Alumina anode steel claw protection ring and method for producing the same

A technology of anode steel claw and production method, applied in the field of metallurgy, can solve the problems of thermal energy loss, increase the probability of electric effect, increase the amount of carbon residue in the fire hole, etc., and achieve the effects of reducing loss, reducing the probability of effect and increasing the content

Inactive Publication Date: 2006-07-19
邹建明 +1
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the carbon anode steel claw protection ring used in the production process of electrolytic aluminum is usually made of carbon or carbon-containing materials. During the manufacturing process, a large amount of asphalt and tar fumes that seriously pollute the environment will be produced; In the process of use, it is easy to burn excessively, and consume electric energy in vain, and the electric energy is converted into heat energy and lost, and at the same time releases CO 2 gas, increasing CO during electrolysis 2 Gas emissions have a certain impact on the environment
In the production process of electrolytic aluminum, because there is not enough oxygen to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Al in alumina material 2 o 3 The content is 95-100%, mixed with a proper amount of bentonite, and solidified after molding by a conventional method.

[0012] The obtained product has high production cost and good quality, and does not affect the quality of the aluminum ingot when used.

Embodiment 2

[0014] Al in alumina material 2 o 3 The content is 90-94%. It is mixed with appropriate amount of water glass and solidified after being molded by conventional methods.

[0015] The obtained product has relatively high production cost and good quality, has little impact on the quality of aluminum ingots during use, and has good performance-price ratio.

[0016] Example

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum oxide anode steel paw protection ring and the production process, wherein the ring is made from 20-100% of aluminum oxide and right amount of binder through mixing, forming and hardening by the conventional methods.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, specifically relates to an alumina anode steel claw protection ring, and also relates to a production method of the alumina anode steel claw protection ring. Background technique [0002] At present, the carbon anode steel claw protection ring used in the production process of electrolytic aluminum is usually made of carbon or carbon-containing materials. During the manufacturing process, a large amount of asphalt and tar fumes that seriously pollute the environment will be produced; In the process of use, it is easy to burn excessively, and consume electric energy in vain, and the electric energy is converted into heat energy and lost, and at the same time releases CO 2 gas, increasing CO during electrolysis 2 Gas emissions have a certain impact on the environment. In the production process of electrolytic aluminum, because there is not enough oxygen to completely burn off the carbon powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25C3/12
Inventor 邹建明阮正林
Owner 邹建明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap