of aluminum powder, 2%-3% a fluxing agent, 2%-3% a surfactant, 1%-2% of a fining agent and 1%-2% of a dispersing agent. According to the fine powder titanium agent for producing the aluminum alloy and the preparation method of the fine powder titanium agent, the synergistic effect of all components in smelting of the fine powder titanium agent is obvious, the effect of reducing the melting point in the aluminum alloy production process is achieved, the fluidity of materials is enhanced, metal and slag phases are separated more easily, waste of raw materials and energy in the aluminum alloy production process is reduced, oxide on the surface of melt can be broken and adsorbed, the adsorption capacity of a solvent is improved, the hydrogen removal capacity is improved, and the utilization rate of the fine powder titanium agent is increased.

Description

technical field [0001] The invention relates to the technical field of fine powder titanium agent, in particular to a fine powder titanium agent for producing aluminum alloy and a preparation method thereof. Background technique [0002] Titanium powder, titanium hydride powder: Purity: 95-99.4%, etc. Various specifications and properties: Titanium powder: The product is silver-gray irregular powder, has a large air absorption capacity, and is flammable under high temperature or electric spark conditions. Titanium hydride powder: The product is black gray irregular powder. Uses Titanium powder and titanium hydride powder are metal powders with a wide range of uses. It is an additive for powder metallurgy and alloy materials. At the same time, it is also an important raw material for cermets, surface coating agents, aluminum alloy additives, electric vacuum getters, spraying, and plating. [0003] With the continuous development of aluminum processing and aluminum alloy in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C14/00C22C21/00C22C1/05C22C1/06C22C1/10
Inventor 张华任浩浩林恒
Owner TONGSHAN COUNTY FENGHUA IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap