Wood bleaching method based on microelectronic technology
A microelectronic technology, wood technology, applied in wood treatment, wood impregnation, wood impregnation, etc., can solve the problems of insufficient absorption of bleaching solvents, uneven color of wood, dull color, etc., to avoid excessive yellowing of bleaching, and improve penetration. The effect of improving efficiency and swelling degree
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0030] A kind of wood bleaching method based on microelectronic technology, comprises the raw material of following mass fraction:
[0031] Wood; penetrating agent 15 parts; anhydrous sulfuric acid 3 parts; magnesium carbonate 2 parts; borax 5 parts; glycerin 3 parts; urea 9 parts; hydrogen peroxide 800 parts; ammonium bicarbonate 1.5 parts; sodium persulfate 0 .5 parts; 5 parts of ionic liquid-based protective agent;
[0032] According to described a kind of wood bleaching method based on microelectronic technology, a kind of preparation method of this wood is proposed now, comprises the following steps:
[0033] S1, peeling, take out the logs that need to be processed, and peel the logs according to the required thickness, the thickness is 1.1mm ~ 2.5mm;
[0034] S2. Pretreatment before bleaching: inject 5 parts of ionic liquid-based protective agent into the first vacuum tank, and soak the planed wood in the first vacuum tank together for 2-3 hours to fully absorb the ioni...
Embodiment 2
[0042] A kind of wood bleaching method based on microelectronic technology, comprises the raw material of following mass fraction:
[0043] Wood; penetrating agent 16 parts; anhydrous sulfuric acid 4 parts; magnesium carbonate 3 parts; borax 6 parts; glycerin 3.5 parts; urea 10 parts; hydrogen peroxide 900 parts; ammonium bicarbonate 2 parts; sodium persulfate 1 part; 8 parts of ionic liquid-based protective agent;
[0044] According to described a kind of wood bleaching method based on microelectronic technology, a kind of preparation method of this wood is proposed now, comprises the following steps:
[0045] S1, peeling, take out the logs that need to be processed, and peel the logs according to the required thickness, the thickness is 1.1mm ~ 2.5mm;
[0046]S2. Pretreatment before bleaching, inject 8 parts of ionic liquid-based protective agent into the first vacuum tank, and put the peeled wood into the first vacuum tank for soaking for 2-3 hours to fully absorb the ioni...
Embodiment 3
[0054] A kind of wood bleaching method based on microelectronic technology, comprises the raw material of following mass fraction:
[0055] Wood; 17 parts of penetrant; 5 parts of anhydrous sulfuric acid; 4 parts of magnesium carbonate; 7 parts of borax; 4 parts of glycerin; 11 parts of urea; 1000 parts of hydrogen peroxide; .5 parts; 11 parts of ionic liquid-based protective agent;
[0056] According to described a kind of wood bleaching method based on microelectronic technology, a kind of preparation method of this wood is proposed now, comprises the following steps:
[0057] S1, peeling, take out the logs that need to be processed, and peel the logs according to the required thickness, the thickness is 1.1mm ~ 2.5mm;
[0058] S2. Pretreatment before bleaching, inject 11 parts of ionic liquid-based protective agent into the first vacuum tank, and put the peeled wood into the first vacuum tank for soaking for 2-3 hours to fully absorb the ionic liquid Based protective agen...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com