Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of nano-diamond beauty makeup product

A nano-diamond, diamond single crystal technology, applied in diamond, cosmetic preparations, dressing preparations, etc., can solve the problems of high surface activity and thermodynamic instability of nano-diamonds, achieve good results, avoid the formation of impurities, and improve dispersion. sexual effect

Inactive Publication Date: 2021-12-10
HENAN UNIVERSITY OF TECHNOLOGY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the deepening of research, some problems have also been exposed, for example, nano-diamond has a higher specific surface energy, a larger specific surface area, and is in a thermodynamically unstable state. In addition, the surface activity of nano-diamond is also Very large, so agglomeration often occurs between particles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] a. Take 1.5g of nano-diamond and another 10ml of concentrated HNO 3 , slowly pour it into a beaker, mix well, heat at 80°C for 2 hours, pour the supernatant in the beaker into the waste liquid bucket, place the beaker containing the nano-diamond sink in a ventilated place, cool to room temperature, and let it stand for 18 hours ;

[0021] b. Put the treated nano-diamond into a crucible and put it into a vacuum tube furnace, and then fill it with nitrogen atmosphere after vacuuming for heat treatment: raise the temperature at a heating rate of 10°C / min, keep the temperature at 600°C for 2 hours, and turn it off after constant temperature Cool the atmosphere to 200°C, turn on the vacuum tube furnace, turn off the atmosphere, and naturally cool to room temperature;

[0022] c. Take the nano-diamond after nitrogen high-temperature heat treatment and add it to a dry and clean small beaker. Add concentrated hydrochloric acid. The amount of concentrated acid in the beaker sho...

Embodiment 2

[0025] a. Take 1.5g of nano-diamond and another 15ml of concentrated HNO 3 , slowly pour it into a beaker, mix well, heat at 90°C for 3 hours, pour the supernatant in the beaker into the waste liquid bucket, place the beaker containing the nano-diamond sink in a ventilated place, cool to room temperature, and let it stand for 20 hours ;

[0026] b. Put the processed nano-diamond into a crucible and put it into a vacuum tube furnace. After vacuuming, fill it with a nitrogen atmosphere for heat treatment: heat up at a heating rate of 15°C / min, and keep the temperature at 700°C for 2 hours. After constant temperature, turn it off. Cool the atmosphere to 200°C, turn on the vacuum tube furnace, turn off the atmosphere, and naturally cool to room temperature;

[0027] c. Take the nano-diamond after nitrogen high-temperature heat treatment and add it to a dry and clean small beaker. Add concentrated hydrochloric acid. The amount of concentrated acid in the beaker should completely i...

Embodiment 3

[0030] a. Take 1.5g of nano-diamond and another 20ml of concentrated HNO 3 , slowly pour it into a beaker, mix well, heat at 100°C for 4 hours, pour the supernatant in the beaker into the waste liquid bucket, place the beaker containing the nano-diamond sink in a ventilated place, cool to room temperature, and let it stand for 24 hours ;

[0031] b. Put the processed nano-diamond into a crucible and put it into a vacuum tube furnace. After vacuuming, fill it with a nitrogen atmosphere for heat treatment: heat up at a heating rate of 20°C / min, and keep the temperature at 800°C for 2 hours. After constant temperature, turn it off. Cool the atmosphere to 200°C, turn on the vacuum tube furnace, turn off the atmosphere, and naturally cool to room temperature;

[0032] c. Take the nano-diamond after nitrogen high-temperature heat treatment and add it to a dry and clean small beaker. Add concentrated hydrochloric acid. The amount of concentrated acid in the beaker should completely ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a nano-diamond beauty makeup product, and belongs to the field of diamond application. The preparation method comprises the following four parts: strong acid treatment of the nano-diamond, N2 atmosphere vacuum heat treatment, surface functionalization treatment of the nano-diamond, and combination of the nano-diamond and vitamin C. The method is simple to operate, the product has the properties of low toxicity, biocompatibility, chemical inertness, fluorescence effect and the like, and the nano-diamond can be combined with the skin surface, so that the transdermal moisture loss is reduced, the function of the water lipid skin surface is influenced, and the skin is protected from aging.

Description

technical field [0001] The patent of the present invention relates to the field of diamond applications, especially a method for preparing nano-diamond cosmetic products. Background technique [0002] From the discovery of the use of diamond to the synthesis of synthetic diamond, especially since the synthetic diamond in my country, the development of diamond has made great progress. For a long time in the past, various synthetic methods of diamond have provided a solid foundation for the application and research of diamond. Among them, nano-diamond has attracted the attention of many researchers because of its excellent properties, such as low toxicity, biocompatibility and large specific surface area, which are different from other materials, and they have been studied in depth. Its surface modification and modification, and then the research on combining with biological macromolecules is gradually carried out. [0003] At present, nano-diamonds are widely used in the fie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/67A61K8/19A61Q19/00A61Q19/02C01B32/28B82Y30/00B82Y40/00
CPCA61K8/19A61K8/676A61Q19/00A61Q19/02C01B32/28B82Y30/00B82Y40/00A61K2800/413A61K2800/592
Inventor 栗正新张鹏陈冰威黄雷波
Owner HENAN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com