Low-water-absorption PA56T/PET composite material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of composite materials and raw materials, applied in the field of bio-based PA56T/PET composite materials, can solve the problems of low regularity of PET macromolecular chains, high rigidity of PET, slow crystallization speed, etc., and achieve good mechanical properties and dimensional stability, Good anti-oxidation performance and low water absorption
Pending Publication Date: 2022-05-13
EAST CHINA UNIV OF SCI & TECH
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, PET has high rigidity, poor toughness, and shows a certain brittleness, and low impact performance.
In addition, due to the low regularity of PET mac
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0022] Example 1: A PA56T / PET composite material, comprising the following components by weight: 65 parts of PA56T, 15 parts of PET, 15 parts of glass fiber, 4 parts of compatibilizer, 0.2 part of antioxidant, lubricant 0.8 doses;
[0023] The compatibilizer is POE-g-MAH, the antioxidant is antioxidant 1010, and the lubricant is EBS wax.
Example Embodiment
[0024] Example 2: A PA56T / PET composite material, prepared from the following components in parts by weight: 60 parts of PA56T, 15 parts of PET, 20 parts of glass fiber, 4 parts of compatibilizer, 0.4 parts of antioxidant, lubricant 0.6 servings;
[0025] The compatibilizer is POE-g-GMA, the antioxidant is Antioxidant 300, and the lubricant is silicone powder.
Example Embodiment
[0026] Example 3: A PA56T / PET composite material, comprising the following components by weight: 60 parts of PA56T, 20 parts of PET, 13 parts of glass fiber, 6 parts of compatibilizer, 0.5 part of antioxidant, lubricant 0.5 doses;
[0027] The compatibilizer is the compound of POE-g-MAH and POE-g-GMA, the antioxidant is the compound of the antioxidant 1010 and the antioxidant 300, and the lubricant is the compound of the EBS wax and the silicone powder.
[0028] The obtained pellets were dried in a vacuum drying oven at 50°C for 6 hours, and then injection-molded to prepare test strips and products.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a PA56T/PET composite material, and relates to the technical field of engineering. The composite material is prepared from the following raw material components in parts by weight: 15-85 parts of PA56T; 15 to 85 parts of PET (Polyethylene Terephthalate); 2 to 20 parts of a compatilizer; 0.2 to 0.8 part of an antioxidant; 20 to 40 parts of glass fiber; and 0.2 to 1 part of a lubricant. According to the composite material and the preparation method thereof, the raw materials are low in price and environment-friendly, compared with the prior art, the PA56T/PBT alloy prepared from the bio-based PA56T combines the advantages of the PA56T and PET, the tensile strength and modulus are obviously improved, the impact strength is not lower than that of pure PA56T, the water absorption rate of the PA56T is greatly reduced, the dimensional stability of the PA56T is improved, and the composite material is suitable for industrial production. By means of the breakthrough, the alloy can be widely applied to materials of air conditioner parts, power distribution parts, automobile parts and the like, the production process is simple, and the excellent market prospect is achieved.
Description
technical field [0001] The invention is a bio-based PA56T / PET composite material, which belongs to the technical field of polymer materials. Background technique [0002] Bio-based nylon 56 (PA56) is a new type of bio-based polyamide polymerized from bio-based pentamethylenediamine and petroleum-based adipic acid. It is a new type of biomass material independently developed by Shanghai Kaisai Biotechnology Co., Ltd. Bio-based pentamethylenediamine is obtained through microbial fermentation of starch, which reduces production costs and alleviates the pressure of shortage of petroleum resources. It is a very competitive nylon material. [0003] PA56T has a melting point close to PA66, but its water absorption rate and water absorption rate are higher than PA6 and PA66. From a structural point of view, PA56T has only one carbon atom less than PA66, and the density, melting point and mechanical properties of the two are relatively close under dry conditions, so its application ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.