A kind of anticorrosion coating containing hatn@ graphene and preparation method thereof

A graphene and coating technology, applied in the field of anti-corrosion coating containing HATN@graphene and its preparation, can solve the problems such as the decrease of electrochemical protection ability of anti-corrosion coating, the reduction of graphene's electrical conductivity, and the inability to protect, and the The barrier range is continuous, the dispersion is improved, and the effect of electrochemical protection is good

Active Publication Date: 2022-04-22
STATE GRID JIANGSU ELECTRIC POWER CO ELECTRIC POWER RES INST +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the compatibility of graphene with organic matter is poor, and it is difficult to disperse in organic matter, resulting in uneven coating and unable to play a complete protective role; at the same time, after being incorporated into organic matter, the structural defects of graphene sheets are exposed, reducing the The conductivity of graphene reduces the electrochemical protection ability of anti-corrosion coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anticorrosion coating containing hatn@ graphene and preparation method thereof
  • A kind of anticorrosion coating containing hatn@ graphene and preparation method thereof
  • A kind of anticorrosion coating containing hatn@ graphene and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Example 1: A HATN@graphene-containing anti-corrosion coating and its preparation method

[0040] The preparation method of the anti-corrosion coating containing HANT@graphene provided in this embodiment specifically includes the following steps:

[0041] Step 1, preparation of graphene oxide: at 0°C, slowly dissolve 2g of graphite and 1g of sodium nitrate in 46mL of concentrated sulfuric acid, slowly add 6g of potassium permanganate, and stir for 2 hours; Stir at 35°C for 2 hours, then raise the temperature to 95°C, slowly add 124mL of warm water and 30mL of 30% hydrogen peroxide to obtain a yellow solution without bubbles; use 5% hydrochloric acid and deionized water Repeated centrifugation and washing until the pH of the solution was neutral; finally dissolved in 100 mL of water, ultrasonicated for 3 hours, and freeze-dried to obtain graphene oxide powder.

[0042] Step 2. Preparation of HATN@graphene composite material: Take 200mg of graphene oxide powder and dissol...

Embodiment 2

[0045] Embodiment 2: A kind of anticorrosion coating containing HATN@graphene and its preparation method

[0046] The preparation method of the anti-corrosion coating containing HANT@graphene provided in this embodiment specifically includes the following steps:

[0047] The preparation method of the present invention comprises the steps:

[0048] Step 1, preparation of graphene oxide: at 0°C, slowly dissolve 2g of graphite and 1g of sodium nitrate in 46mL of concentrated sulfuric acid, slowly add 6g of potassium permanganate, and stir for 2 hours; Stir at 35°C for 2 hours, then raise the temperature to 95°C, slowly add 124mL of warm water and 30mL of 30% hydrogen peroxide to obtain a yellow solution without bubbles; use 5% hydrochloric acid and deionized water Repeated centrifugation and washing until the pH of the solution was neutral; finally dissolved in 100 mL of water, ultrasonicated for 3 hours, and freeze-dried to obtain graphene oxide powder.

[0049] Step 2. Prepar...

Embodiment 3

[0051] Embodiment 3: A kind of anticorrosion coating containing HATN@graphene and its preparation method

[0052] The preparation method of the anti-corrosion coating containing HANT@graphene provided in this embodiment specifically includes the following steps:

[0053] The preparation method of the present invention comprises the steps:

[0054] Step 1, preparation of graphene oxide: at 0°C, slowly dissolve 2g of graphite and 1g of sodium nitrate in 46mL of concentrated sulfuric acid, slowly add 6g of potassium permanganate, and stir for 2 hours; Stir at 35°C for 2 hours, then raise the temperature to 95°C, slowly add 124mL of warm water and 30mL of 30% hydrogen peroxide to obtain a yellow solution without bubbles; use 5% hydrochloric acid and deionized water Repeated centrifugation and washing until the pH of the solution was neutral; finally dissolved in 100 mL of water, ultrasonicated for 3 hours, and freeze-dried to obtain graphene oxide powder.

[0055] Step 2. Prepar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of anti-corrosion coatings, and relates to an anti-corrosion coating containing HATN@graphene and a preparation method thereof. The technical points are as follows: the anti-corrosion coating includes: epoxy resin, HANT@graphene, curing agent and auxiliary agent; among them, the mass fraction of HANT@graphene in the anti-corrosion coating is 0.02~0.4%. The present invention provides an anti-corrosion coating containing HATN@graphene composite material and its preparation method, wherein the HATN organic matter with nano-rod structure provides abundant redox groups, improving the compatibility between graphene and polymer matrix , making the barrier range of graphene sheets more continuous. In addition to the barrier effect of the graphene-enhanced coating, it can effectively reduce the potential difference between the inside and outside of the coating and achieve better electrochemical protection.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion coatings, and relates to an anti-corrosion coating containing HATN@graphene and a preparation method thereof. Background technique [0002] Metal corrosion and failure problems pervade all fields of the national economy, and are related to the safety of people's lives and property, industrial and agricultural production, and national defense construction. Most metal materials will corrode due to contact with corrosive environments. Metal corrosion is not only destructive but also extensive. Therefore, metal corrosion protection has become an important problem to be solved in the engineering field. Among many anti-corrosion measures, coating anti-corrosion has the advantages of wide adaptability, simple construction, low cost, and convenient maintenance. It has become the most widely used, economical and effective anti-corrosion method. [0003] In the prior art, graphene is usually incorpo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/08C09D7/62C09D7/63
CPCC09D163/00C09D5/08C09D7/62C09D7/63C08K9/12C08K3/042C08K5/34
Inventor 肖鹏刘建军
Owner STATE GRID JIANGSU ELECTRIC POWER CO ELECTRIC POWER RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap