PVC (polyvinyl chloride) composite film and preparation method thereof

A composite film and manufacturing method technology, applied in chemical instruments and methods, flat products, other household appliances, etc., can solve the problems of hard PVC bottom material, not cold-proof, and brittle, so as to prevent slipping and improve anti-slip Cold, the effect of increasing the service life

Pending Publication Date: 2022-05-31
江苏展新旅游用品有限公司
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the tent bottom material made of traditional PVC is not cold-proof. In winter, due to insufficient warmth, the PVC bottom material becomes hard, brittle, and even breaks from the middle.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC (polyvinyl chloride) composite film and preparation method thereof
  • PVC (polyvinyl chloride) composite film and preparation method thereof
  • PVC (polyvinyl chloride) composite film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Low temperature resistant layer raw material (parts by weight)

[0041] PVC resin (polymerization degree 1000~1100): 100 parts;

[0042] Dioctyl phthalate: 45 parts

[0043] Dioctyl adipate: 20 parts

[0044] Triphenyl phosphate: 15 parts

[0045] Tribenzyl phosphite: 1 part

[0046] Raw materials for heat storage layer (parts by weight)

[0047] PVC (polymerization degree 1000~1100): 100

[0048] Dioctyl phthalate: 40 parts

[0049] Calcium stearate: 3 parts

[0050] n-decyl alcohol: 2 parts

[0051] Antibacterial layer raw material (parts by weight)

[0052] PVC (polymerization degree 1000~1100): 100

[0053] Dioctyl phthalate: 30 parts

[0054] Calcium stearate: 2 parts

[0055] Antibacterial agent: 0.2 parts

[0056] Raw material of anti-fog layer (parts by weight)

[0057]PVC (polymerization degree 1000~1100): 100 parts

[0058] Dioctyl phthalate: 40 parts

[0059] Triphenyl phosphate: 10 parts

[0060] Silicon-containing surfactant: 0.5 parts

[0...

Embodiment 2

[0074] The difference from Example 1 is only that the formulations of the low-temperature resistant layer, thermal storage layer, antibacterial layer, and anti-fog layer are different, and the formulations are as follows:

[0075] Low temperature resistant layer raw material (parts by weight)

[0076] PVC resin (polymerization degree 1000~1100): 100 parts;

[0077] Diisooctyl phthalate: 50 parts

[0078] Diisooctyl adipate: 25 parts

[0079] Cresyl diphenyl phosphate: 10 parts

[0080] Triphenyl phosphite: 0.5 parts

[0081] Raw materials for heat storage layer (parts by weight)

[0082] PVC (polymerization degree 1000~1100): 100

[0083] Diisooctyl phthalate: 35 parts

[0084] Barium stearate: 1 part

[0085] Isodecyl alcohol: 5 parts

[0086] Antibacterial layer raw material (parts by weight)

[0087] PVC (polymerization degree 1000~1100): 100

[0088] Diisooctyl phthalate: 40 parts

[0089] Barium stearate: 1 part

[0090] Antibacterial agent: 0.5 parts

[0091...

Embodiment 3

[0099] The difference from Example 1 is only that the formulations of the low-temperature resistant layer, thermal storage layer, antibacterial layer, and anti-fog layer are different, and the formulations are as follows:

[0100] Low temperature resistant layer raw material (parts by weight)

[0101] PVC resin (polymerization degree 1000~1100): 100 parts;

[0102] Didecyl phthalate: 40 parts

[0103] Diisodecyl adipate: 15 parts

[0104] Triphenyl phosphate: 10 parts

[0105] Tribenzyl phosphite: 0.5 parts

[0106] Raw materials for heat storage layer (parts by weight)

[0107] PVC (polymerization degree 1000~1100): 100

[0108] Didecyl phthalate: 30 parts

[0109] Magnesium stearate: 2 parts

[0110] Undecanol: 4 parts

[0111] Antibacterial layer raw material (parts by weight)

[0112] PVC (polymerization degree 1000~1100): 100

[0113] Didecyl phthalate: 35 parts

[0114] Magnesium stearate: 1 part

[0115] Antibacterial agent: 0.1 parts

[0116] Raw material ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a PVC composite film and a preparation method thereof, the PVC composite film is composed of four layers from outside to inside: a low temperature resistant layer, a heat storage layer, an antibacterial layer and an antifogging layer, the heat storage film uses fatty alcohol as a heat storage agent, can well absorb the temperature in a tent and timely feed back the temperature to the low temperature resistant layer, better resists the penetration of cold air, and is not easy to break and damage. Segmented extrusion molding is adopted, the low-temperature-resistant layer, the heat storage layer, the antibacterial layer and the anti-fog layer are subjected to first-stage extrusion firstly and then subjected to second-stage extrusion molding, tiny gaps are formed between the heat storage layer and the antibacterial layer by controlling the confluence temperature, and the service life of the composite film is prolonged.

Description

technical field [0001] The invention belongs to the field of polymer composite materials, in particular to a PVC composite film with functions such as cold resistance, heat preservation and antibacterial and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, outdoor activities have become a new way of leisure. At the same time, due to the uncertainty of the outdoor environment, especially in winter or high altitude areas, outdoor appliances are required to have better performance. Tents are indispensable outdoor appliances, and are often set up outdoors. How to improve the cold resistance and thermal insulation capabilities of tents has attracted more and more attention from outdoor enthusiasts. The fabric of the tent is mainly divided into three parts: the outer tent fabric, the inner tent fabric, and the bottom tent fabric. The fabric of the outer tent is mainly made of nylon, canvas and other materials; the fabr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/08B32B27/30B32B27/20C08J5/18C08L27/06C08K5/12C08K5/11C08K5/523C08K5/526C08K5/098C08K5/05B29D7/01B29C48/08B29C48/18B29C48/154B29C48/92B29L7/00
CPCB32B27/08B32B27/304B32B27/20B29D7/01B29C48/08B29C48/18B29C48/154B29C48/92C08J5/18B29C2948/92704C08J2327/06C08K5/12C08K5/11C08K5/523C08K5/526C08K5/098C08K5/05B32B2250/04Y02A40/25
Inventor 张功明张功平周良张志涛张志勇
Owner 江苏展新旅游用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap