Nonmagnetic hard alloy and preparing method thereof

A cemented carbide and a manufacturing method technology, applied in the field of material science, can solve the problems of corrosion resistance, poor wear resistance, uneven distribution of WC grain size, and reduced overall performance, and achieve good wear resistance and guarantee. Surface finish, quality improvement effect

Inactive Publication Date: 2006-12-27
HENGDIAN GRP DMEGC MAGNETICS CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When these two materials are used to produce magnetic tile molds, the sticky material is serious, it is not easy to demould, the pressing yield is low, and the production efficiency is also low; in addition, because the magnetic hard alloy material is easy to oxidize, corrosion resistance and wear resistance Poor, not only reduces the overall performance, but also greatly limits the scope of use
However, the existing magnetic cemented carbide is usually processed by wire cutting, and the WC grain size distribution is uneven, resulting in poor consistency of internal stress.
Therefore, the magnetic tile mold produced by this material is prone to cracking and deformation problems during use due to the inconsistency of internal stress.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0034] 1. Ingredients:

[0035] Carry out batching according to following ratio (by weight):

[0036] Tungsten carbide (WC): 84.4%;

[0037] Nickel (Ni): 14%;

[0038] Chromium (Cr): 0.5%;

[0039] Molybdenum (Mo): 1.1%;

[0040] Among them: the technical requirements of tungsten carbide (WC): WC≥99.5%, total carbon: 5.85%-5.97%; Fe≤0.03%; Fibonacci particle size: 18μm-23μm;

[0041] Technical requirements for nickel (Ni) powder: Ni≥99.5%, O≤0.5%, Fe≤0.03%;

[0042] Technical requirements for chromium (Cr) powder: Cr≥99.0%, Fe≤0.02%;

[0043] Technical requirements for molybdenum (Mo) powder: Mo≥99.0%, O≤0.5%, Fe≤0.03%;

[0044] Second, the production method and process:

[0045] 1. Ball milling:

[0046] Put the mixed material according to the above formula into the ball mill, and add industrial alcohol and non-magnetic alloy steel balls into the ball mill for grinding; the content of industrial alcohol is ≥95%, and the specific gravity is ≤0.82g / cm 3 ; The hardness ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
crystal sizeaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a non-magnetic hard alloy and its preparation method. Said non-magnetic hard-alloy used wolfram carbide (WC) as main component, and is formed by adding Ni, Cr and Mo and its prparation method includes: bending material, wet grinding, filtering mixed slurry, drying and seiving, forming, vacuum sintering and checking. As compared with existent technology said invented product has the advantages of high hardness, good abrasive resistance, small friction coefficience, good polishing property, high compression strength and good rigidity, etc.

Description

1. Technical field [0001] The invention relates to a cemented carbide material and a manufacturing method thereof, belonging to the technical field of material science. 2. Background technology [0002] At present, the materials used for magnetic tile molds in the magnetic material production industry are generally non-magnetic steel and magnetic hard alloy materials. When these two materials are used to produce magnetic tile molds, the sticky material is serious, it is not easy to demould, the pressing yield is low, and the production efficiency is also low; in addition, because the magnetic hard alloy material is easy to oxidize, corrosion resistance and wear resistance Poor, not only reduces the overall performance, but also greatly limited the scope of use. However, the existing magnetic hard alloys are usually processed by wire cutting, and the WC grain size distribution is uneven, resulting in poor consistency of internal stress. Therefore, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C29/08
Inventor 何时金吴志荣金玲红
Owner HENGDIAN GRP DMEGC MAGNETICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com