Preparation of rosen modified mixed alkyl phenolic resin

A technology of alkylphenol-formaldehyde resin and resin, which is applied in the field of preparation of rosin-modified mixed alkylphenol-formaldehyde resin, can solve the problems of unsatisfactory, poor printing performance, low gloss, etc., achieve moderate drying time, excellent printing performance, anti-corrosion Good emulsifying effect

Inactive Publication Date: 2002-03-27
山西省应用化学研究所
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The rosin-modified alkylphenol-formaldehyde resin is prepared by using alkylphenol with a relatively small alkyl group. This resin has poor oil solubility and aliphatic hydrocarbon solubility. The ink made from it has high gloss, but it is easy to skin. Yellowing, too short fixation time, poor printing performance
The rosin-modified alkylphenol-formaldehyde resin is made of alkylphenol with relatively large alkyl group. The resin has good oil solubility and aliphatic hydrocarbon solubility. The ink and printing performance made of it are good but the gloss is low and the fixing time is too long. long
In short, rosin-modified phenolic resin synthesized from a single alkylphenol is used in the ink binder, which affects the printing effect and speed of the ink, and cannot meet the requirements of the growing printing industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Add 34g of p-tert-butylphenol, 100g of p-tert-octylphenol, 60g of 15% caustic soda into a 500ml three-necked flask, heat and melt, start stirring after melting, cool to 60°C and slowly add 141g of 37% formaldehyde dropwise After the addition, keep the reaction at 65°C for 4 hours, cool down to 50°C, neutralize with 10% hydrochloric acid, neutralize until PH=6, stop stirring and let stand for 20 minutes, separate layers, and wash the organic layer twice , and discard the water layer to obtain 216g of a mixed alkylphenol-formaldehyde resin solution.

[0023] Add 400g of rosin into a 1000ml three-necked flask, heat and melt, start stirring after melting, and slowly add 216g of a stage A mixed alkylphenolic resin solution under the condition of 180-182°C. Add 0.2g of zinc oxide, stir evenly, slowly add 60g of glycerin at 220°C, keep warm at this temperature for two hours, raise the temperature to 265°C and keep warm until the acid value of the reaction solution is less than...

Embodiment 2

[0025] Add 68g of p-tert-butylphenol, 65g of p-nonylphenol, and 53g of 15% caustic soda into a 500ml three-necked flask, heat and melt, start stirring after melting, cool to 50°C and slowly add 140g of 37% formaldehyde dropwise, After the addition, keep the reaction at 60°C for 3 hours, cool down to 50°C, neutralize with 10% hydrochloric acid until PH = 5, stop stirring and let stand for 20 minutes, separate layers, and wash the organic layer twice with water. The water layer was discarded to obtain 223g of a mixed alkylphenol-formaldehyde resin solution.

[0026] Add 400g of rosin to a 1000ml three-necked flask, heat and melt, start stirring after melting, and slowly add 223g of a stage A mixed alkylphenolic resin solution under the condition of 190°C, and keep it at 230°C for one hour after adding 0.2g of magnesium oxide, stirred evenly, slowly added 54g of quaternary tetraol at 240°C, kept the reaction for two hours at this temperature, raised the temperature to 270°C and k...

Embodiment 3

[0028] Add 15g of p-methylphenol, 56g of p-tert-butylphenol, 44g of p-tert-octylphenol, 60g of 15% caustic soda into a 500ml three-necked flask, heat and melt, start stirring after melting, cool to 55°C and slowly Add 128g of 37% formaldehyde dropwise, keep it warm at 70°C for 5 hours, cool down to 50°C, neutralize with 10% hydrochloric acid until PH = 6, stop stirring and let stand for 20 minutes, divide layer and the organic layer were washed twice with water, and the aqueous layer was discarded to obtain 191g of a mixed alkylphenol-formaldehyde resin solution.

[0029] Add 400g of rosin to a 1000ml three-necked flask, heat and melt, start stirring after melting, and slowly add 191g of a stage A mixed alkylphenolic resin solution at 200°C. 0.3g of magnesium oxide, stir well, slowly add 57g of glycerin at 210°C, keep warm at this temperature for two hours, heat up to 268°C, keep warm and react until the acid value of the reaction solution is less than 20mgKOH / g, then reduce t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
acid valueaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The present invention belongs to the field of resin preparation technology that is a kind of connecting material to printing ink. It is obtained with processed by the following steps: arbitrarily mixing p-methyl hydroxybenzene, p-tert-butylphenol, p-tex-octylphenol and p-nonylphenol, making them produce reaction with formaldehyde to synthesize A-stage mixed alkyl phenolic resin, then using rosin to make modification and using polyhydric alcohol to make esterification. Said invention is easy to operate, safe, and its resin oil-solubility and fatty hydrocarbon solubility are good. Its colour islight and softening point is high. The printing ink made up by using said invented product does not skin, and possesses good printing property.

Description

1. Technical field [0001] The invention introduces a manufacturing technology of resin used for preparing ink binder, and more specifically relates to a manufacturing technology of rosin-modified mixed alkylphenol-formaldehyde resin. 2. Background technology [0002] Rosin modified phenol novolac resin, rosin modified bisphenol A phenol novolac resin, rosin modified tert-butylphenol novolac resin, etc. have been prepared for many years. Performance, drying, fixing performance and other printing properties all have different defects. The rosin-modified alkylphenol-formaldehyde resin is prepared by using alkylphenol with a relatively small alkyl group. This resin has poor oil solubility and aliphatic hydrocarbon solubility. The ink made from it has high gloss, but it is easy to skin. Yellowing, too short fixation time, poor printing performance. The rosin-modified alkylphenol-formaldehyde resin is made of alkylphenol with relatively large alkyl groups. The resin has good oil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G8/34
Inventor 马国章白国宝候彩英原丽平任晓东
Owner 山西省应用化学研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More