Multi-stage ordered medium hole/big hole composite material and preparation method thereof

A technology of composite carbon and carbon materials, applied in the fields of nanostructure manufacturing, nanotechnology, nanotechnology, etc., can solve the problems of cumbersome, numerous and excessive, and achieve the effect of cumbersome steps, easy availability of raw materials and broad application prospects.

Inactive Publication Date: 2007-09-26
FUDAN UNIV
View PDF0 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(Wang, Z.; Li, F.; Ergang, N.S.; Stein, A. Chem. Mater. 2006, 18, 5543-5553) The

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-stage ordered medium hole/big hole composite material and preparation method thereof
  • Multi-stage ordered medium hole/big hole composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The silica microsphere dispersion liquid with a solid content of 10wt.% and a particle size of 240nm was left to settle for two weeks, the supernatant was sucked off, then dried naturally and baked at 80°C for 12 hours before use. Take 1.0g heat-treated colloidal crystals of silica microspheres and immerse them in 4.0g ethanol solution containing 0.2g resole phenolic resin and 0.1g F127, volatilize at room temperature for 24h, take out the colloidal crystals and bake them at 100°C 24h, and then burn at 800°C for 5 hours under the protection of nitrogen to obtain carbon-containing colloidal crystals, place the calcined colloidal crystals in 10wt% HF aqueous solution and stir slowly for 24h, and the product is washed repeatedly with distilled water by centrifugation And vacuum drying to obtain ordered mesoporous / macroporous carbon material, the macropore diameter is about 230nm, the mesopore diameter is 10nm, and the mesoporous channel structure is three-dimensional cubic ...

Embodiment 2

[0024] The silica microsphere dispersion liquid with a solid content of 10wt.% and a particle size of 320nm was left to settle for two weeks, the supernatant was sucked off, then dried naturally and baked at 80°C for 12 hours before use. Take 1.0g heat-treated colloidal crystals of silica microspheres and immerse them in 5.0g ethanol solution containing 0.2g resole phenolic resin and 0.2g F127, volatilize at room temperature for 24h, take out the colloidal crystals and bake them at 120°C 8h, and then burned at 900°C for 6 hours under the protection of nitrogen gas to obtain carbon-containing colloidal crystals. The calcined colloidal crystals were placed in 10wt% HF aqueous solution and stirred slowly for 24h. The product was washed repeatedly with distilled water by centrifugation and vacuum drying to obtain an ordered mesoporous / macroporous carbon material. The macropore diameter is about 310nm, the mesopore diameter is 11nm, and the mesoporous channel structure is two-dimen...

Embodiment 3

[0026] The silica microsphere dispersion liquid with a solid content of 8wt.% and a particle size of 450nm was left to settle for two weeks, the supernatant was sucked off, then dried naturally and baked at 100°C for 12 hours before use. Take 1.0g heat-treated colloidal crystals of silica microspheres and immerse them in 5.0g ethanol solution containing 0.3g resole phenolic resin and 0.15g F108, volatilize at room temperature for 24h, take out the colloidal crystals and bake them at 100°C 24h, and then burn at 800°C for 5 hours under the protection of nitrogen to obtain carbon-containing colloidal crystals, place the calcined colloidal crystals in 10wt% HF aqueous solution and stir slowly for 24h, and the product is washed repeatedly with distilled water by centrifugation and vacuum drying to obtain an ordered mesoporous / macroporous carbon material. The macropore diameter is about 435nm, the mesopore diameter is 12nm, and the mesopore channel structure is three-dimensional cub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Large hole diameteraaaaaaaaaa
Apertureaaaaaaaaaa
Mesoporousaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparing method of metahloe or larger hole composite carbon material with multi-stage ordered structure, which comprises the following steps: making silica dioxide jelly mould crystal as metal mold plate; setting block copolymer surface activator of polyoxyethylene block as soft mold plate; making soluble phenol resin as carbon source; proceeding organic-organic assemble through gap of colloid crystal; compositing metahloe or larger hole composite carbon material with multi-stage pore path. This invention possess larger hole of ordered array of interconnected and optics forbidden region with continuously adjustable wavelength generated by the colloid crystal structure.

Description

technical field [0001] The invention belongs to the technical field of advanced nanocomposite materials, and in particular relates to a multi-level ordered mesoporous / metaporous composite carbon material and a preparation method thereof. technical background [0002] In recent years, mesoporous carbon materials have broad application prospects in catalyst supports, supercapacitor electrodes, and fuel cells due to their superior properties such as the electrical conductivity of carbon materials and the high specific surface area of ​​mesoporous materials. The synthesis of traditional mesoporous carbon materials is usually obtained by nanocasting. This method first synthesizes mesoporous silica materials with a certain structure, and then fills the pores of mesoporous silica materials with organic molecules. As a carbon precursor, the organic matter was then carbonized and the silica template was further removed to obtain a mesoporous carbon material replica with a channel str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B31/02C01B31/08B82B3/00
Inventor 邓勇辉刘翀郁挺屠波赵东元
Owner FUDAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap