C2N/porous graphene composite material, preparation method thereof and diaphragm containing material

A technology of porous graphene and composite materials, applied in the field of lithium-sulfur batteries, can solve the problems of low energy density, poor cycle performance, and inability to effectively suppress the shuttle effect of lithium-sulfur batteries. The effect of conductivity

Active Publication Date: 2021-11-26
INST OF FLEXIBLE ELECTRONICS TECH OF THU ZHEJIANG
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commercial PP separators, due to their large pore size, allow polysulfides to pass through relatively easily, so they cannot effectively suppress the shuttle effect, resulting in problems such as low actual energy density and poor cycle performance of lithium-sulfur batteries.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • C2N/porous graphene composite material, preparation method thereof and diaphragm containing material
  • C2N/porous graphene composite material, preparation method thereof and diaphragm containing material
  • C2N/porous graphene composite material, preparation method thereof and diaphragm containing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Example 1 Preparation C 2 N / porous graphene composites

[0044] In the first step, graphene oxide was oxidized by hydrogen peroxide to form pores, and 5 mL of 30% hydrogen peroxide (H 2 o 2 ) solution was dropped into 50 mL graphene oxide (GO) aqueous solution (2 mg / mL), then heated at 95 °C for 4 h with continuous stirring, cooled to room temperature, and the product was collected by centrifugation at a speed of 10000 r / min , washed with deionized water to remove residual H 2 o 2 , and finally redispersed in deionized water to obtain a 2 mg / mL porous graphene oxide (HGO) suspension, and then freeze-dried to obtain a porous graphene oxide (HGO) aerogel.

[0045] In the second step, 100 mg of HGO was weighed, added to 100 mL of deoxygenated NMP for ultrasonic dispersion for 4 h, poured into a three-necked flask under a nitrogen atmosphere, and placed in an ice-water bath. 300 mg of hexaaminobenzene (HAB) was dissolved in 30 mL of deoxygenated N-methylpyrrolidone (NM...

Embodiment 2

[0048] Example 2 Preparation of diaphragm

[0049] With the C that embodiment 1 makes 2 N-HG was ultrasonically dispersed in ethanol solution, ultrasonicated for 1 h, and prepared into a uniform dispersion with a concentration of 0.1 mg / mL. Using a glass sand core funnel, the C 2 N-HG was suction-filtered on a PP membrane, then dried naturally, and then dried under reduced pressure at room temperature to obtain single-sided modified C 2 N / porous graphene modified PP separator, C 2 The loading capacity of N / porous graphene is 0.05mg / cm 2 , denoted as C 2 N-HG-P-0.05.

[0050] C prepared in this example 2 See the SEM picture of N-HG-PP-0.05 image 3 .

[0051] Adopt the C that this embodiment makes 2 The performance diagram of the lithium-sulfur battery made of N-HG-PP-0.05 separator cycled at 1 C rate for 300 cycles is shown in Figure 4 .

Embodiment 3

[0053] The same as the method of Example 2, the difference is that the obtained single-sided modified C 2 C in N / porous graphene modified PP separator 2 The loading of N / porous graphene is 0.1 mg / cm 2 , denoted as C 2 N-HG-P-0.1.

[0054] C prepared in this example 2 See the SEM picture of N-HG-PP-0.1 image 3 .

[0055] Adopt the C that this embodiment makes 2 The performance diagram of the lithium-sulfur battery made of N-HG-PP-0.1 separator at 1 C rate for 300 cycles is shown in Figure 4 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a C2N / porous graphene composite material, a preparation method thereof and a diaphragm containing the material. The preparation method of the C2N / porous graphene composite material comprises the following steps: a, forming pores in graphene oxide to obtain porous graphene oxide aerogel; and b, mixing the porous graphene oxide aerogel prepared in the step a, hexa-aminobenzene and cyclohexanehexone, and carrying out a heating reaction to prepare the C2N / porous graphene composite material. Wherein the mass ratio of the porous graphene oxide aerogel to the hexa-aminobenzene to the cyclohexanehexone is 1: (2-5): (2-5). The C2N / porous graphene composite material prepared by the invention can be used for modifying a diaphragm of a lithium-sulfur battery and effectively inhibiting a shuttle effect, so that the lithium-sulfur battery can keep relatively high energy density, and the cycle performance of the battery is improved.

Description

technical field [0001] The invention belongs to the technical field of lithium-sulfur batteries, in particular to a C 2 The N / porous graphene composite material and its preparation method further relate to a diaphragm comprising the composite material and its preparation method. Background technique [0002] With the rapid development of electric vehicles and electronic mobile devices, energy storage devices with higher energy density have become a research hotspot. Although the current specific energy of lithium-ion batteries has reached 250 Wh / kg, it is difficult to increase the specific energy due to the limitation of the specific capacity of the positive electrode material. At the same time, there is a huge security in increasing the specific energy by increasing the charging voltage Therefore, it is imminent to develop a new type of electrochemical energy storage system. Lithium-sulfur batteries are a new type of energy storage system that uses elemental sulfur or sul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B32/194C01B21/06H01M10/052H01M50/403H01M50/431
CPCC01B32/194C01B21/0605H01M50/431H01M50/403H01M10/052C01P2004/80C01B2204/22Y02E60/10
Inventor 陈鹏宋远强揭斌勇付际
Owner INST OF FLEXIBLE ELECTRONICS TECH OF THU ZHEJIANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More