Method for producing slag forming agent contg. high calcium and low silicone by corundum arc furnace
An electric arc furnace and slag-forming agent technology, applied in the field of smelting, can solve the problems of high content of harmful impurities, affecting the production of high-quality steel, unstable performance indicators, etc., and achieve the effects of thorough chemical reaction, stable performance indicators, and strong activity.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0013] Example 1:
[0014] Referring to the accompanying drawings, a method for producing high-calcium and low-silicon slag-forming agent with corundum electric arc furnace, comprising the following steps:
[0015] (1) batching: the raw material is crushed to 2-15mm, then mixed batching according to the following proportions, slaked bauxite 4200kg, quicklime 5300kg, calcite 4kg, coke 1kg;
[0016] (2) Smelting: the raw materials are put into the 3000KVA corundum in stages and poured into the electric arc furnace, 1000kg is put into the electric arc furnace before the furnace is started, and the remaining materials are put in 3 times on average. When the material layer is completely melted, the material surface turns red and forms a soft cover, the furnace can be stopped;
[0017] (3) pour the furnace, pick up the package and cool;
[0018] (4) Classification: the unqualified crystals are crushed to 0-15mm for later use (after reaching a certain amount, they are returned to b...
Example Embodiment
[0020] Example 2:
[0021] Referring to the accompanying drawings, a method for producing high-calcium and low-silicon slag-forming agent with corundum electric arc furnace, comprising the following steps:
[0022] (1) batching: the raw material is crushed to 2-15mm, then mixed batching according to the following proportions, slaked bauxite 4300kg, quicklime 5200kg, calcite 3kg, coke 2kg;
[0023] (2) Smelting: The raw materials are put into the 3000KVA corundum by stages and poured into the electric arc furnace, 2000kg is put in before the furnace is started, and the remaining materials are put in 4 times on average, after the current and voltage are stabilized for 20-30min, 2000kg each time. When the material layer is completely melted, the material surface turns red and forms a soft cover, the furnace can be stopped;
[0024] (3) pour the furnace, pick up the package and cool;
[0025] (4) Classification: the unqualified crystals are crushed to 0-15mm for later use (after...
Example Embodiment
[0027] Example 3:
[0028] Referring to the accompanying drawings, a method for producing high-calcium and low-silicon slag-forming agent with corundum electric arc furnace, comprising the following steps:
[0029] (1) batching: the raw material is crushed to 2-15mm, then mixed batching according to the following proportions, slaked bauxite 4500kg, quicklime 5000kg, calcite 3kg, coke 2kg;
[0030] (2) Smelting: The raw materials are put into the 3000KVA corundum and poured into the electric arc furnace in stages, and 3000kg is put into the electric arc furnace before the furnace is started. The remaining materials are put in 3 times on average. When the material layer is completely melted, the material surface turns red and forms a soft cover, the furnace can be stopped;
[0031] (3) pour the furnace, pick up the package and cool;
[0032] (4) Classification: the unqualified crystals are crushed to 0-15mm for later use (after reaching a certain amount, they are returned to b...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap