Nano modified display shell position gum and preparing method thereof

A technology of nano-modification and positioning adhesive, which is applied in the direction of adhesives, attacking equipment, adhesive types, etc., which can solve the problems of difficult to guarantee sealing performance and slow construction speed, and achieve the effects of fast drying speed, good viscosity and good toughness

Active Publication Date: 2007-10-17
HUNAN SHENLI IND
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The varnish-yarn process was used for the bonding between the squib and the spherical shell, the construction speed is slow and the sealing is difficult to guarantee
The invention patent with the application number of 200410045044 discloses a solvent-based adhesive with ABS, polymethyl methacrylate, and vinyl acetate resin as the main resin, which is used for bonding the paper spherical shell of the fireworks shell to the paper fuse. High bonding str

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Weigh 120 # Solvent gasoline, butanone, ethyl acetate, mixed evenly. Take out 20% from the mixed solvent, put it into a high-speed disperser, start stirring at a speed of 120 rpm, add terpene resin, modified glycerin rosin resin, stir and dissolve for 1 hour, and increase the speed of the disperser to 4000 rpm Slowly add nano-silica and nano-calcium carbonate, continue stirring for 45 minutes after adding, reduce the speed to 200 rpm, and set aside to obtain a nano-material dispersion.

[0029] Add the remaining mixed solvent into the stirred reactor, start stirring, add SBS resin, dissolve at room temperature for 3.5 hours, add C9 petroleum resin, antioxidant-264, dissolve for 1 hour, then add kaolin, stir and disperse for 40 minutes, and finally Add the nanomaterial dispersion liquid in the high-speed disperser, stir for 50 minutes, and filter the material.

Embodiment 2

[0030] Embodiment 2, embodiment 3, comparative example 1 preparation method is the same as embodiment 1.

[0031] component name

Example 1

Example 2

Example 3

Comparative example 1

SBS resin

15

20

24

24

Modified Glycerin Rosin

8

7

5

5

Terpene resin

5

8

4

4

C9 petroleum resin

10

6

14

14

Nano silica

1.2

1.8

2.1

0

Nano calcium carbonate

2.5

3.5

2.8

0

Kaolin

12

20

25

25

120 # Solvent oil

15

10

9

9

butanone

9

14

14

14

ethyl acetate

14

12

18

18

Antioxidant-264

0.3

0.25

0.4

0.4

[0032] The sample of embodiment 1, embodiment 2, embodiment 3, comparative example 1 and application number are the sample that the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a nano-modified salute bomb location glue and method for preparing same. The glue uses SBS elastomer as the major material, addes with adhesion resin and nano-materials to reinforce the surface adhesive force and adhesion strength between the location glue and ignition pipe and the ball shells.

Description

technical field [0001] The invention relates to a nano-modified SBS adhesive, in particular to a nano-modified SBS adhesive used for positioning fireworks shells. Background technique [0002] The fireworks bomb in the fireworks series is a festive product that is launched into the air by propellant and explodes in the air to form a colorful picture. The main spherical shell of the fireworks shell is composed of two hemispherical paper shells, and the outer surface is cemented and reinforced with kraft paper. It contains explosives, effect drugs and accessories. There are 1 to 2 fuse tubes on the spherical shell, and fuses are installed in the tubes. It is required that the fuse tubes and the spherical shell be firmly bonded and tightly sealed. The varnish-yarn process was originally used for the bonding between the squib and the spherical shell, and the construction speed was slow and the sealing was difficult to guarantee. The invention patent with the application number...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J153/02F42B4/00C09J193/04C09J147/00C09J157/02C09J11/00
Inventor 袁素珍谭璋颜珍琼李冬月
Owner HUNAN SHENLI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap