Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Magnetic brick with electromagnetic shielding and decoration functions and its preparation method thereof

A technology of electromagnetic shielding and tiles, applied in the field of tiles with electromagnetic shielding and decorative functions and its preparation, to achieve good architectural decoration functions, overcome the influence of toxicity, and make molds simple

Inactive Publication Date: 2005-11-23
SOUTH CHINA UNIV OF TECH
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The toxicity of acrylamide has become a bottleneck restricting the industrial application of this technology in addition to process factors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] In terms of parts by mass, add 5 parts of hydroxyethyl methacrylate and tetraethylene glycol diacrylate mixture prepared by mixing according to the mass ratio of 10:1 into 100 parts of deionized water, 3 parts of Duramax TMD-3005, 0.17 parts of ammonium persulfate, mixed well and evenly to make a monomer solution. Subsequently, in terms of parts by mass, 70 parts of Ni—Zn soft ferrite powder was mixed with 30 parts of the monomer solution prepared in the previous step to prepare a suspension system. Then the suspension system is poured into a forming mold, heated to 70° C., kept for 3 hours, demolded and dried to make a tile green body. Finally, glazing and printing the tile blanks; and keeping the glazed and printed tile blanks at 1200° C. for 4 hours, and the tiles with electromagnetic shielding and decorative functions can be fired at one time. After testing, the density of the prepared tiles is 4.60g / cm 3 , the reflection loss in the frequency range of 30 ~ 300MHz...

Embodiment 2

[0024] In terms of parts by mass, add 15 parts of a mixture of hydroxyethyl methacrylate and tetraethylene glycol diacrylate prepared by mixing according to a mass ratio of 25:1 into 100 parts of deionized water, and then add 3 parts of Water-soluble polymer material PEO, 5 parts of Duramax TM D-3005, 0.3 part of ammonium persulfate, made into monomer solution. Then, in parts by mass, 75 parts of Ni-Zn soft magnetic ferrite powder was mixed with 25 parts of the monomer solution prepared in the previous step to obtain a suspension system; and the suspension system was poured into a molding mold and heated to 60°C , keep warm for 6 hours, demould, dry, and make tile green body. Afterwards, glaze and print the green tiles; and heat the green tiles for glazing and printing at 1200° C. for 3 hours, and fire them once to produce tiles with electromagnetic shielding and decorative functions. After testing, the density of the prepared tiles is 4.78g / cm 3 , the reflection loss in t...

Embodiment 3

[0026] In terms of parts by mass, add 18 parts of hydroxyethyl methacrylate and tetraethylene glycol diacrylate mixture prepared by mixing according to the weight to mass ratio of 35:1 in 100 parts of deionized water, and then add 10 parts 1 part of water-soluble polymer material PVP, 7 parts of dispersant Duramax TM D-3005, 0.5 part of ammonium persulfate, made into monomer solution. Then, in parts by mass, 78 parts of Ni-Zn soft magnetic ferrite powder and 22 parts of the monomer solution prepared in the previous step were mixed to obtain a suspension system; and the suspension system was poured into a molding mold and heated to 65°C , keep warm for 2 hours, demould, dry, and make tile green. Subsequently, glaze and print the green tiles; and heat the green tiles for glazing and printing at 1300° C. for 4 hours, and fire them once to produce magnetic tiles with electromagnetic shielding and decorative functions. After testing, the density of the prepared tiles is 4.80g / cm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a magnetic brick with electromagnetic shielding and decoration functions and its preparation method which comprises charging the mixture of hydroxyethyl methacrylate and triethylene glycol dimethylacrylate mixed by the mass ratio of 10 : (50-1), water-soluble macromolecular material, dispersing agent, initiating agent into deionized water, mixing to prepare monomer solution, then charging soft magnetic ferrite powder into the prepared monomer solution, mixing to obtain suspension system, then pouring the suspension system into molding dies, heating, thermal insulating, demoulding, drying, thus obtaining ceramic tile plain blanks, then glazing and stamping on the blanks, finally thermal insulating 3-4 hours at 1200-1400 deg. C.

Description

technical field [0001] The invention relates to the technical field of anti-electromagnetic interference material preparation and magnet molding processing, in particular to a magnetic tile with electromagnetic shielding and decoration functions and a preparation method thereof. Background technique [0002] Electromagnetic interference (EMI), or electromagnetic noise, is an invisible pollution that cannot be sensed by the senses due to the development of electronic technology, especially the popularization and application of digital circuits, mobile communications and switching power supplies. With the rapid development of information technology, especially the rapid popularization of mobile communications, computers, and household appliances, electronic products have been widely used in various fields of people's daily production and life. On the other hand, in order to reduce the size of the equipment and improve the performance of the equipm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/26
Inventor 车晓舟
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com