Antioxidant stabilized crosslinked ultra-high molecular weight polyethylene for medical device applications

Abstract

An antioxidant combined with UHMWPE prior to subjecting the UHMWPE to crosslinking irradiation. In one exemplary embodiment, the antioxidant is tocopherol. After the antioxidant is combined with the UHMWPE, the resulting blend may be formed into slabs, bar stock, and/or incorporated into a substrate, such as a metal, for example. The resulting product may then be subjected to crosslinking irradiation. In one exemplary embodiment, the UHMWPE blend is preheated prior to subjecting the same to crosslinking irradiation. Once irradiated, the UHMWPE blended product may be machined, packaged, and sterilized in accordance with conventional techniques.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS[0001]This application claims the benefit under Title 35 U.S.C. § 119(e) of U.S. Provisional Patent Application Ser. No. 60 / 922,738, entitled AN ANTIOXIDANT STABILIZED CROSSLINKED ULTRA-HIGH MOLECULAR WEIGHT POLYETHYLENE FOR MEDICAL DEVICE APPLICATIONS, filed on Apr. 10, 2007, the entire disclosure of which is expressly incorporated by reference herein.BACKGROUND[0002]1. Field of the Invention.[0003]The present invention relates to crosslinked ultra-high molecular weight polyethylene and, particularly, to antioxidant stabilized, crosslinked ultra-high molecular weight polyethylene.[0004]2. Description of the Related Art.[0005]Ultra-high molecular weight polyethylene (UHMWPE) is commonly utilized in medical device applications. In order to beneficially alter the material properties of UHMWPE and decrease its wear rate, UHMWPE may be crosslinked. For example, UHMWPE may be subjected to electron beam irradiation, gamma irradiation, or x-ray irradi...

AI Technical Summary

Benefits of technology

[0009]In one exemplary embodiment, the formed UHMWPE/antioxidant blend may be subjected to multiple passes of crosslinking irradiation. By irradiating the blend in multiple passes, the maximum dose of radiation received by the UHMWPE blend at any one time is lessened. As a result, the maximum temperature of the UHMWPE blend reached during irradiation is correspondingly lessened. This allows for the UHMWPE to maintain a higher level of desirable mechanical properties and prevents substantial melting of the UHMWPE. In one exemplary embodiment, the UHMWPE is cooled after each individual pass of crosslinking irradiation. By allowing the UHMWPE blend to cool, the temperature at the time of subsequent irradiation is high enough to encourage the mobility of the individual polyethylene molecules, but is also low enough that the temperature increase experienced during irradiation is unlikely to substantially alter any desired material properties of the UHMWPE blend.

[0010]Advantageously, by incorporating an antioxidant, such as tocopherol, into the UHMWPE prior to subjecting the same to crosslinking irradiation, the UHMWPE may be stabilized without the need for post irradiation melt annealing or any other post-irradiation treatment to quench free radicals. Specifically, an antioxidant, such as tocopherol, acts as a free radical scavenger and, in particular, acts as

Problems solved by technology

Oxidation detrimentally affects the material properties of UHMWPE and may also increase its wear rate.

By allowing the UHMWPE blend to cool, the temperature at the time of subsequent irradiation is high enough to encourage the mobility of the individual polyethylene molecules, but is also low enough that the temperature increase experienced during irradiation is unlikely to substantially alter an