High temperature resistant anti-corrosion coating and its preparation method

A technology for anti-corrosion coatings and high temperature resistance, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of no heat resistance and corrosion resistance improvement

Inactive Publication Date: 2010-01-27
JIANGSU RONGCHANG NEW MATERIAL TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent 200710098668.4 discloses an epoxy silicone anti-corrosion coating, the cumulative time of salt spray can reach up to 360h, and the corrosion resistance is excellent, but the heat resistance and corrosion resistance have not been improved at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The present invention will be further described below in conjunction with specific embodiments, but not limited thereto.

[0028] Add 100 parts of epoxy silicone resin ES-06 into a reaction vessel equipped with a thermometer, stirring, reflux and dropping device, start stirring and raise the temperature to 70-90°C, and evenly add phosphate ester monomer dropwise within 2-3 hours. The mixed solution of 8 parts of PAM-100 and 40 parts of xylene, and 8 parts of TDI, after the dropwise addition, keep warm for 3 to 4 hours to complete the synthesis of the resin, and obtain the phosphate and isocyanate modified epoxy silicone resin ESPN- 100.

[0029] Phosphate- and fluoropolymer-modified epoxy silicone resins ESPN-200 and ESPN-300 were prepared using phosphate monomers PAM-200 and PAM-300, respectively, and the preparation method was the same as ESPN-100.

[0030] Table 1 (the embodiment unit is parts by weight in the table)

[0031] components

raw material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-temperature resistant and anticorrosive coating and a preparation method thereof. The coating uses organic phosphate and isocyanate modified epoxy organic siliconresin as main materials. The epoxy organic siliconresin has good high-temperature resistant and anticorrosive performance; the introduction of organic phosphate radical not only can improve the high-temperature resistant performance of the resin, but also can improve the anticorrosive performance of the later period of the coating; during the film forming process of the coating, the organic phosphate radical and substrate metal can form a compact phosphate protecting film to lead the surface of the metal to be passivated so as prevent water molecules and salt ions from being contacted with the metal, thus leading the coating to have good anticorrosive function; isocyanate radical is introduced and reacts with epoxy radical to generate high-temperature resistant polyoxazolidine radical, thus improving the high-temperature resistant performance of the coating; the modified epoxy organic siliconresin is used by being matched with a high-temperature resistant pigment, thus leading the coating to be capable of not only keeping proper physical and mechanical performances, but also having good anticorrosive performance under the environment of high temperature of 550 DEG C.

Description

technical field [0001] The invention relates to a high-temperature-resistant anti-corrosion paint, in particular to a modified epoxy organic silicon anti-corrosion paint resistant to a high temperature of 550°C and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of high-tech, the requirements for high-temperature-resistant structural materials and high-temperature-resistant coatings have become higher and higher. Practice has proved that high-temperature structural materials must have good high-temperature strength and excellent anti-corrosion properties. Oxidation and corrosion resistance are more difficult and expensive. In contrast, high-temperature-resistant coatings have the above two advantages, which can not only improve the high-temperature resistance of materials, but also have certain corrosion resistance. Therefore, since the 1950s, people's research on high temperature resistant coatings has been in the asc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/06C09D5/08
Inventor 黄顺道常春陈群
Owner JIANGSU RONGCHANG NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap