Preparation technology for composite of epoxy resin nano silicon dioxide

A technology of nano-silica and epoxy resin, which is applied in the preparation process of epoxy resin composite materials, can solve problems such as complex processes, and achieve the effects of uniform mixing, increased dispersion and dispersion stability, and excellent mechanical properties

Inactive Publication Date: 2005-03-23
CHANGJIANG RIVER SCI RES INST CHANGJIANG WATER RESOURCES COMMISSION
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The traditional preparation process of epoxy resin nano-silica composite material is to use dispersant to nano-SiO 2 The surface is modified, and then the modified nano-SiO 2 Dispersed into the epoxy resin, due to the nano-SiO 2 The surface needs to be modified first, so the process is complicated; in addition, how to solve the problem of uniform dispersion of nanoparticles in the epoxy resin matrix, the aging (weather resistance) of epoxy resin, and improve the preparation level and efficiency still needs further research.
At the same time, the application research of nano-material modified epoxy resin in hydraulic engineering is still a blank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation technology for composite of epoxy resin nano silicon dioxide
  • Preparation technology for composite of epoxy resin nano silicon dioxide
  • Preparation technology for composite of epoxy resin nano silicon dioxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In the case of high-speed dispersion (5000-6000r / min), 0.1-5.0 parts by weight of nano silicon dioxide (SiO 2 ) particles are directly added to 95-105 parts by weight of liquid epoxy resin, and dispersed at high speed for 40 minutes; then add 40-60 parts by weight of water-based amine curing agent, mix evenly at a slow speed (100-200r / min), and mature for 20 minutes. The mixture was poured into a mold made of polytetrafluoroethylene, cured at constant temperature and humidity for 14 days (T=23±2° C., RH=55±5%), and the obtained polymer film was used for various performance tests.

Embodiment 2

[0023] Under the action of ultrasonic waves, the nanoparticles are directly dispersed in the liquid epoxy resin. Others are the same as method 1.

Embodiment 3

[0025] Under the action of ultrasonic waves, the nano-silica particles are firstly dispersed in 10-60 parts by weight of epoxy active diluent, and then mixed evenly with epoxy resin under the action of a high-speed disperser. Others are the same as method 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is a preparing process of epoxy resin nano-SiO2 composite, under the action of ultrasonic wave, adding nano-SiO2 particles to the mixed solutin of silane coupling agent and epoxy active diluter for uniformly mixing, mixing with epoxy resin uniformly by high speed dispersion, then adding in water-borne amine hardener, making low-speed dispersion and curing, pouring the mixture into a mould: constant-temperature and constant-humidity curing for 14 days at T=23plus or minus 2 deg.C and RH= 55 plus or minus 5%, and obtaining it. The nano-SiO2 particles need no surface preprocessing but are directly added to the silane coupling agent-epoxy resin system, thus simplifying the operating procedures of complicated nano-particle surface preprocessing, drying, etc, and improving various properties of epoxy resin composite, beneficial to product industrialization.

Description

technical field [0001] The invention relates to a preparation process of epoxy resin composite material, more specifically, it is a preparation process of epoxy resin composite material modified by adding nano silicon dioxide particles. The composite material prepared by this process has good physical and mechanical properties, thermal properties and weather resistance; it is suitable for use as anti-shock and wear-resistant materials, anti-cavitation materials, concrete coating materials, chemical grouting materials, etc. in water conservancy and hydropower projects. Background technique [0002] Epoxy resin has good mechanical properties, dielectric properties and outstanding bonding ability. It has been widely used as a composite material matrix, coating, electrical insulation material, adhesive, etc., and plays a leading role in thermosetting resins. In the application field of hydraulic materials, because these properties of epoxy resin meet some special requirements of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K3/36C08L63/00
Inventor 汪在芹李珍魏涛夏正斌李晓鄂苏杰黄良锐
Owner CHANGJIANG RIVER SCI RES INST CHANGJIANG WATER RESOURCES COMMISSION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com