Vanadium dioxide nanometer rod and preparation method thereof

A technology of vanadium dioxide and nanorods, applied in the field of nanomaterials and nanometers, to achieve the effects of good reproducibility, simple preparation process, and high degree of controllability

Inactive Publication Date: 2004-08-25
武汉理工力强能源有限公司
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, as one of the basic building blocks of nano-devices, one-dimensional nanomaterials have also aroused widespread interest among scientific and technol...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vanadium dioxide nanometer rod and preparation method thereof
  • Vanadium dioxide nanometer rod and preparation method thereof
  • Vanadium dioxide nanometer rod and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: (1) V 2 o 5 and hexadecyltrimethylammonium bromide in a molar ratio of 2:1; (2) magnetically stir the ingredients in an anhydrous ethanol medium for 1 hour; (3) add an appropriate amount of deionized water, stir and age for 48 After more than 1 hour, a light yellow rheological product is formed; (4) the above-mentioned rheological product is moved into a stainless steel reaction kettle with a polytetrafluoroethylene substrate, and subjected to a hydrothermal reaction at 180°C for 6 to 8 days; (5) the hydrothermal reaction product is Washing and filtering with water for 3 times, and drying at 80° C. for 12 hours can obtain a black vanadium dioxide nanorod product.

[0014] Analytical tests show (see attached figure) that the synthesized product is in the form of a short rod, 1-2 μm long, and a single VO 2 The diameter of the nanorods is 20-50nm, they are aggregated together, and the diameter ranges from 80-200nm.

[0015] raw material

[0016...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides a method for preparing B phase vanadium dioxide nano rod by means of rheological phase reaction and self-assembly process combination, and is characterized by that said method includes the following steps: mixing inorganic vanadium oxide powder and cationic surfactant according to the mole ratio of 2:1, magnetic stirring for 1 hr. in absolute ethyl alcohol medium, adding proper quantity of deionized water, stirring and ageing for 48 hr to form rheological product, moving it into the stainless reactor still with teflon lining bottom, making hydrothermal reaction for 6-8 days at 180 deg.C, water-washing and filtering for 3 times, drying for 12 hr at 80 deg.C so as to obtain B phasek vanadium dioxide nano rod product with high surface activity.

Description

technical field [0001] The invention relates to a new method for synthesizing vanadium dioxide nanorods by combining rheological phase reaction and self-assembly technology, which belongs to the field of nanomaterials and nanotechnology. Background technique [0002] In recent years, one-dimensional nanomaterials have shown promising application prospects in optics, electrochemistry, electromagnetism, nanoelectronics, biomedicine and other fields, and have become the frontier research field of nanotechnology. At the same time, as one of the basic building blocks of nanodevices, one-dimensional nanomaterials have also attracted widespread interest from scientific and technological workers, but there has been no report on the synthesis of vanadium dioxide nanorods through the combination of rheological phase reaction and self-assembly technology. Contents of the invention [0003] The problem to be solved by the present invention is to provide a vanadium dioxide nanorod with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B82B3/00C01G31/02
Inventor 陈文麦立强徐庆彭俊锋朱泉峣周静黄学辉
Owner 武汉理工力强能源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap