Gel capable of injecting temperature sensitive complex and its preparation method
A complex and gel technology, applied in the field of material science, can solve problems such as unfavorable salt resistance, and achieve the effect of broadening the scope of application and maintaining excellent performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] Embodiment 1. prior art:
[0027] Accurately weigh 1.0 g of chitosan and add it to 45 ml of 0.1 mol / l HCl solution. After dissolving at room temperature for 2 hours, filter with a G3 glass sand core funnel to filter out insoluble substances, and take 9 ml of chitosan filtrate. Weigh 420 mg of β-GP and dissolve it in 1 ml of distilled water, and carefully add it dropwise into the chitosan filtrate under continuous stirring to obtain a uniform and clear solution, and then continue to stir for about 20 min. The pH of the final solution was 7.0.
[0028] The prepared complex solution is in a liquid state at room temperature, and gels at a body temperature of 37°C. The gelation time at 37°C is about 10 minutes, and the gel strength is about 0.126KPa.
Embodiment 2
[0030] Accurately weigh 1.0 g of chitosan and add it to 45 ml of 0.1 mol / L HCl solution. After dissolving at room temperature for 2 hours, filter with a G3 glass sand core funnel to filter out insoluble substances, and take 9 ml of chitosan filtrate. The GP (the percentage content of α-GP in GP is 30%w / w) that takes by weighing 420mg is dissolved in 1ml distilled water, under the condition of continuous stirring, carefully drop in the chitosan filtrate, finally obtain uniform and clear solution, and continue to stir for about 20 min. The pH of the final solution was 7.15.
[0031] This complex solution, compared with the system using β-GP alone in Example 1, without increasing the salt content of the system, IGT decreased from 37°C to 29°C, and the gelation time at 37°C was shortened from 10min to 200s, and the gel strength increased about 4 times.
Embodiment 3
[0033] Accurately weigh 1.0 g of chitosan and add it to 45 ml of 0.1 mol / L HCl solution. After dissolving at room temperature for 2 hours, filter with a G3 glass sand core funnel to filter out insoluble substances, and take 9 ml of chitosan filtrate. Weigh 50 mg of disodium hydrogen phosphate and 200 mg of β-GP and dissolve them in 1.0 ml of distilled water, and carefully drop them into the chitosan filtrate under continuous stirring to obtain a uniform and clear solution, and then continue to stir for about 20 min. The pH of the final solution was 6.95.
[0034] The complex solution can gel at 37°C, and the gelation time and gel strength at 37°C are equivalent to those of the system using β-GP alone in Example 1, but the salt content in the system is changed from 4.0%w / The w dropped to 2.4% w / w, a 40% drop in salt content.
PUM
Login to view more Abstract
Description
Claims
Application Information
Login to view more - R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap