a technology of resin composition and composition, applied in the direction of synthetic resin layered products, semiconductor/solid-state device details, transportation and packaging, etc., can solve the problems of reduced productivity, mechanical and electrical failure of electronic devices, and significant mechanical stress experienced in the construction of chips, so as to reduce the misalignment of chips, improve transparency, and reduce the effect of

Inactive Publication Date: 2005-08-04
MOMENTIVE PERFORMANCE MATERIALS INC
View PDF11 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0006] Thus, improved underfill materials having low CTE and improved transparency which ...

Problems solved by technology

While flip chip technology has been developed to respond to these demanding requirements, a weak point of the flip chip construction is the significant mechanical stress experienced by solder bumps during thermal cycling due to the coefficient of thermal expansion (“CTE”) mismatch between silicon die and substrate.
This mismatch, in turn, causes mechanical and electrical failures of the electronic devices.
Currently, capillary underfill is used to fill gaps between silicon chip and substrate and improve the fatigue life of solder bumps; however capillary underfill based fabrication processes introduce additional steps into the chip assembly process that reduce pr...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin compositions and methods of use thereof
  • Resin compositions and methods of use thereof
  • Resin compositions and methods of use thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0082] Preparation of functionalized colloidal silica (FCS) predispersion. A functionalized colloidal silica predispersion was prepared by combining the following: 935 g of isopropanol (Aldrich) was slowly added by stirring to 675 grams of aqueous colloidal silica (Nalco 1034A, Nalco Chemical Company) containing 34 weight % of 20 nm particles of SiO2. Subsequently, 58.5 g phenyl trimethoxysilane (PTS) (Aldrich), which was dissolved in 100 g isopropanol, was added to the stirred mixture. The mixture was then heated to 80° C. for 1-2 hours to afford a clear suspension. The resulting suspension of functionalized colloidal silica was stored at room temperature. Multiple dispersions, having various levels of SiO2 (from 10% to 30%) were prepared for use in Example 2.

example 2

[0083] Preparation of dispersion of a functionalized colloidal silica in epoxy resin. A round bottom 2000 ml flask was charged with 540 g of each of the pre-dispersions, prepared in Example 1. Additional pre-dispersion compositions are shown in Table 1, below. 1-methoxy-2-propanol (750 g) was then added to each flask. The resulting dispersion of functionalized colloidal silica was vacuum stripped at 60° C. and 60 mmHg to remove about 1L of solvents. The vacuum was slowly decreased and solvent removal continued with good agitation until the dispersion weight had reached 140 g. The clear dispersion of phenyl-functionalized colloidal silica contained 50% SiO2 and no precipitated silica. This dispersion was stable at room temperature for more than three months. The results in Table 1 show that a certain level of phenyl functionality is required in order to prepare a concentrated, stable FCS dispersion in 1-methoxy-2-propanol (Dispersion 1 through 5). The functionality level can be adjus...

example 3

[0084] Preparation of a dispersion of capped functionalized colloidal silica in epoxy resin. A solution combining 5.33 g of epoxy cresol novolac (ECN 195XL-25 available from Sumitomo Chemical Co.), 2.6 g of novolac hardener (Tamanol 758 available from Arakawa Chemical Industries) in 3.0 g of 1-methoxy-2-propanol was heated to about 50° C. A 7.28 g portion of the solution was added, dropwise, to 10.0 g of the FCS dispersion, by stirring at 50° C. (see, Table 1, entry #3, 50% SiO2 in methoxypropanol, above). The clear suspension was cooled and a catalyst solution of N-methylimidazole, 60 microliters of a 50% w / w solution in methoxypropanol was added by stirring. The clear solution was used directly to cast resin films for characterization or stored at −10° C. Additional films were prepared using differing catalysts in various amounts and some variations in the epoxy as set forth in Table 2 below which shows final resin compositions.

[0085] Films were cast by spreading a portion of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Percent by massaaaaaaaaaa
Percent by massaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

A composition comprises a first curable resin composition that includes at least one aromatic epoxy resin in combination with a solvent, a functionalized colloidal silica dispersion, and at least one other component selected from the group consisting of cycloaliphatic epoxy monomers, aliphatic epoxy monomers, hydroxy aromatic compounds, combinations thereof, and mixtures thereof. The composition can include a separate second curable fluxing composition that comprises at least one epoxy resin. The first curable resin or the combination of the two resin compositions is useful in producing underfill materials and is suitable for use as an encapsulant for electronic chips.

Description

CROSS REFERENCE TO RELATED APPLICATIONS [0001] This patent application is a continuation-in-part patent application of U.S. Ser. No. 10 / 737,943, filed Dec. 16, 2003, which is a continuation-in-part patent application of U.S. Ser. No. 10 / 654378, filed Sep. 3, 2003, and U.S. Ser. No. 10 / 736946, filed Dec. 16, 2003. The priority of these patent applications is hereby claimed, and the entire contents of these patent applications are hereby incorporated by reference.BACKGROUND OF THE INVENTION [0002] The present disclosure relates to the use of a first curable resin composition in combination with a second curable fluxing resin composition in underfill materials. More specifically, the first curable resin composition includes a thermosetting resin, solvent and functionalized colloidal silica. The second curable fluxing resin composition preferably includes a thermosetting epoxy resin and optional additives. The final cured composition has a low coefficient of thermal expansion and a high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/38
CPCC08G59/24H01L2924/01087C08G59/4215C08G59/68C08K3/36H01L21/563H01L23/293H01L2224/73203H01L2924/01012H01L2924/01013H01L2924/0102H01L2924/01049H01L2924/01051H01L2924/01077H01L2924/01078H01L2924/01079H01L2924/10253H01L2924/01322H01L2924/01005H01L2924/01006H01L2924/01019H01L2924/01024H01L2924/01033H01L2924/0104H01L2924/01042H01L2924/01047H01L2924/01072H01L2924/01074C08G59/3218C08L63/00H01L2924/00Y10T428/31511
Inventor CAMPBELL, JOHN ROBERTRUBINSZTAJN, SLAWOMIRGIBSON, DAVID ALEXANDER IIITONAPI, SANDEEP SHRIKANTMILLS, RYAN CHRISTOPHERPRABHAKUMAR, ANANTH
Owner MOMENTIVE PERFORMANCE MATERIALS INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap