The invention relates to a manufacturing method for heat-proof pressure-proof aluminum wire aluminum foil. The technology process is that: taking softening and cleaning process to the bare aluminum wire aluminum foil or aluminum band, taking continuously anode oxidation by 100-1000HZ 38V AC voltage at 2.6 +/-0.3m/min in electrolytic tank electrolyte; putting into the solution made up of water, vitriol and oxalic acid to form 0.02-0.04mm A1203 oxide film, washing and drying. The invention has thick aluminum film, good heat proof pressure proof ability, low cost, high efficiency, good safety, and has great application prospect.

Description

1. Technical field [0001] The invention relates to a production method of aluminum wire and aluminum foil for winding electrical appliances, in particular to a production method of temperature-resistant and pressure-resistant oxide film aluminum wire and aluminum foil. 2. Background technology [0002] Aluminum wire and aluminum foil are commonly used materials in the production of electrical appliances, such as electric welding machines, general transformers, iron removers, electromagnets, rectifiers and other electrical equipment need to use aluminum wire and aluminum foil (tape) to wind the wire group, but in the process of use, these materials themselves It is not insulated. When using it, it needs to be coated with a layer of insulating material (such as insulating paint) or wrapped with a layer of insulating paper. In this way, the following problems will occur: [0003] 1. The temperature resistance and cost of insulating materials are important issues in the producti...

AI Technical Summary

Problems solved by technology

[0006] In view of the above situation, the purpose of the present invention is to provide an improved production method of temperature-resistant and voltage-resistant oxide film aluminum wire and aluminum foil, which can effectively solve the problems of temperature and voltage resistance of oxide film aluminum wire aluminum foil or aluminum strip and reduce production costs. The technical solution is to soften and heat-preserve the aluminum foil or strip of the bare aluminum wire, decontaminate it with a purification solution, rinse it with water, and use 100-1000HZ (Hertz) AC 38V to work in the electrolyte of the electrolytic cell. Voltage, continuous anodic oxidation at a speed of 2.6±0.3m per minut