Metal printing soft paint and preparation method thereof

A soft-feeling and coating technology, applied in polycarbonate coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as poor weather resistance, back-sticking of soft-touch coatings on iron printing, and unsatisfactory surface touch

Active Publication Date: 2022-03-25
广东鑫皇冠新材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]Based on this, in order to solve the problems of sticking back, poor stability, poor weather resistance and surface tactile feeling that cannot meet the requirements in the soft-feeling coating for printed iron in the prior art, the present invention provides A soft-feeling coating for printed iron is proposed, and the specific technical scheme is as follows:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal printing soft paint and preparation method thereof
  • Metal printing soft paint and preparation method thereof
  • Metal printing soft paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] In addition, the present invention also provides a preparation method of a soft-touch coating for iron printing, the preparation method for preparing the soft-touch coating for iron printing as claimed in any one of claims 1-8, comprising the following steps:

[0038] Add the raw materials of the composite matting agent to the ball mill, and mix it for 5min-10min at a speed of 1000r / min-1500r / min, then use it for later use;

[0039] Add the water-based mixed resin to the mixing kettle, heat it to 65°C-75°C, then add coupling agent, dispersant, curing agent, film-forming agent, defoamer and solvent, at a speed of 500r / min-800r / min Stir and mix for 20min-30min to obtain mixture A;

[0040] Add the filler and the composite matting agent to the mixture A, stir and mix at a rotational speed of 1000r / min-1500r / min for 10min-15min to obtain the mixture B;

[0041] Add a leveling agent to the mixture B, and continue to stir and mix at a rotational speed of 300r / min-450r / min fo...

Embodiment 1-5

[0045] The mass percent of the preparation raw materials of Examples 1-5 is shown in Table 1;

[0046] The preparation method of a kind of printing iron soft-feeling paint of embodiment 1-5, comprises the following steps:

[0047] 10g of porous silica, 8g of Tween-80, 5g of polyurethane and 3g of polytetrafluoroethylene are added to the ball mill, and mixed by ball milling at a speed of 1000r / min-1500r / min for 5min-10min to obtain a composite matting agent, which is for later use;

[0048] Mix 20g of acrylic resin, 15g of polycarbonate polyurethane resin, 5g of organosilicon modified polyurethane resin and 10g of polycarbonate to obtain a water-based mixed resin for use;

[0049] Mix 3g of titanate with 4g of ethylenediaminepropyl triethoxysilane, as a coupling agent, for subsequent use;

[0050] Mix 50 mL of water with 50 mL of propanol as a solvent for later use;

[0051] The water-based mixed resin was added to the mixing kettle, heated to 75°C, and then the coupling agent,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Login to View More

Abstract

The invention provides a soft coating for metal printing and a preparation method thereof, and the soft coating for metal printing comprises the following preparation raw materials in percentage by mass: water-based mixed resin, a coupling agent, a composite delustering agent, a dispersing agent, a curing agent, a flatting agent, a film-forming agent, a defoaming agent, a filling agent and a solvent, the composite delustering agent is prepared by compounding porous silicon dioxide, an emulsifier, polyurethane and polytetrafluoroethylene, and the mass ratio of the porous silicon dioxide to the emulsifier to the polyurethane to the polytetrafluoroethylene is (10-15): (1-8): (2-7): (1-5). By optimizing the formula of the soft paint for metal printing, the formula system is more stable, the storage and use stability of the paint are facilitated, and the dispersity of the components of the formula system can be promoted by compounding the porous silicon dioxide, the emulsifier, the polyurethane and the polytetrafluoroethylene as a composite delustering agent, so that a coating film is more uniform and has a soft hand feeling; the wear resistance, the scratch resistance and the weather resistance are excellent.

Description

technical field [0001] The invention relates to the field of coating preparation, in particular to a soft-touch coating for iron printing and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, in the automotive industry, low-end automotive interior parts cannot be wrapped in leather due to cost issues, and a large number of imitation leather decorations will also bring environmental protection problems; the use of a large number of rigid plastics is cheap, but The feel is relatively poor, giving people a strong sense of low-end decoration. Therefore, some car manufacturers will spray elastic paint on the dashboard and other positions to make it feel like a leather. The soft-touch coating for printed iron has a rubber-like texture and a velvet-like touch, and is soft to the touch. It is more and more widely used in switch panels, high-end beauty appliances, computer cases and other products made of aluminum or stain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D175/04C09D169/00C09D7/42
CPCC09D133/00C09D7/42C08L75/04C08L69/00C08L27/18C08K7/26
Inventor 张明远胡海宏谭贺洵
Owner 广东鑫皇冠新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com