Multifunctional environment protection metal degreasing derusting rust-proofing liquid

A multi-functional, anti-rust technology, applied in the direction of metal material coating process, etc., can solve the problems of flammability and explosion, environmental pollution, unfavorable safety production, etc., and achieve the effect of reducing labor intensity and improving work efficiency

Inactive Publication Date: 2007-12-05
彭文表
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This anti-rust agent simplifies the process of metal surface treatment, but the ethylene oxide in this formula is a toxic substance, flammable and explosive, pollutes the environment, and is unfavorable for safe production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A multifunctional environment-friendly metal degreasing, rust-removing and rust-preventing liquid is special in that it is prepared from the following components (amounts are in parts by weight).

[0020] Polyoxyethylene alkyl ether 1 Sodium dodecyl sulfonate 1

[0021] 1.3-Dibutylthiourea 0.5 Hexamethylenetetramine 0.5

[0022] Zinc dihydrogen phosphate 1 Phosphoric acid 10

[0023] water 20

[0024] Weigh the above-mentioned raw materials in proportion, dissolve the solid into a solution with water, dilute the liquid, then put each raw material into the reaction kettle, stir for 15-30 minutes, and filter through a 120-mesh gauze to make the finished product. The water temperature is 25°C.

Embodiment 2

[0026] Polyoxyethylene alkyl ether 4 Sodium dodecyl sulfonate 5

[0027] 1.3-Dibutylthiourea 6 Hexamethylenetetramine 3

[0028] Zinc dihydrogen phosphate 6 Phosphoric acid 25

[0029] Sodium butylnaphthalene sulfonate 3 Sodium succinate sulfonate 3

[0030] Triethanolamine 5 Sodium bicarbonate 3

[0031] Tartaric acid 7 1.3-Diethylthiourea 5

[0032] water 50.

[0033] Weigh the above-mentioned raw materials in proportion, dissolve the solid into a solution with water, dilute the liquid, then put each raw material into the reaction kettle, stir for 15-30 minutes, and filter with 120-mesh gauze to make the finished product. The water temperature is 50°C.

Embodiment 3

[0035] Polyoxyethylene alkyl ether 6 Sodium dodecyl sulfonate 8

[0036] 1.3-Dibutylthiourea 10 Hexamethylenetetramine 5

[0037] Zinc dihydrogen phosphate 10 Phosphoric acid 40

[0038] Sodium butylnaphthalene sulfonate 5 Sodium succinate sulfonate 5

[0039] Triethanolamine 8 Sodium bicarbonate 5

[0040] Tartaric acid 10 1.3-Diethylthiourea 10

[0041] water 75.

[0042] Weigh the raw materials in proportion, dissolve the solid raw materials with water to form a solution, then put the raw materials into the reaction kettle, stir for 15-30 minutes, and filter through 120-mesh gauze to make the finished product. The water temperature is 25-75°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The functional environment friendly metal deoiling, derusting and antirusting fluid is prepared with polyoxyethylene alkyl ether, sodium dodecyl sulfate, 1.3-dibutyl thiourea, hexamethylidyene tetraamine, zinc dihydrogene phosphate, phosphoric acid, sodium butylnaphthalene sulfonate, sodium sulfosuccinate, triethanolamine, sodium bicarbonate, tartaric acid and 1.3-diethyl sulfourea in certain weight proportion, and through dissolving, diluting with water, mixing to react, and filtering. It has the synergistic effect of the components to deoil, derust, phosphorize, deactivate and antirust metal surface, no harm to human body and no environmental pollution.

Description

technical field [0001] The invention relates to the technical field of metal surface treatment, in particular to a degreasing and descaling fluid for surface pretreatment of metal materials and their products. Background technique [0002] At present, in the existing technology, the degreasing and derusting of the metal surface basically use artificial, physical and chemical methods. Product quality, and produce a lot of dust, pollute the environment, endanger the health of workers; physical derusting, mainly ultrasonic degreasing and derusting effect, due to the large investment, the scope of application is not universal; chemical degreasing and derusting is the most effective method for metal surface treatment The common and most economical method, the traditional degreasing is to use strong alkali NaOH and tetrachlorethylene, rust removal with strong acid such as HCl and H 2 SO 4 These raw materials are highly corrosive and irritating substances, which can cause serious...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/08C23G1/04C23G5/036
Inventor 彭文表
Owner 彭文表
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com