Kettle type catalytic hydrogenation of C5 and C9 petroleum resin for removing color and foreign flavour

A petroleum resin and catalytic hydrogenation technology, which is applied in the hydrogenation of C5 and C9 petroleum resins catalyzed by skeleton nickel, can solve the problems of unstable quality indicators, small production scale of equipment, and low product quality, and achieve thermal stability and resistance Good oxidizing property, improved hue, and reduced production cost

Inactive Publication Date: 2006-07-19
DALIAN UNIV OF TECH
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the devices have small production scales, single varieties, and low product quality, especially the main quality indicators such as product chroma and softening point are unstable, and many devices are in a state of shutdown or semi-stop production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Put 11.2 grams of C in a tank-type high-pressure reactor with a volume of 75 milliliters 5 Petroleum resin, 30 milliliters of solvent A, 1.5 grams of activated modified skeleton nickel catalyst, airtightly replaced, then filled with 2.0 MPa of hydrogen, put into an oil bath and slowly heat up to 180 degrees, adjust the hydrogen valve to make the system The pressure reaches 6.0MPa, and then maintains for 6 hours, C 5 The hue of the resin is improved to light yellow and close to water white.

Embodiment 2

[0013] Put 11.2 grams of C in a tank-type high-pressure reactor with a volume of 75 milliliters 9 Petroleum resin, 30 milliliters of solvent A, 1.5 grams of activated modified skeleton nickel catalyst, airtightly replaced, then filled with 2.0 MPa of hydrogen, put into an oil bath and slowly heat up to 200 degrees, adjust the hydrogen valve to make the system The pressure reaches 6.0MPa, and then maintains for 4 hours, C 9 The hue of the resin is improved to light yellow and close to water white.

Embodiment 3

[0015] Put 8 grams of C in a tank-type high-pressure reactor with a volume of 75 ml 5 Petroleum resin, 25 milliliters of solvent B, 2 grams of activated modified skeleton nickel catalyst, airtightly replaced, then filled with 3.0 MPa hydrogen, put into an oil bath and slowly heat up to 200 degrees, adjust the hydrogen valve to make the system The pressure reaches 7.5MPa, and then maintains for 4 hours, C 5 The resin hue improved to water white.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to view more

Abstract

The disclosed hydrogenation and discolor method relates mainly to catalyze the C5 and C9 petroleum resin with modified frame nickel on mild condition. This invention reduces unsaturated bond in product obviously, and improves the resin hue to water white.

Description

technical field [0001] The invention belongs to framework nickel catalyst C 5 and C 9 Petroleum resin hydrogenation application technology field, is a kind of C 5 and C 9 Petroleum resin kettle-type catalytic hydrogenation decolorization and deodorization method Background technique [0002] Petroleum resin is a by-product of ethylene plant C 5 、C 9 Distillate is the main raw material, and it is polymerized in the presence of a catalyst, or it is a thermoplastic resin obtained by copolymerizing it with aldehydes, aromatic hydrocarbons, and terpenes. Its molecular weight is generally less than 2000, and its softening point is 5-150°C. It is a thermoplastic viscous liquid or solid. According to different raw material sources and polymerization methods, it is generally divided into: C-5 (aliphatic hydrocarbon resin), C-5 / C-9 (aliphatic hydrocarbon, aromatic hydrocarbon resin), C-9 (aromatic hydrocarbon resin) and dicyclopentadiene vinyl resin (DCPD). Petroleum resin has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F240/00C08F8/04
Inventor 吕连海荣泽明胡爽袁忠义杜文强郭方郭文革张好宽
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap