Method for smelting scrap steel through blast furnace oxygen-enriched large-proportion bituminous coal injection
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A large-scale, blast furnace technology, applied in the metallurgical field, can solve the problems of poor system stability, high volatile content of bituminous coal, and reduce costs, and achieve the effects of reducing coke ratio, increasing coal injection volume, and increasing output.
Active Publication Date: 2022-07-01
武汉钢铁有限公司
View PDF6 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0013] However, due to the high volatile content of bituminous coal, there are potential safety hazards such as spontaneous combustion, fire, and explosion. When the content of
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0045] A blast furnace (3222m 3 ),
[0046] Table 1 A blast furnace charge composition parameters
[0047]
[0048] Table 2 A blast furnace using South African block chemical composition
[0053] (1) All charging materials for blast furnace A are: large-size sintered ore, small-size sintered ore, Ezhou pellets, South African lumps, coke and scrap steel with crushed material type; the conventional ore batch is 92t for blast furnace, and specific scrap steel is charged The amount is 2.7t;
[0054] (2) A blast furnace injection coal is a mixture of bituminous coal and anthracite, the anthracite is Yongcheng anthracite and Jincheng anthracite, the bituminous coal is Shenhua bituminous coal, and the mass percentage of Shenhua bituminous coal is 42%;
[0055] (3) The standard air volume of blast furnace A is 6222m 3 / min, the oxygen enrichment rate is 8%, and t...
Embodiment 2
[0059] B blast furnace of a domestic ironworks (3222m 3 ),
[0060] Table 4 B blast furnace charge composition parameters
[0061]
[0062] Table 5 The chemical composition of Aussie block used in B blast furnace
[0066] (1) All the charging materials for B blast furnace are: large particle size sinter, small particle size sinter, Ezhou pellet, Australian block, coke and scrap steel with crushed material type; the blast furnace adopts the conventional ore batch of 86t, and the specific scrap is loaded into The amount is 4.3t;
[0067] (2) B blast furnace injection coal is a mixture of bituminous coal and anthracite, the an...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a method for smelting waste steel by blast furnace oxygen-enriched large-proportion bituminous coal injection, which comprises the following steps: charging: all charging materials of a blast furnace comprise sintered ore, pellet ore, lump ore, coke and waste steel, adding the waste steel at the edge ring belt of the blast furnace according to the mass ratio of the waste steel consumption to the ore batch weight in each batch of charging materials of (3-5): 22, and charging into the furnace for smelting; material distribution: the ore-coke ratio at the edge of a furnace wall is 4: 3 or 3: 2, and the mass percent of the central coke adding amount is 29.4-33.3% of that of a coke batch; blowing: blowing coal is mixed coal of anthracite and bituminous coal, and the mass percentage of the bituminous coal is 42-45%; air blowing: the adopted air blowing oxygen enrichment rate is 8-12%, and the standard air speed (standard air volume/air inlet area) is 252-272 m/s; by improving the blast oxygen enrichment rate of the blast furnace, using high-volatile bituminous coal for injection in a large proportion, adding waste steel into the furnace, adjusting the material distribution system, strengthening the central gas flow of the blast furnace and inhibiting the edge gas flow, the stable furnace condition, low consumption and high yield of the blast furnace are realized.
Description
technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a method for smelting scrap steel. Background technique [0002] Due to the country's increasingly strict environmental protection requirements, coupled with the constraints of factors such as the regulation of the metallurgical industry, at present, iron and steel enterprises will not be able to add new process equipment, but at the same time, with the rapid development of my country's economy, for different purposes The demand for iron and steel products is also increasing day by day. In order to meet the rapid growth of iron and steel products in different industries, iron and steel enterprises need to use existing equipment conditions to fully tap their own capabilities to meet the growing market demand. As for the ironmaking process, the increase in production capacity means that the production capacity must increase under the condition that a new blast furnace...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more