Potassium tripolyphosphate preparation method
A technology of potassium tripolyphosphate and potassium carbonate, applied in chemical instruments and methods, phosphorus compounds, inorganic chemistry, etc., to achieve the effects of saving equipment investment, reducing production costs, and simplifying process operations
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1
[0025] Potassium carbonate is used as potassium source, 105% superphosphoric acid is used as phosphorus source, and the molar ratio K 2 O:P 2 O 5 = 5.0: 3, and the initial temperature of raw material potassium carbonate and raw material superphosphoric acid is raised to 60 ℃, and the potassium carbonate of 1.60kg is metered into the feed hopper of the twin-screw at a speed of 7.10 g / min using a feeding screw, and at the same time, 1.30 kg of 105% superphosphoric acid was also metered into the twin-screw feed hopper using a peristaltic pump at a rate of 5.76 g / min. The extruder barrel had 4 heated barrel-jacketed temperature control sections, self-feeding from the feed hopper. The temperature of the head part is set as follows: 95°C, 230°C, 380°C, 510°C, the residence time of the material in the extruder barrel is 0.5 hour to 1 hour, and the obtained potassium tripolyphosphate is in the extruder. The top of the powder is discharged in the form of white pow...
Example Embodiment
[0026] Example 2
[0027] The operation procedure is the same as in Example 1, except that the initial temperature of the raw material potassium carbonate and raw material superphosphoric acid is increased to 50 ° C, and the extruder barrel has 6 heating barrel jacket temperature control sections, from the feeding hopper to the machine. The temperature of the head part is set as follows: 80°C, 170°C, 240°C, 350°C, 460°C, 520°C, the residence time of the material in the extruder barrel is 1 hour to 1.5 hours, and the rest are the same;
Example Embodiment
[0028] Example 3
[0029] The operation procedure is the same as in Example 1, except that the initial temperature of the raw material potassium carbonate and raw material superphosphoric acid is increased to 40 ° C, and the extruder barrel has 9 heating barrel jacket temperature control sections, from the feeding hopper to the machine. The temperature of the head part is set as follows: 60°C, 130°C, 200°C, 260°C, 310°C, 370°C, 430°C, 490°C, 530°C, and the residence time of the material in the extruder barrel is 1.5 hours to 2 hour, the obtained potassium tripolyphosphate was discharged in the form of white powder at the top of the extruder, and the desired potassium tripolyphosphate product was obtained after being cooled to ambient temperature and pulverized to a fineness of 0.10 mm, and the rest were the same;
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap