Clump weight for head of golf club

A technology for golf club heads and counterweights, applied in the field of counterweights, which can solve problems such as difficult control of process conditions and different finished products

Inactive Publication Date: 2006-10-18
FUSHENG IND CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Furthermore, if image 3 As shown, since tungsten is often precipitated on the surface of tungsten-iron-nickel alloy [the dark part is the wavelaid iron structure, and the white part surrounded by the wavelaid iron is the precipitated tungsten], therefore, the "tungsten + The γ[iron, nickel] phase also causes the weight block made of tungsten-iron-nickel alloy to produce patterns after grinding and polishing, so that the weight block made of tungsten-iron-nickel alloy is directly bonded to the bottom surface of the club head body At the same time, the fitting line between the tungsten-iron-nickel alloy and the club head body is clearly visible, and with the difference in grinding thickness and angle, each finished product is different, so it is difficult to control the process conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Clump weight for head of golf club
  • Clump weight for head of golf club
  • Clump weight for head of golf club

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] refer to Figure 4-Figure 6 As shown, most of the manufacturing methods of the counterweight of the golf club head of the present invention are the same as the manufacturing method of the counterweight of the traditional golf club head of Taiwan Patent No. 91116681, so the same parts of the two manufacturing processes and conditions are no longer I will repeat it in detail.

[0030] The counterweight of the golf club head of the present invention is preferably manufactured by precision casting. When performing precision casting, firstly, according to the specific metal melting sequence and composition ratio, the required ingredients are added into the high-temperature furnace at a temperature between 1450-1750°C, preferably between 1600-1680°C, and chromium is added at the same time And properly control the mixing ratio of nickel and tungsten to produce molten tungsten-iron-nickel alloy;

[0031] Then, the molten tungsten-iron-nickel alloy is cast into a preheated mol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

A clump weight for head of golf club made from precision cast tungsten iron-nickel alloy, which comprises 15-40% of iron, nickel 30-60%, tungsten15-30%, chromium 1.5-10.0% and molybdenum 0.5-5.0%.

Description

technical field [0001] The invention relates to a counterweight of a golf club head, in particular to a counterweight of a tungsten-iron-nickel alloy that improves cracks caused by welding heat by controlling the mixing ratio of nickel and tungsten and adding molybdenum at the same time. Background technique [0002] The weight of the traditional golf club head is usually made of tungsten [19.30g / cm 3 ], iron [7.8g / cm 3 ] and nickel [8.9g / cm 3 ] The metal powder with high specific gravity and high hardness is press-formed and sintered to form a tungsten-iron-nickel weight suitable for golf club heads. Although the powder metallurgy process is widely used in the industry, there are still many disadvantages in this process, such as: high cost of molding, low elongation of the finished product, long process time, easy thermal expansion and contraction, and inability to form precise patterns, characters, and models and trademarks etc. [0003] Another traditional golf club h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/05C22C30/00A63B53/04A63B60/02A63B102/32
Inventor 陈建同苏晏正
Owner FUSHENG IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com