Fireproof coating for exhaust equipment

A technology for refractory coatings and exhaust equipment, applied in fire-resistant coatings, anti-corrosion coatings, coatings, etc., can solve the problems of reducing the comprehensive performance of materials, low compatibility, etc., to improve rust and corrosion resistance, excellent storage performance, Promising effects

Inactive Publication Date: 2016-09-21
CHUZHOU VOCATIONAL & TECHN COLLEGE
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention uses aluminum powder and fly ash to mix and prepare high-alumina fly ash microspheres, which can greatly improve the corrosion resistance, impact resistance, and erosion and wear resistance of the coating, but directly add compatible The performance is not high, which will greatly reduce the overall performance of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A refractory coating for exhaust equipment, prepared from the following raw materials in parts by weight (kg): fly ash 21, fluorocarbon resin 78, polyacrylamide 0.6, n-butyl acetate 13, methacrylate 8, polyurethane resin 28. Acrylic leveling agent 0.3, aluminum powder 9, floating beads 2, expanded mica 3, styrene 12, azobisisobutyronitrile 1.2, silicon powder 3, zinc methacrylate 1.2, aluminum dihydrogen tripolyphosphate 0.6, Zirconate coupling agent 0.2, sulfur 2.2, diethanolamine 2.5, sawdust powder 2.8, an appropriate amount of ethanol.

[0014] Described a kind of refractory paint for exhaust equipment is prepared by the following specific steps:

[0015] (1) Soak the fly ash in deionized water for 24 hours, filter and dry, then mix the fly ash and sawdust powder well and calcinate at 550°C for 2 hours, after cooling, crush and sieve into 200 mesh, and then mix with zinc methacrylate , aluminum dihydrogen tripolyphosphate, and zirconate coupling agent are ground an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fireproof coating for exhaust equipment. The coating is made from the following raw materials: coal ash, a fluorocarbon resin, polyacrylamide, n-butyl acetate, methacrylate, a polyurethane resin, an acrylic acid leveling agent, aluminium powder, floaters, expanded mica, styrene, azodiisobutyronitrile, silica powder, zinc methacrylate, aluminum dihydrogen tripolyphosphate, a zirconate coupling agent, sulphur, diethanol amine, sawdust powder and a proper amount of absolute ethanol. The coating has preferable fire retardance and weather resistance, is high in strength and excellent in storage performance, and is convenient to apply. The coating can be operated at a high-temperature environment for a long time and is not easy to spoil. The coating has excellent overall performance and obvious cost advantage, and has bright application prospects.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a refractory coating for exhaust equipment. Background technique [0002] The shell surface of the exhaust equipment will be painted with different paints to ensure that the shell is not damaged and prolong the service life of the equipment. Aluminum pigments are widely used in traditional solvent-based coatings and inks due to their special metallic luster and "color flop" effect. It has excellent metal effect and large demand. Flake aluminum powder has a good ability to reflect light and heat radiation, and forms a continuous metal film in the coating, which can reflect visible light, ultraviolet rays and infrared rays. The reflection of the full spectrum of visible light is silvery white, which makes it have good decorative performance, and the reflection of infrared rays makes it have the thermal insulation performance of reflecting heat radiation, while the reflection of u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/18C09D5/10C09D7/12
CPCC09D4/06C09D5/103C09D5/18C09D7/61C09D7/62C09D7/65
Inventor 赵玉霞苏和堂
Owner CHUZHOU VOCATIONAL & TECHN COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com