Imitation metal fluorocarbon paint

A fluorocarbon paint, imitating metal technology, applied in coating and other directions, can solve the problems of complex process, high cost, affecting the application of fluorocarbon baking paint, etc., and achieve the effects of good recoatability, simple construction and easy maintenance.

Inactive Publication Date: 2002-03-27
大连振邦氟涂料股份有限公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The construction method of fluorocarbon baking varnish is to process the aluminum plate according to the engineering drawings, then spray fluorocarbon baking varnish, plasticize and switch at a high temperature of 200-235°C to form a film, stick a protective film, transport it to the construction site, and install it on the construction site. On the metal frame, this method is complicated and costly, which affects the application of fluorocarbon baking varnish

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The performance measurement is shown in Table 2:

[0025] serial number

name

1

2

3

1

Adhesion level

1

1

1

2

Hardness (Pencil)

3H

3H

3H

3

Impact 50cm

pass

pass

pass

4

Flexibility≤1mm

1

1

1

[0026] The preparation method of above-mentioned imitation metal fluorocarbon paint:

[0027] 1. Pre-dispersion of metallic pigment paste. Such as taking the material according to the proportioning of the components in Example (1).

[0028] For example, take 3.5kg of aluminum powder slurry (non-leafing type), use the same amount of solvent, take 1.5kg of xylene, 2kg of butyl acetate and 0.1kg of wetting and dispersing agent Byk161 for pre-infiltration, and add the amount of fluorocarbon resin that needs to be added. 10-20% that is 4kg-8kg Stir evenly:

[0029] 2. The remaining fluoroca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The imitation metal fluorocarbon paint includes component A containing fluorocarbon resin (53%), metal pigment paste, wetting dispersing agent, cellulose acetate-butyrate, colour paste, antisettling sagging agent and solvent and component B containing hexamethylene diisocyanate tripolymer. Their mixing ratio is A:B=10-14:1, according to the above-mentioned mixing ratio, the imitation metal fluorocarbon paint can be made up. It possesses the following advantages: 1. it can be solidified and film-formed at normal temp.; 2. it can be directly spray-coated on the surface of external wall of cement building; 3. its construction is simple, its cost is 1/5 of that of baked aluminium curtain wall; and 4. said paint not only can be used for decorative protection of wall body but also can be used in the fields of steel and iron structure, wooden product and plastics.

Description

(1) Technical field: [0001] The invention is a metal imitation fluorocarbon paint. (two) background technology: [0002] On the exterior walls of high-rise buildings, metal aluminum curtain wall hanging panels are often used for decoration and protection to ensure an anti-aging service life of more than 20 years. In terms of weather resistance, such as ultraviolet radiation, wind erosion, chalking, cracking, and atmospheric corrosion resistance are very demanding. The only paint that can achieve this high weather resistance is fluorocarbon baking paint. The construction method of fluorocarbon baking varnish is to process the aluminum plate according to the engineering drawings, then spray fluorocarbon baking varnish, plasticize and switch at a high temperature of 200-235°C to form a film, stick a protective film, transport it to the construction site, and install it on the construction site. On the metal frame, this method is complicated and costly, which affects the appli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12
Inventor 王万令乔敦殷宪霞尚德宇王军
Owner 大连振邦氟涂料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka