Electric insulation polyurethane resin composition and electric or electronic parts
A technology of polyurethane resin and electrical insulation, which is applied in the field of electrical or electronic components and electrical insulating polyurethane resin composition, which can solve the problems of polyurethane resin water resistance and low heat and humidity resistance, and achieve excellent electrical insulation and transparency Good results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0048] Example 1
[0049] 30 g of diphenylmethane diisocyanate (NCO=33.6 mol%), 0.05 g of calcium hydroxide and tris(cresyl phosphate) were mixed with 100 g of polyester polyol (hydroxyl value of about 160 mg KOH / g) of glyceryl ricinoleate ) 20 g were mixed, degassed, and the resulting mixture was placed in a 60°C thermostat for 1 hour to solidify.
[0050] The volume intrinsic resistance value, moist heat resistance and flame retardancy of the obtained cured product were measured. The results are shown in Table 1. Comparative Example 1
Example
[0053] Examples 2 to 9
[0054] A cured product was obtained in the same manner as in Example 1 except that the amounts of calcium hydroxide and tris(cresyl phosphate) were changed as shown in Table 1.
[0055]
[0056] As clearly shown in Table 1, the cured products obtained in Examples 1 to 9 did not impair their electrical insulating properties and flame retardancy, and had improved heat and humidity resistance. Examples 10 to 12
Example
12
[0057] Example number
[0058] Example number
[0059] As described above, the present invention provides an electrically insulating urethane resin composition which is excellent in flame retardancy and hydrolysis resistance and is less likely to cause environmental problems. In addition, since the electrical and electronic parts of the present invention are encapsulated with the electrically insulating polyurethane resin composition having the above advantages, they are excellent in moisture resistance, especially moisture and heat resistance, and are suitable for use as washing machines, toilet seats, water heaters, and water purifiers and other electrical and electronic components.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap