Wear-resistant wood plastic floor and its production technology

A technology of wood-plastic flooring and production technology, which is applied in the field of decoration and decoration materials, can solve the problems of low mechanical properties, short service life, poor water resistance, and poor wear resistance, and achieve the effect of excellent weather resistance, corrosion resistance, and excellent mechanical properties

Active Publication Date: 2007-02-14
无锡市中德装饰新材料有限公司
View PDF0 Cites 82 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it has the advantages of lightness and cheap price, it has poor water resistance and wear resistance, low mechanical properties, instability, and it will also warp after watering, poor decorative effect, and short service life, so it is not easy to be accepted by people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant wood plastic floor and its production technology
  • Wear-resistant wood plastic floor and its production technology
  • Wear-resistant wood plastic floor and its production technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1: The production process steps of the wear-resistant wood-plastic floor in the embodiment of the present invention are as follows:

[0039] 1. Mixing and granulation of main and auxiliary materials of wood-plastic floor substrate:

[0040] First, the waste wood is crushed with sawdust and ground into waste wood sawdust powder with a fineness of 200 mesh; it is naturally dried and ready for use;

[0041] Get polyvinyl chloride (PVC) resin powder: 35% by weight, add waste wood sawdust powder: 40% by weight, active calcium carbonate (stone powder): 11% by weight, plastic reinforcing agent selects chlorinated polyethylene (CPE) for use Azodicarbonamide: 5% by weight, calcium carbonate (stone powder) as plastic filler: 3% by weight, AC foaming agent as plastic processing aid: 6% by weight, mixed at high speed, mixing temperature: 100°C , mixing time, 10 minutes, speed: 100 rpm; extruded into wood plastic granules through an extrusion mixer, temperature: 160 ° C,...

Embodiment 2

[0048] 1. Mixing and granulation of main and auxiliary materials of wood-plastic floor substrate:

[0049] First, the waste fiber material is crushed with grain straw (water content reaches 12-14%), and ground into waste grain straw powder with a fineness of 350 mesh; it is naturally dried and ready for use;

[0050]Get plastic raw material PE in the embodiment of the present invention: 45% by weight, add waste grain stalk powder: 30% by weight, active calcium carbonate (stone powder): 13% by weight, plastic reinforcing agent selects methyl methacrylate copolymer ( ACR) is: 4% by weight, calcium carbonate (stone powder) is selected as plastic filler: 2% by weight, foam regulator is selected as plastic processing aid: 6% by weight, mixed at high speed, mixing temperature: 110 ° C, mixing time , 13 minutes, speed: 110 rpm; extruded into wood plastic pellets through the extrusion mixer, temperature: 190 ° C, screw speed: 35 rpm;

[0051] 2. Production of wood-plastic floor subst...

Embodiment 3

[0056] 1. Mixed granulation of main and auxiliary materials of wood-plastic floor substrate:

[0057] First, the waste wood is crushed with wood twigs (water content reaches 12-14%), and ground into waste wood twig powder, the fineness reaches 500 mesh; natural drying, stand-by;

[0058] Get the plastic raw material PP in the embodiment of the present invention: 55% by weight, add wood branch powder: 20% by weight, active calcium carbonate (stone powder): 15% by weight, plastic reinforcing agent selects chlorinated polyethylene (CPE) as: 3% by weight, wood fiber powder as plastic filler: 1% by weight, calcium stearate as 6% by weight as plastic processing aid, mixed at high speed, mixing temperature: 120°C, mixing time, 15 minutes, rotating speed: 120 revolutions per minute; extruded into wood-plastic granules through the extrusion mixer, the temperature is: 200 ° C, the screw speed is: 40 revolutions per minute;

[0059] 2. Production of wood-plastic floor substrate:

[006...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention is wear-resistant wood-plastic floor board and its production process, and belongs to the field of decoration material technology. Polyvinyl chloride resin or plastic material is added with waste wood powder or fiber material powder, active calcium carbonate, assistant, stuffer, etc, and the mixture is pelletized, and further treated through extruding, molding, vacuum cooling, settling, drawing and cutting to form the basic wood-plastic board. The basic wood-plastic board is polished, groove milled and covered with surface decoration layer to form the wear resistant wood-plastic floor board product. The wear resistant wood-plastic floor board is beautiful, wear resistant, fireproof, waterproof, non-skid, anticorrosive and environment friendly and has high strength, heat insulation, electrical insulation and other advantages.

Description

technical field [0001] The invention relates to a wear-resistant wood-plastic floor and its production process, specifically for decoration of homes and offices, and belongs to the technical field of decoration materials. Background technique [0002] The floor that is used for family, office room decoration usually adopts solid wood floor or compound floor on the market at present. Solid wood flooring consumes a lot of wood and is expensive. Although it has the advantages of wear resistance, it has poor water resistance after laying and use, and is easy to crack and warp. Composite flooring is made by mixing and extruding wood chips and adhesives. Although it has the advantages of lightness and cheap price, it has poor water resistance and wear resistance, low mechanical properties, instability, and it will also warp after being soaked in water. The decorative effect is poor and the service life is short, so it is not easy to be accepted by people. Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08L23/12C08L67/00C08K3/26B29C47/40B29D7/00C08L97/02
Inventor 庄广盛
Owner 无锡市中德装饰新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com