Resin composition, cured resin product, wiring board, and manufacturing method for wiring board

a technology of resin products and wiring boards, applied in the direction of synthetic resin layered products, applications, synthetic resin products, etc., can solve the problems of inability to use help, unclear degree of effect, etc., and achieve high adhesive force and high adhesive force

Inactive Publication Date: 2013-08-08
HITACHI CHEM CO LTD
View PDF7 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The invention provides a resin composition that has strong adhesion to wiring conductors even when the surface of the insulating resin layer is small and irregular. Additionally, even when treated with a roughening liquid to remove smear from via holes, the adhesive force between the resin and the wiring conductor is maintained. This results in a wiring board with improved performance and reliability.

Problems solved by technology

However, the strength of an adhesive force at the time of roughening treatment is not specifically disclosed, and a degree of its effect is unclear.
In addition, the polyphenylene ether resin which is used as the insulating resin in Patent Document 1 involves a problem in view of manufacture such that a xenon excimer lamp or a low pressure mercury vapor lamp each having a wavelength of not more than 300 nm, which is different from an ultraviolet ray lamp usually used for many purposes for post-exposure of a solder resist, or the like, cannot help being used.
In addition, in the technology disclosed in Patent Document 2, the insulating resin composition is not mentioned at all, and therefore, a degree of its effect is unclear.
In addition, a step of dipping in an ozone solution having an ozone concentration of 100 ppm or more is substantially essential, so that there is involved such a problem that the operation is complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin composition, cured resin product, wiring board, and manufacturing method for wiring board
  • Resin composition, cured resin product, wiring board, and manufacturing method for wiring board
  • Resin composition, cured resin product, wiring board, and manufacturing method for wiring board

Examples

Experimental program
Comparison scheme
Effect test

embodiment

[2-1] Embodiment a of the Second Invention

[Laminate Forming Step]

[0087]In the present step, a support-provided insulating resin layer composed of a laminate having an insulating resin layer and a support is formed.

[0088]A material of this support is not particularly limited so far as it is sparingly soluble in a desmearing treatment liquid which is used in a desmearing treatment step as described later, and a synthetic resin, a metal, and the like are useful. As the synthetic resin, polyester films with heat resistance, such as polyethylene terephthalate (PET), polyethylene naphthalate (PEN), etc., are preferable. As the metal, copper is preferable.

[0089]A thickness of this support is not particularly limited so far as it is a thickness such that the occurrence of exposure of a part of the surface of the insulating resin layer to be caused due to dissolution in a process of the desmearing treatment step is prevented. The thickness of the support is preferably from about 10 to 200 μm...

modification example 1

[2-2] Modification Example 1 of Embodiment a of the Second Invention:

[0117]In the foregoing Embodiment A of the second invention, the ultraviolet ray irradiation step is carried out after the support removal step and before the wiring forming step, but it should not be construed that the second invention is limited thereto.

[0118]For example, the ultraviolet ray irradiation step may be carried out after the hole forming step and before the desmearing treatment step. In that case, after the hole forming step, ultraviolet rays are irradiated on the insulating resin layer from the support side of the laminate. The ultraviolet rays transmit through the support to reach the surface of the insulating resin layer, thereby enhancing an adhesive force of this surface of the insulating resin layer to the wiring.

[0119]Incidentally, a material of the support which is used in this Modification Example 1 is not particularly limited so far as it is sparingly soluble in the desmearing treatment liqu...

modification example 2

[2-3] Modification Example 2 of Embodiment a of the Second Invention:

[0123]In addition, the ultraviolet ray irradiation step may also be carried out after the desmearing step and before the support removal step. In that case, after the desmearing step, ultraviolet rays are irradiated on the insulating resin layer from the support side of the laminate. The ultraviolet rays transmit through the support to reach the surface of the insulating resin layer, thereby enhancing an adhesive force of this surface of the insulating resin layer to the wiring.

[0124]Incidentally, a material of the support which is used in this Modification Example 2 is not particularly limited so far as it is sparingly soluble in the desmearing treatment liquid which is used in the desmearing treatment step and is able to transmit ultraviolet rays therethrough, and a synthetic resin is useful. As the synthetic resin, polyester films with heat resistance, such as polyethylene terephthalate (PET), polyethylene napht...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
temperatureaaaaaaaaaa
Login to View More

Abstract

By producing a resin composition containing (A) an epoxy resin having two or more epoxy groups in one molecule thereof and containing a hexanediol structure, (B) an ultraviolet ray active ester group-containing compound, and (C) an epoxy resin curing accelerator, even in a state where an irregular shape of the surface of an insulating resin layer is small, a high adhesive force to a wiring conductor can be easily revealed.

Description

TECHNICAL FIELD[0001]The present invention relates to a resin composition, a cured resin product, a wiring board, and a method for manufacturing a wiring board. In more detail, the present invention relates to an insulating resin capable of revealing a high adhesive force to a wiring conductor even in a state where an irregular shape of the surface of an insulating resin layer is small, and also to a wiring board and a method for manufacturing a wiring board.BACKGROUND ART[0002]Miniaturization, weight reduction and multifunctionalization of electronic instruments make remarkable progress. Following this, high integration of LSI, chip parts, and the like makes progress, and forms thereof are rapidly changed to a multi-pin system or a miniaturized system. Therefore, in order to enhance a mounting density of electronic parts, the development of a wiring board capable of coping with fine wiring is advanced. As such wiring boards, there is a wiring board of a build-up system in which a g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): C09D163/00H05K1/03
CPCC08L63/00H05K1/0353H05K3/46C08G59/38H05K1/0306C08G59/24C09D163/00H05K3/00H05K3/0055H05K3/386H05K3/4632H05K3/4644C08G59/22C08G59/4223C08G59/4276C08G59/68B32B27/18B32B27/16B32B27/38B32B2457/08
Inventor MORITA, MASAKINAKAMURA, KONATSUTAKANEZAWA, SHIN
Owner HITACHI CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com