High-strength light ceramic filler

A light-weight ceramic and high-strength technology, which is applied in the field of ceramic fillers, can solve the problems of reduced impact resistance and wear resistance, poor manufacturing process, and low compressive strength, so as to achieve increased filler pores and reasonable microstructure. , the effect of not easy to fall off

Inactive Publication Date: 2007-08-22
杨剑
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problems that the compressive strength of the clay filler in the above prior art is not very high, the impact resistance and wear resistance are reduced, the surface is not white, and the manufacturing process is not very good, the present invention proposes a material that not only has high compressive strength, but also has a high compressive strength. , good impact and wear resistance, long service life, high surface whiteness, high-strength lightweight ceramic filler with better manufacturing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1, the high-strength light-weight ceramic filler described in the present embodiment 1 is prepared with five kinds of raw material components of clay, black soil, calcium carbonate, talc and chaff bran powder, and the weight of described clay, black soil, calcium carbonate and talc The percentages are: clay 60%, black soil 15%, calcium carbonate 15%, talc 3%, the content of aluminum oxide in the clay is 25.3%, and the added amount of chaff chaff powder is clay, black soil, calcium carbonate and talc 10% of the total weight of the four raw materials, the percentage by weight of the chemical composition of the high-strength lightweight ceramic filler is: silicon dioxide 53.3%, aluminum oxide 14.4%, calcium oxide 6.7%, magnesium oxide 10.7%, potassium oxide 1.4%, sodium oxide 0.47%, ferric oxide 0.39%. And prepared according to the following process steps:

[0023] 1. Weigh the materials according to the above-mentioned various raw material process formulas, po...

Embodiment 2

[0036] Embodiment 2, the high-strength light-weight ceramic filler described in this embodiment 2 is prepared with five kinds of raw material components of clay, black soil, calcium carbonate, talc and chaff bran powder, and the weight of described clay, black soil, calcium carbonate and talc The percentages are: clay 70%, black soil 12%, calcium carbonate 10%, talc 6%, the content of aluminum oxide in the clay is 22.7%, and the added amount of chaff chaff powder is clay, black soil, calcium carbonate and talc 15% of the total weight of the four raw materials, the percentage by weight of the chemical composition of the high-strength lightweight ceramic filler is: silicon dioxide 56.1%, aluminum oxide 17.1%, calcium oxide 4.8%, magnesium oxide 12.1%, potassium oxide 0.9%, sodium oxide 0.61%, ferric oxide 0.55%. And prepared according to the process steps described in Example 1.

[0037] After testing, the main performance indicators of the high-strength lightweight ceramic fil...

Embodiment 3

[0043]Embodiment 3, the high-strength light-weight ceramic filler described in this embodiment 3 is prepared with five kinds of raw material components of clay, black soil, calcium carbonate, talc and chaff bran powder, and the weight of described clay, black soil, calcium carbonate and talc The percentages are: clay 78%, black soil 8%, calcium carbonate 8%, talc 10%, the content of aluminum oxide in the clay is 19.5%, and the added amount of the chaff bran powder is clay, black soil, calcium carbonate and talcum 20% of the total weight of the four raw materials, the percentage by weight of the chemical composition of the high-strength lightweight ceramic filler is: silicon dioxide 59.1%, aluminum oxide 16.3%, calcium oxide 3.9%, magnesium oxide 14.2%, potassium oxide 1.07%, sodium oxide 0.56%, ferric oxide 0.47%. And prepared according to the process steps described in Example 1.

[0044] After testing, the main performance indicators of the high-strength lightweight ceramic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
acid resistanceaaaaaaaaaa
Login to View More

Abstract

The high strength light ceramic filler is prepared with clay 60-78 wt%, black earth 8-15 wt%, calcium carbonate 8-15 wt%, talcum 3-10 wt% and rice bran powder for the rest. Chemically, it consists of silica 50-60 wt%, alumina 13-20 wt%, calcium oxide 3-8 wt% and magnesia 10-16 wt% except impurity. It has high compression strength, long service life, low impurity content, high whiteness and high porosity.

Description

technical field [0001] The invention relates to a ceramic filler, in particular to a high-strength and light-weight ceramic filler. Background technique [0002] With the development of modern science and technology and modern industry, in the reaction tower of chemical industry and metallurgy industry, in the distillation tower of industrial treatment and filtration and pharmaceutical industry, in the washing and desulfurization of coking industry, a large amount of light specific gravity and wet It is a filler with strong sex and adsorption, high acid and alkali resistance, good resistance to rapid cooling and heat, high compressive strength, large specific surface area, and the surface is not easy to fall off, so as to achieve the purpose of industrial use and treatment. At present, there are many types of fillers used, which are made of metal materials, wood, plastic and clay materials. Among these types of fillers, although metal has high strength, it has low acid and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/16C04B38/06C02F3/10
CPCY02W10/10
Inventor 杨剑杨昆
Owner 杨剑
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com